High-gloss alloy material and preparation method thereof
An alloy material and high-gloss technology, applied in the field of alloy materials, can solve the problems of environmental protection and poor flame retardancy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] The present invention proposes a high-gloss alloy material, including the following raw materials in parts by weight: 50 parts of PC, 10 parts of ABS, 5 parts of flame retardant, 0.1 part of anti-dripping agent, 1 part of compatibilizer, 1 part of HDPE, lubricating 0.1 part of antioxidant, 0.5 part of primary antioxidant, 0.5 part of secondary antioxidant, 0.5 part of synergist, 1 part of low temperature resistant agent, and 1 part of heat stabilizer;
[0026] Its preparation method comprises the following steps:
[0027] S1: Mix PC, ABS, flame retardant, anti-dripping agent, compatibilizer, HDPE, lubricant, primary antioxidant, secondary antioxidant, synergist, low temperature resistant agent, heat stabilizer, and the mixing time is 30min, mixing speed is 200r / min, makes compound;
[0028] S2: Add the mixture into the twin-screw extruder, melt and extrude to obtain the extrudate. The temperatures of the 1-9 sections of the twin-screw extruder are: 180°C, 240°C, 240°C,...
Embodiment 2
[0031] The present invention proposes a high-gloss alloy material, including the following raw materials in parts by weight: 60 parts of PC, 12 parts of ABS, 8 parts of flame retardant, 0.3 parts of anti-dripping agent, 3 parts of compatibilizer, 3 parts of HDPE, lubricating 0.3 parts of antioxidant, 0.7 parts of primary antioxidant, 0.8 part of secondary antioxidant, 0.7 part of synergist, 3 parts of low temperature resistant agent, and 3 parts of heat stabilizer;
[0032] Its preparation method comprises the following steps:
[0033] S1: Mix PC, ABS, flame retardant, anti-dripping agent, compatibilizer, HDPE, lubricant, primary antioxidant, secondary antioxidant, synergist, low temperature resistant agent, heat stabilizer, and the mixing time is 40min, mixing speed is 250r / min, makes compound;
[0034] S2: Add the mixture into the twin-screw extruder, melt and extrude to obtain the extrudate. The temperatures of the 1-9 sections of the twin-screw extruder are: 180°C, 240°C,...
Embodiment 3
[0037] The present invention proposes a high-gloss alloy material, including the following raw materials in parts by weight: 69 parts of PC, 14 parts of ABS, 11 parts of flame retardant, 0.4 parts of anti-dripping agent, 4 parts of compatibilizer, 4 parts of HDPE, lubricating 0.4 part of antioxidant, 0.9 part of primary antioxidant, 0.9 part of secondary antioxidant, 0.9 part of synergist, 4 parts of low temperature resistant agent, 4 parts of heat stabilizer;
[0038] Its preparation method comprises the following steps:
[0039] S1: Mix PC, ABS, flame retardant, anti-dripping agent, compatibilizer, HDPE, lubricant, primary antioxidant, secondary antioxidant, synergist, low temperature resistant agent, heat stabilizer, and the mixing time is 50min, mixing speed is 300r / min, makes compound;
[0040]S2: Add the mixture into the twin-screw extruder, melt and extrude to obtain the extrudate. The temperatures of the 1-9 sections of the twin-screw extruder are: 180°C, 240°C, 240°C...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com