Decorative coating capable of decomposing formaldehyde and releasing high-concentration negative oxygen ions

A technology of negative oxygen ions and decorative coatings, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problem of different purification effects, low purification efficiency, and tourmaline's negative oxygen ion release Unsure etc.

Active Publication Date: 2020-10-23
佛山市邦韵建材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, some environmentally friendly wall materials have appeared. These wall materials add tourmaline to the raw materials, and release negative oxygen ions through tourmaline to achieve the purpose of purifying the air. However, the amount of negative oxygen ions released by tourmaline is uncertain, resulting in the purification effect of these wall materials. Different, for example, a green environment-friendly tourmaline composite home improvement material disclosed in Chinese invention patent CN 104386982 A, including the following raw materials in parts by weight: tourmaline powder: 2-20 parts; slag: 20-80 parts; activated carbon 2-10 parts; Binder: 5-40 parts; Excipients: 1-40 parts; Air-entraining agent: 0.1-0.3 parts
According to investigation and research, the most standard tourmaline releases only about 6,000 negative oxygen ions per cubic centimeter. The release of negative oxygen ions is small, the purification efficiency is low, and the purification effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decorative coating capable of decomposing formaldehyde and releasing high-concentration negative oxygen ions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The preparation embodiment of auxiliary agent:

[0043] a, first prepare modified diatomite, the method is as follows:

[0044] (1) 100mL of ethanol is added to a 250mL three-neck flask with a heating and stirring device;

[0045] (2) Add 2g of diatomite powder in the three-necked flask of step (1), and disperse evenly by ultrasonic;

[0046] (3) Add 0.1 g of 4-amino-2-butanol to the system in step 2, and react at 70°C for 1 hour. Ultrasonic dispersion and stirring are carried out alternately during the reaction.

[0047] (4) Finally, centrifuge and dry the reaction product obtained in step (3) to obtain modified diatomite.

[0048] B, prepare modified titanium dioxide again, the method is as follows:

[0049] (1) Weigh 10g of anatase titanium dioxide into a 240mL four-neck flask, add 200mL of toluene, 10gKH570, 0.6mL of triethylamine, and ultrasonically disperse in an ice-water bath for 30min;

[0050] (2) Raise the temperature of the system in step (1) to 110°C, i...

Embodiment 2

[0060] The preparation method of auxiliary agent is with embodiment 1, and difference is: in step (c), 25 parts of modified diatomites and 5 parts of modified titanium dioxide are dispersed in 30 parts of water.

[0061] Preparation of decorative coatings:

[0062] Add 60 parts of additives, 18 parts of modified tourmaline, 5 parts of aloe freeze-dried powder, 10 parts of calcium phosphate powder, 5 parts of hydroxymethyl cellulose, 20 parts of Shuangfei powder, 12 parts of bentonite, and 8 parts of ash calcium powder. Add it to 50 parts of water and stir evenly to obtain home improvement paint.

[0063] With 1kg according to embodiment 2 as the home improvement paint that raw material is made, evenly spread out, airtight 24h, with the AIC-1000 negative oxygen ion detector that U.S. Alphalab company produces every 1h detection once, get 20 data each time, obtain The average value of each data is 78000 / cm 3 .

Embodiment 3

[0065] The preparation method of auxiliary agent is with embodiment 1, and difference is: in step (c), 30 parts of modified diatomaceous earths and 8 parts of modified titanium dioxide are dispersed in 35 parts of water.

[0066] Preparation of decorative coatings:

[0067] Add 73 parts of additives, 18 parts of modified tourmaline, 5 parts of aloe freeze-dried powder, 10 parts of calcium phosphate powder, 5 parts of hydroxymethyl cellulose, 20 parts of Shuangfei powder, 12 parts of bentonite, and 8 parts of ash calcium powder. Add it to 55 parts of water and stir evenly to obtain home improvement paint.

[0068] With 1kg according to embodiment 3 as the home improvement paint that raw material is made, evenly spread out, airtight 24h, with the AIC-1000 negative oxygen ion detector that U.S. Alphalab Company produces every 1h detect once, get 20 data at every turn, obtain The average value of each data is 81000 / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of indoor decorative coatings, in particular to a decorative coating capable of adsorbing and decomposing formaldehyde and releasing negative oxygen ions,and aims to further improve the purpose that the decorative coating releases high-concentration negative oxygen ions to decompose indoor formaldehyde. According to the decorative coating capable of adsorbing and decomposing formaldehyde and releasing negative oxygen ions, the decorative coating comprises the following components in parts by weight: 200-300 parts of a coating additive and 80-100 parts of water. All the components of the prepared decorative coating have a synergistic effect and can release high-concentration negative oxygen ions, the concentration of the negative oxygen ions reaches 80,000 per cubic centimeter, the generated negative oxygen ions can directly decompose formaldehyde, methylbenzene and other pollutants into non-toxic and odorless carbon dioxide and water, indoor pollution is relieved, and the decorative coating has a remarkable influence on air purification and has a good application prospect.

Description

technical field [0001] The invention relates to the technical field of interior decorative coatings, in particular to a decorative coating that absorbs and decomposes formaldehyde and releases negative oxygen ions. Background technique [0002] Negative oxygen ions are known as "air vitamins". Negative oxygen ions can directly decompose formaldehyde, toluene and other pollutants into non-toxic and tasteless carbon dioxide and water, relieve indoor pollution, and have a significant impact on air purification. Moreover, medical research shows that , Negative oxygen ions increase the oxygen content in the blood, which is beneficial to the transportation, absorption and utilization of blood oxygen, and has the functions of promoting human metabolism, improving human immunity, enhancing human muscle energy, and regulating the balance of body functions. According to research, negative oxygen ions have the functions of inhibiting, alleviating and adjuvant treatment on 7 systems of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D199/00C09D101/28C09D1/00C09D5/14C09D7/62C09D7/61C09D7/65
CPCC08K2003/2206C08K2003/2241C08K2003/325C09D1/00C09D5/14C09D101/284C09D199/00C09D7/61C09D7/62C09D7/65C08L1/284C08K13/06C08K9/04C08K7/26C08K9/06C08K3/22C08K3/38C08K3/32C08K3/346C08L99/00
Inventor 吴晨伟
Owner 佛山市邦韵建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com