Heat treatment method for eliminating laves phases in beta phases in high temperature alloy incone1783 bolt

A heat treatment method and high-temperature alloy technology, which is applied in the field of alloy heat treatment, can solve the problems of plastic toughness decrease, affect the safety of bolts, destroy the original structure of β phase, etc., and achieve the recovery of plastic toughness, refinement of size, recovery of strength and plastic toughness. Effect

Active Publication Date: 2020-10-13
HEFEI UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the problem that the Laves phase exists in the β phase during the use of the current inconel783 bolts, which destroys the original structure of the β phase, causes a decrease in plasticity and toughness, and affects the use safety of the bolts. Heat treatment method of laves phase in β phase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat treatment method for eliminating laves phases in beta phases in high temperature alloy incone1783 bolt
  • Heat treatment method for eliminating laves phases in beta phases in high temperature alloy incone1783 bolt
  • Heat treatment method for eliminating laves phases in beta phases in high temperature alloy incone1783 bolt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In this embodiment, the heat treatment method for eliminating the laves phase in the β phase in the superalloy inconel783 bolt is as follows:

[0024] 1. Solution treatment: Select the inconel783 superalloy bolt with Laves phase after the main valve of the 660MW supercritical unit is in service, cut the sample from the inconel783 superalloy bolt axially, and put the sample into the KSL-1400X box-type resistance furnace Heat up to 1100°C at a heating rate of 5°C / min, hold for 1 hour, and air cool to room temperature;

[0025] 2. β aging treatment: put the sample after solid solution treatment into KSL-1400X box-type resistance furnace, heat up to 840°C at a heating rate of 5°C / min, keep it warm for 6 hours, and air cool to room temperature;

[0026] 3. γ' aging treatment: put the sample after β aging treatment into the KSL-1400X box-type resistance furnace, the heating rate is 5 ℃ / min, the temperature is raised to 720 ℃, kept for 8 hours, and cooled to 630 ℃ with the fur...

Embodiment 2

[0028] In this embodiment, the heat treatment method for eliminating the laves phase in the β phase in the superalloy inconel783 bolt is as follows:

[0029] 1. Solution treatment: Select the inconel783 superalloy bolt with Laves phase after the main valve of the 660MW supercritical unit is in service, cut the sample from the inconel783 superalloy bolt axially, and put the sample into the KSL-1400X box-type resistance furnace Heat up to 1110°C at a heating rate of 5°C / min, hold for 1 hour, and air cool to room temperature;

[0030] 2. β aging treatment: put the sample after solid solution treatment into KSL-1400X box-type resistance furnace, heat up to 840°C at a heating rate of 5°C / min, keep it warm for 6 hours, and air cool to room temperature;

[0031] 3. γ' aging treatment: put the sample after β aging treatment into the KSL-1400X box-type resistance furnace, the heating rate is 5 ℃ / min, the temperature is raised to 720 ℃, kept for 8 hours, and cooled to 630 ℃ with the fur...

Embodiment 3

[0033] In this embodiment, the heat treatment method for eliminating the laves phase in the β phase in the superalloy inconel783 bolt is as follows:

[0034] 1. Solution treatment: Select the inconel783 superalloy bolt with Laves phase after the main valve of the 660MW supercritical unit is in service, cut the sample from the inconel783 superalloy bolt axially, and put the sample into the KSL-1400X box-type resistance furnace Heat up to 1120°C at a heating rate of 5°C / min, hold for 1 hour, and air cool to room temperature;

[0035] 2. β aging treatment: put the sample after solid solution treatment into KSL-1400X box-type resistance furnace, heat up to 840°C at a heating rate of 5°C / min, keep it warm for 6 hours, and air cool to room temperature;

[0036] 3. γ' aging treatment: put the sample after β aging treatment into the KSL-1400X box-type resistance furnace, the heating rate is 5 ℃ / min, the temperature is raised to 720 ℃, kept for 8 hours, and cooled to 630 ℃ with the fur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat treatment method for eliminating laves phases in beta phases in a high temperature alloy incone1783 bolt. An incone1783 bolt sample of the laves phases in the beta phases is subjected to solution treatment, beta aging treatment and gamma' aging treatment in sequence. Through the heat treatment method disclosed by the invention, Nb solid solutions in the laves phasesenter an austenitic matrix, and the Laves phases in the beta phases are refined, so that lots of needle-like Laves phases are converted into fine rod-like Laves phases, or even the Laves phases are completely eliminated; thus, the plasticity and toughness of materials are restored; and through the heat treatment method disclosed by the invention, the size of the beta phase can be refined, and theplasticity and toughness of the materials are restored.

Description

technical field [0001] The invention belongs to the technical field of alloy heat treatment, and in particular relates to a heat treatment method for eliminating the laves phase in the β phase in the high-temperature alloy inconel783 bolt. Background technique [0002] In order to meet the requirements of the development of the times, the power industry has continuously increased the requirements for energy saving and emission reduction, and the thermal power generating units with conventional parameters are accelerating the transformation to supercritical generating units with high parameters. Inconel783, a low-expansion superalloy introduced from the aerospace field, is widely used in supercritical units. Inconel783 is a low expansion coefficient superalloy based on Fe-Ni-Co. Because its Al content (≥5%) is much higher than other traditional low expansion coefficient superalloys, it can not only precipitate and disperse on the γ-austenite matrix The γ' phase of the alloy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/00
CPCC22F1/00
Inventor 杜晓东陶思友巫振伟刘润飞王赛龙
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap