Zero-dimensional cesium lead bromine inorganic perovskite material and preparation method thereof

A zero-dimensional cesium lead and inorganic calcium technology, applied in inorganic chemistry, luminescent materials, chemical instruments and methods, etc., can solve the problems of difficulty in mass synthesis and high synthesis cost, and achieve mild and controllable preparation conditions, stable properties, and products. high purity effect

Active Publication Date: 2022-05-10
SHENZHEN UNIV
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, since Cs 4 PbBr 6 It is an inorganic material, and its synthetic raw material CsBr is very ionic. It is commonly used as a solvent for the synthesis of organic-inorganic hybrid lead-based halide perovskite materials, such as: 1,4-butyrolactone (GBL), dimethyl Formamide (DMF), dimethyl sulfoxide (DMSO), etc. cannot provide an effective dissolution environment for CsBr raw materials
And the sol method (organic phase), although Cs can be synthesized 4 PbBr 6 Quantum dots, but it is difficult to achieve a large number of synthesis, and the synthesis cost is too high, it is only suitable for a small amount of synthesis in the laboratory
In addition, although HBr hydrobromide can simultaneously dissolve Cs 4 PbBr 6 The precursors of CsBr and PbBr 2 , however, excess Br ions in the system will lead to Cs 4 PbBr 6 Quenching of material fluorescence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zero-dimensional cesium lead bromine inorganic perovskite material and preparation method thereof
  • Zero-dimensional cesium lead bromine inorganic perovskite material and preparation method thereof
  • Zero-dimensional cesium lead bromine inorganic perovskite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The first aspect of the embodiment of the present application provides a method for preparing a zero-dimensional cesium lead bromine inorganic perovskite material, comprising the following steps:

[0026] Dissolving the first lead source in a mixed solution of DMF and DMSO to obtain the first solution;

[0027] CsBr is dissolved in water to obtain a second solution;

[0028] After thermal mixing treatment of the first solution and the second solution, cooling treatment and separation treatment, Cs 4 PbBr 6 Inorganic perovskite materials, that is, zero-dimensional cesium lead bromine inorganic perovskite.

[0029] The zero-dimensional cesium lead bromide (Cs) provided by the first aspect of the application 4 PbBr 6 ) The preparation method of the inorganic perovskite material, using a mixed solvent of DMF and DMSO to dissolve the lead source, using water to dissolve CsBr, and mixing the first solution and the second solution to form a three-solvent system of water-DM...

Embodiment 1

[0051] a Cs 4 PbBr 6 An inorganic perovskite material, the preparation steps of which include:

[0052] 1. Add 10mmol PbBr 2 Dissolve in a mixed solution of 20mL DMF and 10mL DMSO, and heat to 80-90°C to obtain the first solution;

[0053] 2. Take 4mL of 10Mmol / L CsBr aqueous solution and heat it to 90°C. After clarification, the second solution is obtained;

[0054] 3. Mix and stir the first solution with a temperature of 80-90°C and the second solution with a temperature of about 90°C, and naturally cool to room temperature;

[0055] 4. After centrifugation, the obtained solid was washed twice with toluene and n-hexane with a volume ratio of 1:2, put into a vacuum drying oven, dried for more than 8 hours, and stored dry to obtain Cs 4 PbBr 6 Inorganic perovskite materials.

Embodiment 2

[0057] a Cs 4 PbBr 6 A cyclic preparation method for an inorganic perovskite material, the steps comprising:

[0058] 1. In the mother liquor after centrifugation in Example 1, add the PbBr of 8mmol 2 After fully stirring, add 16ml of 2M CsBr aqueous solution;

[0059] 2. After heating the system to 80°C, continue to stir, and evaporate excess water under low pressure. After the system solution changes from orange to yellow-green, stop heating and cool down to room temperature naturally;

[0060] 3. After centrifugation, the obtained solid was washed twice with toluene and n-hexane with a volume ratio of 1:2, put into a vacuum drying oven, dried for more than 8 hours, and dried to obtain Cs 4 PbBr 6 Inorganic perovskite materials.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application belongs to the technical field of perovskite materials, and in particular relates to a preparation method of a zero-dimensional cesium lead bromine inorganic perovskite material, comprising the following steps: dissolving the first lead source in a mixed solution of DMF and DMSO to obtain the first solution; CsBr is dissolved in water to obtain a second solution; after the first solution and the second solution are thermally mixed, cooled and separated to obtain Cs 4 PbBr 6 Inorganic perovskite materials, that is, zero-dimensional cesium lead bromine inorganic perovskite. The preparation method of the zero-dimensional cesium-lead-bromine inorganic perovskite material of the present application can selectively control the phase state of the precipitated inorganic perovskite through the three-solvent system of water-DMSO-DMF, so that the product can be as Cs as possible. 4 PbBr 6 phase precipitation, reducing the CsPbBr in the product 3 , CsPb 2 Br 5 Phase content, get high-purity Cs 4 PbBr 6 Inorganic perovskite materials, the preparation conditions are mild and controllable, and the operation is simple and flexible.

Description

technical field [0001] The application belongs to the technical field of perovskite materials, in particular to a zero-dimensional cesium lead bromine inorganic perovskite material and a preparation method thereof. Background technique [0002] Among all spectra, the human eye is most sensitive to green light, and green fluorescent light-emitting materials are one of the most demanded materials in LEDs. At present, green fluorescent materials are mainly quantum dots, organic materials, and rare earth materials. New Inorganic Perovskite Material Cs 4 PbBr 6 It is a green fluorescent material with a zero-dimensional perovskite structure. It has the advantages of high fluorescence quantum yield and color purity, and small spectral line broadening. It has broad application prospects in fluorescent lamps, electroluminescent devices, and solid-state lasers. [0003] However, since Cs 4 PbBr 6 It is an inorganic material, and its synthetic raw material CsBr is very ionic. It i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/66C01G21/16
CPCC09K11/665C01G21/006C01G21/16C01P2002/72C01P2002/82
Inventor 时玉萌周勃李贺楠
Owner SHENZHEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com