A technology of natural rubber and high temperature resistance, applied in the rubber field, can solve the problems of improper selection of natural rubber preparation components, difficulty in meeting the technical requirements of automobile vibration damping products in anti-vulcanization reversion, and damage to natural rubber properties, and achieve anti-vulcanization. The effect of improving the reversion performance, improving the anti-reversion performance and improving the fatigue resistance performance

Inactive Publication Date: 2020-12-15
北威(重庆)科技股份有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] It can be seen that improper selection of natural rubber preparation components will cause damage to the performance of natural rubber to a certain extent, making it difficult for the fatigue life, temperature resistance, and anti-reversion performance of natural rubber to meet the requirements of automobile vibration reduction. Technical requirements for internal products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Raw material for preparing high-temperature-resistant high-fatigue-resistance natural rubber
  • Raw material for preparing high-temperature-resistant high-fatigue-resistance natural rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A raw material for preparing high-temperature-resistant and high-fatigue-resistant natural rubber, which is composed of the following raw materials in parts by mass: 100 parts of smoked sheet rubber, 3-8 parts of zinc oxide, 1-2 parts of stearic acid, 1-3 parts of anti-aging agent RD, anti-aging agent 1-2 parts of 4010NA, 1-2 parts of anti-aging agent 40201-2 parts, 2-5 parts of microcrystalline wax 9332F, 3-5 parts of silane coupling agent Si-669 / G, 0.5-1.5 parts of PAPI, 0-40 parts of carbon black N33020, carbon 30-60 parts of black N6600, 10-30 parts of barium sulfate, 845-20 parts of aromatic oil Tudalen, 2-3 parts of sulfur, 1-2 parts of accelerator CZ, 0.5-1 part of IDH, 2-4 parts of Perkalink 9000.

[0016] The above-mentioned natural rubber preparation raw materials are further limited, including the following mass components: 100 parts of smoked sheet rubber, 5-7 parts of zinc oxide, 1-2 parts of stearic acid, 1-3 parts of anti-aging agent RD, and 1 part of anti...

Embodiment 2

[0034]Embodiment 2 is a kind of preferred scheme selected on the basis of embodiment 1, selects definite weight part value from each batching weight part range in embodiment 1, carries out the refining of natural rubber then, with The natural rubber of natural rubber is carried out physical property test, with every physical property test result that draws, demonstrates in embodiment 1, and each raw material weight portion proportioning is as follows:

[0035] Including the following raw materials by mass, 100 parts of smoked sheet glue, 3 parts of zinc oxide, 1 part of stearic acid, 1 part of anti-aging agent RD, 2 parts of anti-aging agent 4010NA, 1.5 parts of anti-aging agent 40201, 5 parts of microcrystalline wax 9332F, silane di 3 parts of joint agent Si-669 / G, 0.5 parts of PAPI, 20 parts of carbon black N33020 parts, 60 parts of carbon black N66060, 10 parts of barium sulfate, 845 parts of aromatic oil Tudalen, 2 parts of sulfur, 1 part of accelerator CZ, 0.5 parts of IDH...

Embodiment 3

[0039] Embodiment 3 is the second preferred scheme selected on the basis of Example 1, select certain parts by weight from the range of parts by weight of the ingredients in Example 1, then carry out refining of natural rubber, use The natural rubber that obtains carries out physical performance test, with the various physical performance test results that draw, demonstrates in embodiment 1, and each raw material weight portion proportioning is as follows:

[0040] Including the following raw materials by mass, 100 parts of smoked sheet glue, 5 parts of zinc oxide, 1.5 parts of stearic acid, 2 parts of anti-aging agent RD, 2 parts of anti-aging agent 4010NA, 1.5 parts of anti-aging agent 40201, 4 parts of microcrystalline wax 9332F, silane coupling Joint agent Si-669 / G 3 parts, PAPI 0.5 parts, carbon black N33025 parts, carbon black N66050 parts, barium sulfate 15 parts, aromatic hydrocarbon oil Tudalen 8420 parts, sulfur 2 parts, accelerator CZ 1 part, IDH 0.6 parts, Perkalink...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of rubber, in particular to a high-temperature-resistant high-fatigue-resistance natural rubber preparation raw material. The rubber is prepared from, by mass, 100 parts of smoke sheet rubber, 3-8 parts of zinc oxide, 1-2 parts of stearic acid, 1-3 parts of anti-aging agent RD, 1-2 parts of anti-aging agent 4010NA, 1-2 parts of anti-aging agent 4020, 2-5 parts of microcrystalline wax 9332F, 3-5 parts of silane coupling agent Si-669 / G, 0.5-1.5 parts of PAPI, 20-40 parts of carbon black N330, 30-60 parts of carbon blackN660, 10-30 parts of barium sulfate, 5-20 parts of aromatic oil Tudalen 84, 2-3 parts of sulphur, 1-2 parts of accelerant CZ, 0.5-1 parts of IDH, and 2-4 parts of Perkalink 900. By reasonably adjusting a formula system, the fatiguelife, the temperature resistance and the vulcanization reversion resistance of the natural rubber can be remarkably improved.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a raw material for preparing natural rubber with high temperature resistance and high fatigue resistance. Background technique [0002] In the process of continuous development of the rubber industry, rubber products are more and more widely used in aerospace, automobile, industrial products and other fields, but the requirements for rubber are becoming more and more stringent. Most of the automotive vibration damping products use natural rubber. In order to improve the technical performance of natural rubber such as aging resistance, wear resistance, and fatigue life, most of them use BR (butadiene rubber) and SBR (styrene-butadiene rubber) together. With the continuous development, some companies will also use TPI (trans-polyisoprene rubber), TBIR (trans-butadiene rubber), etc., but at the same time, they will lose some of the unique properties of natural rubber. BR rubber will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L91/06C08K13/02C08K3/22C08K5/09C08K3/04C08K3/30C08K3/06C08K5/3415C08K5/25
CPCC08L7/00C08L2201/08C08K2003/2296C08K2003/3045C08L91/06C08K13/02C08K3/22C08K5/09C08K3/04C08K3/30C08K3/06C08K5/3415C08K5/25
Inventor 臧运朋侯向阳李华邓又木
Owner 北威(重庆)科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap