Degradable master batch for BOPP film, preparation method thereof and BOPP film
A masterbatch and film technology, applied in the field of BOPP film degradable masterbatch and its preparation, BOPP film, can solve the problems of non-degradability, ecological damage, environmental pollution, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0027] The degradation masterbatch for BOPP film of the present embodiment comprises the following components in weight percent:
[0028]
[0029]
[0030] Wherein, the polypropylene resin is selected from the isotactic homopolypropylene of the oriented stretchable film grade, and the melt index is 1-25g / 10min; the photodegradation preoxidant is specifically titanium dioxide, and the average particle diameter is 80nm; natural biomass is selected What is used is the powdered natural plant fiber modified by plasticization, with an average particle size of 5 μm; the plasticizer is glycerol; the compatibilizer is PP-g-MAH; the lubricant is stearic acid.
Embodiment 2
[0032] The degradation masterbatch for BOPP film of the present embodiment comprises the following components in weight percent:
[0033]
[0034] Wherein, the polypropylene resin is selected from the syndiotactic homopolypropylene of the oriented stretchable film grade, and the melt index is 1-25g / 10min; the thermal degradation preoxidant is specifically iron stearate, and the average particle diameter is 50nm; natural The biomass is plasticized modified starch with an average particle size of 10 μm; the plasticizer is tributyl citrate; the compatibilizer is PE-g-MAH; the lubricant is stearic acid.
Embodiment 3
[0036] The degradation masterbatch for BOPP film of the present embodiment comprises the following components in weight percent:
[0037]
[0038] Wherein, the polypropylene resin is selected from the syndiotactic homopolypropylene of the oriented stretchable film grade, and the melt index is 1-25g / 10min; the photodegradation oxidant is calcium oxide, and the average particle diameter is 1nm; the thermal degradation preoxidant is Cobalt acetate, with an average particle size of 1nm; the natural biomass is plasticized modified starch, with an average particle size of 0.1μm; the plasticizer is epoxidized soybean oil; the compatibilizer is EVA-g-MAH; The lubricant is polyethylene wax.
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap