A fishing bait, a mouldable composition for manufacturing the fishing bait, a method for manufacturing the fishing bait and a use of the mouldable composition
A molding composition and fishing bait technology, which can be used in artificial fish bait, fishing accessories, fishing, etc., can solve the problems of useless, biodegradable bait, easy degradation, and non-optimal performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0053] A base solution comprising 26.1 kg of gelatin having a gel strength of 280 g (280 Bloom), 63.9 kg of water, 26.3 kg of corn syrup and 78.8 kg of glycerin was brought to a boil. Water was evaporated in a vacuum chamber (negative pressure -0.6 bar to -0.33 bar; temperature 92.5°C to 99.5°C) in such a way that the total solids content reached 80 wt%. A mixture comprising a fish attractant additive and a crosslinking agent is added to the base solution to form a moldable composition. The amount of the mixture is 9% by weight of the total mass of the moldable composition. The moldable composition is poured into oiled molds to form fishing lures.
[0054] The following results were obtained:
[0055] A.9
[0056] B.7
[0057] C.7
[0058] D.9
[0059] E.5
Embodiment 2
[0061] A base solution comprising 62.2 kg of gelatin with a gel strength of 280 g (280 Bloom), 62.2 kg of water, 53.7 kg of corn syrup and 53.7 kg of glycerin was brought to a boil. Water was evaporated in a vacuum chamber (negative pressure -0.6 bar to -0.33 bar; temperature 92.5°C to 99.5°C) in such a way that the total solids content reached 80 wt%. A mixture comprising a fish attractant additive and a crosslinking agent is added to the base solution to form a moldable composition. The amount of the mixture is 9% by weight of the total mass of the moldable composition. The moldable composition is poured into oiled molds to form fishing lures.
[0062] The following results were obtained:
[0063] A.9
[0064] B.7
[0065] C.8
[0066] D.9
[0067] E.6
Embodiment 3
[0069] A base solution comprising 26.5 kg of gelatin with a gel strength of 280 g (280 Bloom), 65 kg of water and 103.5 kg of glycerin was boiled. The water was evaporated in a vacuum chamber (negative pressure -0.6 bar; temperature 92°C to 96°C) in such a way that the total solids content reached 80% by weight. A mixture comprising a fish attractant additive and a crosslinking agent is added to the base solution to form a moldable composition. The amount of the mixture is 9% by weight of the total mass of the moldable composition. The moldable composition is poured into oiled molds to form fishing lures.
[0070] The following results were obtained:
[0071] A.9
[0072] B.9
[0073] C.9
[0074] D.9
[0075] E.6-7
PUM
| Property | Measurement | Unit |
|---|---|---|
| molecular weight | aaaaa | aaaaa |
| molecular weight | aaaaa | aaaaa |
| molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More