An epoxy ester resin, water-based acrylic technology, applied in coatings, anti-corrosion coatings, etc., can solve the problems of loss of anti-corrosion performance and decline of epoxy active groups, and achieve high weather resistance, low VOC emissions, and high anti-corrosion properties. Effect

Pending Publication Date: 2021-06-18
西北永新涂料有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a water-based acrylic modified epoxy ester resin to solve the problem that the introduction of hydrophilic groups in the existing method leads to the loss of part of the epoxy active group and the decline in its anti-corrosion performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne acrylic acid modified epoxy ester resin as well as preparation method and application thereof
  • Waterborne acrylic acid modified epoxy ester resin as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047]A waterborne acrylic modified epoxy ester resin, comprising the following components in mass percentage: epoxy ester resin 42%, epoxy phosphate ester 4%, styrene 5%, methyl methacrylate 8%, butyl acrylate 1 %, acrylic acid 3%, benzoyl peroxide 0.5%, tert-butyl hydroperoxide 0.07%, ethylene glycol monobutyl ether 1.5%, dimethylethanolamine 5%, deionized water 29%.

[0048] The epoxy ester resin is prepared from the following raw materials in mass percentage: 35% linoleic acid, 1.3% crotonic acid, 27% E20 epoxy resin, 0.013% zinc oxide, 4% xylene, ethylene glycol Monobutyl ether 30%.

[0049] The epoxy phosphate is prepared according to the following mass percentages of raw materials: 60% of E20 epoxy resin, 1% of phosphoric acid, and 38% of ethylene glycol monobutyl ether.

[0050] A kind of preparation method of waterborne acrylic acid modified epoxy resin, comprises the following steps:

[0051] A. Add epoxy ester resin and epoxy phosphate into the reaction kettle, ra...

Embodiment 2

[0073] A water-based acrylic modified epoxy ester resin, comprising the following components in mass percentage: epoxy ester resin 38%, epoxy phosphate ester 6%, styrene 6%, methyl methacrylate 9%, butyl acrylate 2 %, acrylic acid 4%, benzoyl peroxide 0.7%, tert-butyl hydroperoxide 0.09%, ethylene glycol monobutyl ether 1.7%, dimethylethanolamine 6%, deionized water 31%.

[0074] The epoxy ester resin is prepared from the following raw materials in mass percentage: 33% linoleic acid, 1.5% crotonic acid, 29% E20 epoxy resin, 0.015% zinc oxide, 5% xylene, ethylene glycol Monobutyl ether 33%.

[0075] The epoxy phosphate is prepared from the following raw materials in mass percentage: E20 epoxy resin 58%, phosphoric acid 2%, ethylene glycol monobutyl ether 40%.

[0076] A kind of preparation method of waterborne acrylic acid modified epoxy resin, comprises the following steps:

[0077] A. Add epoxy ester resin and epoxy phosphate into the reaction kettle, raise the temperature ...

Embodiment 3

[0098]A water-based acrylic modified epoxy ester resin, comprising the following components in mass percentage: epoxy ester resin 41%, epoxy phosphate ester 5%, styrene 5.11%, methyl methacrylate 8.4%, butyl acrylate 1.2% %, acrylic acid 3.1%, benzoyl peroxide 0.6%, tert-butyl hydroperoxide 0.08%, ethylene glycol monobutyl ether 1.6%, dimethylethanolamine 5.6%, deionized water 30%.

[0099] The epoxy ester resin is prepared according to the following mass percentage raw materials: 34% linoleic acid, 1.4% crotonic acid, 28% E20 epoxy resin, 0.014% zinc oxide, 4.5% xylene, ethylene glycol Monobutyl ether 32%.

[0100] The epoxy phosphate is prepared from the following raw materials in mass percentage: 59% of E20 epoxy resin, 1.5% of phosphoric acid, and 39% of ethylene glycol monobutyl ether.

[0101] A kind of preparation method of waterborne acrylic acid modified epoxy resin, comprises the following steps:

[0102] A. Add epoxy ester resin and epoxy phosphate into the reacti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Impact strengthaaaaaaaaaa
Flexibilityaaaaaaaaaa
Login to view more

Abstract

The invention discloses waterborne acrylic modified epoxy ester resin as well as a preparation method and application thereof, belongs to the field of chemical engineering, and solves the problem that the corrosion resistance of existing hydrophilic resin is reduced. The resin comprises epoxy ester resin, epoxy phosphate, styrene, methyl methacrylate, butyl acrylate, acrylic acid, benzoyl peroxide, tert-butyl hydroperoxide, ethylene glycol monobutyl ether, dimethylethanolamine and deionized water. The preparation method comprises the following steps: heating the epoxy ester resin and the epoxy phosphate; dropwise adding a mixed solution of the styrene, methyl methacrylate, butyl acrylate, acrylic acid and benzoyl peroxide; adding the tert-butyl hydroperoxide; cooling and vacuumizing; adding the dimethylethanolamine for a neutralization reaction, and adding the deionized water for emulsification and dispersion. The waterborne acrylic modified epoxy ester resin is applied to water-based industrial anticorrosive paint. The water-based anticorrosive paint prepared from the waterborne acrylic modified epoxy ester resin has the characteristics of quick drying and high weather resistance of acrylic resin, and also has the characteristics of high adhesive force, high corrosion resistance and the like of epoxy resin.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to a water-based acrylic modified epoxy ester resin and a preparation method thereof. Background technique [0002] Coatings are polymer functional material products that provide supporting protection and surface decoration for many industries in the national economy. Among them, water-based industrial coatings are emerging new environmentally friendly coating products, which belong to the category of new materials for national strategic emerging industries. In 2019, my country's paint production has reached 24.388 million tons, making it the world's largest paint production and consumption country. However, in stark contrast to the rapid development of output, the share of domestic environmental protection coatings is very low, especially the market share of water-based industrial coatings is very low due to the constraints of key technologies and backward key material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F283/10C08F212/08C08F220/14C08F220/18C08F220/06C09D151/08C09D5/08
CPCC08F283/105C09D151/08C09D5/08C08F212/08C08F220/14C08F220/1804C08F220/06
Inventor 肖菲雍涛孙学军史芳沅杨敬霞王海彤姚兆鹏吴柏君
Owner 西北永新涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap