Selective contact area buried solar cell and back contact structure thereof

A solar cell and back contact technology, applied in the field of solar cells, can solve the problems of high groove width control requirements, poor passivation effect, etc., to solve the problem of high groove width control requirements, loose width control requirements, and good internal back reflection effect of effect

Pending Publication Date: 2021-08-24
ZHEJIANG AIKO SOLAR ENERGY TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the embodiments of the present invention is to provide a back contact structure of a solar cell, aiming to solve the existing problems of high requirements for groove width control and poor passivation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Selective contact area buried solar cell and back contact structure thereof
  • Selective contact area buried solar cell and back contact structure thereof
  • Selective contact area buried solar cell and back contact structure thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] The first embodiment of the present invention provides a back contact structure of a solar cell. For the convenience of description, only the parts related to the embodiment of the present invention are shown. Refer to Figure 1-Figure 10 As shown, the back contact structure of the solar cell provided by the embodiment of the present invention includes:

[0086] Grooves arranged at intervals on the back side of the silicon substrate 10;

[0087] A first dielectric layer 20 disposed on the back side of the silicon substrate 10;

[0088] a first doped region 30 disposed on the first dielectric layer 20 and disposed in the groove;

[0089] a second doped region 40 disposed on the first dielectric layer 20 and outside the groove;

[0090] A second dielectric layer 50 disposed between the first doped region 30 and the second doped region 40, the second dielectric layer 50 is at least one layer and its refractive index decreases sequentially from the back of the silicon sub...

Embodiment 2

[0130] The second embodiment of the present invention provides a selective contact area buried solar cell. For the convenience of description, only the parts related to the embodiment of the present invention are shown. Refer to Figure 1-Figure 10 As shown, the selective contact area buried solar cell provided by the embodiment of the present invention includes:

[0131] silicon substrate 10;

[0132] The back contact structure described in the foregoing embodiments on the back side of the silicon substrate 10; and

[0133] The third dielectric layer 90 is disposed on the front surface of the silicon substrate 10 .

[0134] Further, in an embodiment of the present invention, the second dielectric layer 50 and the third dielectric layer 90 can be prepared by preparing the front and back sides of the silicon substrate 10 respectively through the same process, and at this time, the third dielectric layer 90 can be The structure is the same as that of the second dielectric laye...

Embodiment 3

[0141] The third embodiment of the present invention provides a method for fabricating a selective contact region buried solar cell. For the convenience of description, only the parts related to the embodiment of the present invention are shown. Refer to Figure 11 As shown, the selective contact region buried solar cell manufacturing method provided in the embodiment of the present invention is used to prepare the selective contact region buried solar cell as described in the foregoing embodiments. Specifically, the method includes:

[0142] Step S11, creating a plurality of grooves arranged at intervals on the back surface of the silicon substrate;

[0143] Wherein, before step S11, it should also include preprocessing the silicon substrate;

[0144] The above pretreatment includes cleaning the silicon substrate and removing the damaged layer. Specifically, including:

[0145] (1) RCA standard cleaning, remove particles and organic matter on the surface of the silicon subs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention is suitable for the technical field of solar cells, and provides a selective contact area buried solar cell and a back contact structure thereof. The back contact structure comprises grooves arranged on the back of a silicon substrate at intervals; a first dielectric layer, arranged on the back surface of the silicon substrate; a first doped region, arranged on the first dielectric layer and arranged in the groove; a second doped region, arranged on the first dielectric layer and arranged outside the groove; a second dielectric layer, arranged between the first doped region and the second doped region, and the number of the second dielectric layer being at least one; and a conductive layer disposed on the first doped region and the second doped region. According to the back contact structure provided by the invention, the problems of high control requirement on the width of the groove and poor passivation effect in the prior art are solved.

Description

technical field [0001] The invention belongs to the technical field of solar cells, in particular to a selective contact region buried solar cell and its back contact structure. Background technique [0002] In crystalline silicon solar cells, the efficiency loss of the cell can be divided into two aspects: electrical loss and optical loss. Shielding of surface metal grid lines. [0003] Among them, the passivated metal contact structure has remarkable electrical properties, and can obtain low contact resistivity and low surface recombination at the same time. This structure consists of an ultra-thin tunnel oxide layer and N-type doped or P-type doped polysilicon layer. . Since the light absorption of the doped polysilicon layer is a "parasitic" absorption, that is, it does not contribute to the photo-generated current, so the passivated metal contact structure is mostly used on the back of the cell, so that the front surface can completely avoid the shielding of the metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01L31/0224H01L31/0216H01L31/0352H01L31/056H01L31/068H01L31/18
CPCH01L31/022441H01L31/02167H01L31/02168H01L31/035272H01L31/056H01L31/0682H01L31/1804H01L31/1868Y02E10/547Y02E10/52H01L31/0747H01L31/035281H01L31/0516H01L31/068
Inventor 邱开富王永谦杨新强陈刚
Owner ZHEJIANG AIKO SOLAR ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap