A kind of superhydrophobic perovskite/silicon dioxide composite luminescent film and its preparation method and application

A technology of silicon dioxide and light-emitting thin films, applied in chemical instruments and methods, light-emitting materials, semiconductor devices, etc., can solve the problem that the surface of perovskite materials does not have super-hydrophobic properties, does not meet the requirements of environmentally friendly preparation, and the stability needs to be further improved Improvement and other issues, to achieve the effect of low preparation cost, excellent stability, and easy operation

Active Publication Date: 2022-01-11
WUHAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the preparation conditions involved in the above method are relatively complicated, and toxic ligands or high temperature conditions need to be introduced, which do not meet the requirements of environmentally friendly preparation; and the surface of the obtained perovskite material does not have superhydrophobic properties, and its water resistance is limited. to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of superhydrophobic perovskite/silicon dioxide composite luminescent film and its preparation method and application
  • A kind of superhydrophobic perovskite/silicon dioxide composite luminescent film and its preparation method and application
  • A kind of superhydrophobic perovskite/silicon dioxide composite luminescent film and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A superhydrophobic perovskite / silicon dioxide composite luminescent film, the preparation method of which comprises the following steps:

[0037] 1) Weigh 69mg of PbBr with an electronic balance 2 In a 50mL beaker, measure 8mL of methanol with a graduated cylinder and pipette 0.6mL of ammonia water (concentration: 26wt%) into the above beaker, and continue stirring for 10min to obtain a mixed solution I;

[0038] 2) Weigh 11 mg of Cs with an electronic balance 2 CO 3 In a 10mL beaker, pipette 1mL of methanol and 4.4mL of tetraethyl orthosilicate (TEOS) into the above beaker, stir well until Cs 2 CO 3 Dissolve completely to obtain mixed solution II;

[0039] 3) Under magnetic stirring, slowly drop the mixed solution II prepared in step 2) into the mixed solution I prepared in step 1) with a rubber dropper, and continue to stir and react for 0.5 h;

[0040] 4) While stirring, slowly add 4 mL of hexamethyldisilazane (HMDS) dropwise into the dispersion obtained in step...

Embodiment 2

[0045] A superhydrophobic perovskite / silicon dioxide composite luminescent film, the preparation method of which comprises the following steps:

[0046] 1) At room temperature, weigh 69 mg of PbBr with an electronic balance 2 In a 100mL beaker, measure 16mL of methanol with a graduated cylinder, pipette 1.2mL of ammonia water (concentration: 26wt%) into the above beaker, and continue stirring for 10min to obtain a mixed solution I;

[0047] 2) Weigh 11 mg of Cs with an electronic balance 2 CO 3 In a 25mL beaker, measure 2mL of methanol and 8.8mL of tetraethyl orthosilicate (TEOS) in the above beaker with a graduated cylinder, stir well until Cs 2 CO 3 Dissolve completely to obtain mixed liquid II;

[0048] 3) Under magnetic stirring, slowly drop the mixed solution II prepared in step 2) into the mixed solution I prepared in step 1) with a rubber dropper, and continue to stir and react for 0.5 h;

[0049] 4) While stirring, slowly add 8 mL of hexamethyldisilazane (HMDS) dr...

Embodiment 3

[0053] A superhydrophobic perovskite / silicon dioxide composite luminescent film, the preparation method of which comprises the following steps:

[0054] 1) At room temperature, weigh 69 mg of PbBr with an electronic balance 2 In a 250mL beaker, measure 24mL of methanol with a graduated cylinder and pipette 1.8mL of ammonia water (concentration: 26wt%) into the above beaker, and continue stirring for 10min to obtain a mixed solution I;

[0055] 2) Weigh 11 mg of Cs with an electronic balance 2 CO 3 In a 25mL beaker, use a measuring cylinder to measure 3mL of methanol and 13.2mL of tetraethyl orthosilicate (TEOS) in the above beaker, stir well until Cs 2 CO 3 Dissolve completely to obtain mixed liquid II;

[0056] 3) Under magnetic stirring, slowly drop the mixed solution II prepared in step 2) into the mixed solution I prepared in step 1) with a rubber dropper, and continue to stir and react for 0.5 h;

[0057] 4) While stirring, slowly add 12 mL of hexamethyldisilazane (H...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a superhydrophobic perovskite / silicon dioxide composite luminescent film, the preparation method of which comprises the following steps: firstly, PbBr 2 and lye are uniformly dispersed in alcohol solvent to obtain Pb-based dispersion, Cs 2 CO 3 , TEOS is uniformly dissolved in an alcohol solvent to obtain a Cs-Si-based dispersion, and then the Cs-Si-based dispersion is added dropwise to the Pb-based dispersion under stirring conditions, and after a sufficient reaction for a certain period of time, hexamethyldisilamine is added Alkanes are used for modification reaction, and then the resulting dispersion is coated and dried to obtain a superhydrophobic perovskite / silicon dioxide composite luminescent film with high efficiency and high stability. The preparation method involved in the present invention is simple and easy, the reaction conditions are mild, the cost is low, and macro-scale preparation can be realized. The obtained perovskite / silicon dioxide composite material can exhibit good superhydrophobic function and stability, and is self-cleaning, Efficient and stable LEDs or fluorescent solar concentrators have broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of luminescent materials, and in particular relates to a high-efficiency and high-stable superhydrophobic perovskite / silicon dioxide composite luminescent film and its preparation method and application. Background technique [0002] In recent years, perovskite nanomaterials have become a research hotspot of semiconductor light-emitting materials due to their excellent luminescence performance, adjustable luminescence wavelength, and narrow half-maximum width of the fluorescence peak; however, the poor stability of this material limits its practical application. Popularization and application, especially in the air and humid environment, it will degrade due to the influence of water and oxygen, thus losing stability. Perovskite is an ionic crystal, and its instability mainly comes from the instability of its structure itself and the instability caused by its degradation in the environment. [0003] In order...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/02C09K11/66H01L33/50
CPCC09K11/025C09K11/665H01L33/502
Inventor 谢毅胡永飞
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com