Hydroxyapatite type toothpaste

A hydroxyapatite and toothpaste technology, applied in dentistry, medical science, digestive system, etc., can solve the problems of single formula, single toothpaste smell, unable to adjust the toothpaste smell, etc., achieve comfortable fragrance and taste, increase the number of suitable people, good The effect of cleaning the mouth and its surroundings

Pending Publication Date: 2020-10-16
浙江埃普瑞纳米新材料股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a hydroxyapatite-type toothpaste, which aims to solve the problem that the above existing formula is relatively single, so that the smell of the toothpaste is single, and the smell of the toothpaste cannot be adjusted according to people's preferences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydroxyapatite type toothpaste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A hydroxyapatite toothpaste, comprising the following raw materials in parts by weight: 100-120 parts of hydroxyapatite, 80-100 parts of calcium carbonate, 5-9 parts of sodium fluoride, 3-7 parts of potassium fluoride, fluoride 1-5 parts of stannous chloride, 2-6 parts of monofluorophosphoric acid, 1-5 parts of calcium hydrogen phosphate, 3-7 parts of calcium pyrophosphate, 4-8 parts of silicon dioxide, 4-8 parts of aluminum hydroxide, 5 parts of glycerin -9 parts, 7-11 parts of sorbitol, 7-11 parts of propylene glycol, 6-10 parts of polyethylene glycol, 5-9 parts of sodium lauryl sulfate, 5-9 parts of sodium 2-acyloxy bond sulfonate, Sodium lauroyl sarcosinate 6-10 parts, carboxymethyl cellulose 7-11 parts, staghorn pectin 8-12 parts, hydroxyethyl cellulose 9-13 parts, xanthan gum 10-14 parts, guar gum 6-10 parts, 5-9 parts of carrageenan, 5-9 parts of glycerin, 6-10 parts of sodium cyclamate, 3-7 parts of sodium saccharin, 3-7 parts of potassium sorbate and sodium ben...

Embodiment 2

[0027] A hydroxyapatite toothpaste, comprising the following raw materials in parts by weight: 100-120 parts of hydroxyapatite, 80-100 parts of calcium carbonate, 5-9 parts of sodium fluoride, 3-7 parts of potassium fluoride, fluoride 1-5 parts of stannous chloride, 2-6 parts of monofluorophosphoric acid, 1-5 parts of calcium hydrogen phosphate, 3-7 parts of calcium pyrophosphate, 4-8 parts of silicon dioxide, 4-8 parts of aluminum hydroxide, 5 parts of glycerin -9 parts, 7-11 parts of sorbitol, 7-11 parts of propylene glycol, 6-10 parts of polyethylene glycol, 5-9 parts of sodium lauryl sulfate, 5-9 parts of sodium 2-acyloxy bond sulfonate, Sodium lauroyl sarcosinate 6-10 parts, carboxymethyl cellulose 7-11 parts, staghorn pectin 8-12 parts, hydroxyethyl cellulose 9-13 parts, xanthan gum 10-14 parts, guar gum 6-10 parts, 5-9 parts of carrageenan, 5-9 parts of glycerin, 6-10 parts of sodium cyclamate, 3-7 parts of sodium saccharin, 3-7 parts of potassium sorbate and sodium ben...

Embodiment 3

[0035] A hydroxyapatite toothpaste, comprising the following raw materials in parts by weight: 100-120 parts of hydroxyapatite, 80-100 parts of calcium carbonate, 5-9 parts of sodium fluoride, 3-7 parts of potassium fluoride, fluoride 1-5 parts of stannous chloride, 2-6 parts of monofluorophosphoric acid, 1-5 parts of calcium hydrogen phosphate, 3-7 parts of calcium pyrophosphate, 4-8 parts of silicon dioxide, 4-8 parts of aluminum hydroxide, 5 parts of glycerin -9 parts, 7-11 parts of sorbitol, 7-11 parts of propylene glycol, 6-10 parts of polyethylene glycol, 5-9 parts of sodium lauryl sulfate, 5-9 parts of sodium 2-acyloxy bond sulfonate, Sodium lauroyl sarcosinate 6-10 parts, carboxymethyl cellulose 7-11 parts, staghorn pectin 8-12 parts, hydroxyethyl cellulose 9-13 parts, xanthan gum 10-14 parts, guar gum 6-10 parts, 5-9 parts of carrageenan, 5-9 parts of glycerin, 6-10 parts of sodium cyclamate, 3-7 parts of sodium saccharin, 3-7 parts of potassium sorbate and sodium ben...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses hydroxyapatite type toothpaste, and particularly relates to the field of toothpaste. The hydroxyapatite type toothpaste comprises the following raw material in parts by weight:100-120 parts of hydroxyapatite, 80-100 parts of calcium carbonate, 5-9 parts of sodium fluoride, 3-7 parts of potassium fluoride, 1-5 parts of stannous fluoride, 2-6 parts of monofluorophosphoric acid, 1-5 parts of calcium hydrophosphate, 3-7 parts of calcium pyrophosphate, 4-8 parts of silicon dioxide, 4-8 parts of aluminum hydroxide, 5-9 parts of glycerin, 7-11 parts of sorbitol, 7-11 parts ofpropylene glycol and 6-10 parts of polyethylene glycol. The hydroxyapatite type toothpaste disclosed by the invention is diversified in smell, can be purchased according to favorite smell of a user,is increased in applicable crowd and improved in product competitiveness, increases the original basic efficacy, and can remove thin films and dental plaque on the surfaces of teeth without damaging enamel and dentin; the toothpaste has a good effect of cleaning the oral cavity and the surroundings.

Description

technical field [0001] The invention belongs to the technical field of toothpaste, in particular to a hydroxyapatite toothpaste. Background technique [0002] Toothpaste is a commonly used cleaning product in daily life. It is a kind of toothpaste, which is generally in the form of gel. It is usually applied on a toothbrush to clean teeth and keep them beautiful and white. Toothpaste has a long history. With the continuous development of science and technology, the continuous improvement and perfection of production technology and equipment, various types of toothpaste have come out one after another, and the quality and grade of products are also continuously improving. As of 2019, the variety of toothpaste has developed from a single clean toothpaste to It has become a multi-functional toothpaste with complete varieties and various functions, and hundreds of brands, meeting the needs of different levels of consumption. [0003] Hydroxyapatite-type toothpaste has special e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/9794A61K8/9789A61K8/24A61Q11/00A61P1/02
CPCA61K8/9794A61K8/9789A61K8/24A61Q11/00A61P1/02
Inventor 倪成辉
Owner 浙江埃普瑞纳米新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com