Antiskid anti-icing-night visible asphalt pavement material and preparation method thereof

An asphalt pavement and anti-icing technology, applied in the field of road engineering materials, can solve the problems of high cost of self-luminous materials, complex material system and preparation process, etc., achieve rich edges and corners, improve night visibility, and improve insufficient adhesion Effect

Active Publication Date: 2021-04-09
WUHAN UNIV OF TECH
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the material system and preparation process of this material are complicated, and the cost of the self-luminous material used is relatively high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antiskid anti-icing-night visible asphalt pavement material and preparation method thereof
  • Antiskid anti-icing-night visible asphalt pavement material and preparation method thereof
  • Antiskid anti-icing-night visible asphalt pavement material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] An anti-skid and anti-icing-visible asphalt pavement material at night is provided, which comprises the following components in parts by mass:

[0041] 55 parts of steel slag coarse aggregate, 15 parts of waste glass fine aggregate, 30 parts of steel slag fine aggregate, 5 parts of filler containing phase change material, 4.1 parts of modified asphalt; wherein:

[0042] In the steel slag coarse aggregate, the gradation is 36 parts with a particle size of 9.5-16mm, and 19 parts with a particle size of 4.75-9.5mm;

[0043] The preparation of the above-mentioned anti-skid and anti-icing-visible asphalt pavement material at night comprises the following steps:

[0044]1) Mix the steel slag coarse aggregate, waste glass fine aggregate and steel slag fine aggregate to obtain the mixed aggregate, heat it with the filler containing phase change material and modified asphalt respectively, at a temperature of 170°C, and keep it warm for 4 hours;

[0045] 2) Put the heated mixed ...

Embodiment 2

[0047] An anti-skid and anti-icing-visible asphalt pavement material at night is provided, which comprises the following components in parts by mass:

[0048] 55 parts of steel slag coarse aggregate, 10 parts of waste glass fine aggregate, 26 parts of steel slag fine aggregate, 5 parts of filler containing phase change material, 4.7 parts of modified asphalt; wherein:

[0049] In the steel slag coarse aggregate, the gradation is 36 parts with a particle size of 9.5-16mm, and 19 parts with a particle size of 4.75-9.5mm;

[0050] The preparation of the above-mentioned anti-skid and anti-icing-visible asphalt pavement material at night comprises the following steps:

[0051] 1) Mix the steel slag coarse aggregate, waste glass fine aggregate and steel slag fine aggregate to obtain the mixed aggregate, heat it with the filler containing phase change material and modified asphalt respectively, at a temperature of 170°C, and keep it warm for 4 hours;

[0052] 2) Put the heated mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-skid anti-icing night visible asphalt pavement material and a preparation method thereof. The asphalt pavement material comprises the following components in parts by mass: 50-65 parts of steel slag coarse aggregate, 20-30 parts of steel slag fine aggregate, 10-15 parts of waste glass fine aggregate, 3-5 parts of filler containing a phase change material and 3.8-5.1 parts of modified asphalt. The preparation method comprises the following steps: mixing coarse and fine aggregates, and then respectively heating the coarse and fine aggregates, the filler containing the phase-change material and the modified asphalt; then putting the heated mixed aggregate into a stirring pot which is preheated in advance for stirring, and then sequentially and respectively adding the heated modified asphalt and the filler containing the phase-change material for stirring. The asphalt pavement material has good skid resistance and wear resistance, the thermal performance of the pavement is improved, and the icing resistance of the pavement is improved; meanwhile, the night visibility of the asphalt pavement is enhanced, the preparation process is simple, the cost is low, the source is wide, and high-added-value utilization of the steel slag and the waste glass is realized.

Description

technical field [0001] The invention belongs to the technical field of road engineering materials, and in particular relates to an anti-skid and anti-icing-visible asphalt pavement material at night and a preparation method thereof. Background technique [0002] Road traffic safety has always been the focus of widespread attention, especially in winter road traffic safety has its particularity and importance. For example, in areas with a large temperature difference between day and night, the road surface is very icy in winter, which will reduce the friction between the wheels and the road surface, which is easy to slip and cause traffic accidents. At the same time, poor visibility conditions for driving at night, especially on suburban roads, rural roads and expressways far away from urban areas, and poor roadside lighting also increase traffic safety hazards. Asphalt pavement is comfortable to drive, easy to maintain, and high in traffic efficiency. It is the mainstream p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/0075C04B2201/10C04B2201/50C04B18/142C04B14/42C04B14/28C04B14/024C04B24/26
Inventor 陈美祝张建伟杨天元吴少鹏程明朱云升刘全涛谢君
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap