Synthetic resin production process
A synthetic resin and production process technology, applied in the field of synthetic resin production process, can solve the problems of poor heat resistance, performance degradation failure, loss, etc., and achieve the effect of high mechanical properties and thermal stability
Inactive Publication Date: 2020-12-22
江苏铭泰新材料有限公司
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
At present, traditional synthetic resin products have poor heat resistance and are easy to break. Affected by the harsh external environment, phenomena such as shedding, aging, and performance degradation and failure often occur, causing huge losses.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The preferred embodiments of the present invention will be described in detail below, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.
[0016] A synthetic resin production process, comprising the steps of:
[0017] (1) Mixing selection of raw materials for synthetic resin products. Raw materials are selected as: bisphenol A epoxy resin, PA6 resin, antioxidant, polymerization inhibitor, alkali-free glass fiber, thermal conductive filler, thermal conductive filler treatment agent, hollow glass micro Beads, according to the weight ratio, the bisphenol A epoxy resin occupies 40%-50%, PA6 resin 15%-20%, antioxidant 5%-10%, polymerization inhibitor 5%-6.5%, no Alkali glass fiber 3%-6%, thermal conductive filler 8%-10%, thermal conductive filler treatment agent 2%-2.5%, hollow glass microsphere 4%-5%;
[0018] (2) Stir the raw mat...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a synthetic resin production process which comprises the following steps: (1), mixing and selecting raw materials of a synthetic resin product: 40%-50% of bisphenol A epoxy resin, 15%-20% of PA6 resin, 5%-10% of an antioxidant, 5%-6.5% of a polymerization inhibitor, 3%-6% of alkali-free glass fiber, 8%-10% of heat-conducting filler, 2%-2.5% of a heat-conducting filler treating agent and 4%-5% of glass beads; (2), stirring the raw materials in a reaction kettle, and keeping the temperature at 180 DEG C under the protection of inert gas to obtain synthetic resin; (3), inspecting the synthetic resin, and stopping the reaction in the reaction kettle after the synthetic resin is qualified; and (4), crushing the synthetic resin, performing bagging and discharging. The synthetic resin produced by the production process provided by the invention is reinforced and toughened, flame-retardant and self-repairing, and high in mechanical property and thermal stability.
Description
technical field [0001] The invention relates to the technical field of polymer materials, in particular to a synthetic resin production process. Background technique [0002] Synthetic resin is a kind of artificially synthesized high molecular weight polymer. It is a resin that has both or exceeds the inherent characteristics of natural resins. Synthetic resin products are widely used in daily life. At present, traditional synthetic resin products have poor heat resistance and are easy to break. Affected by the harsh external environment, phenomena such as shedding, aging, and performance degradation and failure often occur, causing huge losses. In order to solve the above problems, it is necessary to propose a production process of a synthetic resin with enhanced toughness, flame retardant self-repair, high mechanical properties and thermal stability. Contents of the invention [0003] In order to solve the above-mentioned defects, the purpose of the present invention i...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L77/02C08K13/06C08K7/28C08K7/14C08K9/06C08K7/18C08K3/22C08K3/38
CPCC08K2003/2227C08K2003/385C08K2201/003C08L63/00C08L2201/02C08L2201/08C08L77/02C08K13/06C08K7/28C08K7/14C08K9/06C08K7/18C08K3/22C08K3/38
Inventor 陆志强涂相欣赵建明
Owner 江苏铭泰新材料有限公司