Negative wide-temperature-phase liquid crystal composition material and application thereof

A liquid crystal composition, negative technology, applied in liquid crystal materials, nonlinear optics, optics, etc., can solve problems such as poor viewing experience, low display contrast, unstable display, etc., to improve the influence of operating voltage, display In terms of stability, improve the effect of displaying low contrast

Active Publication Date: 2021-12-14
重庆汉朗精工科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to improve the problems existing in the prior art, the present invention provides a negative wide temperature phase liquid crystal composition, which is used to improve the problems of low display contrast and poor viewing experience in vehicle-mounted liquid crystals, as well as problems caused by harsh outdoor work. Display instability caused by the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative wide-temperature-phase liquid crystal composition material and application thereof
  • Negative wide-temperature-phase liquid crystal composition material and application thereof
  • Negative wide-temperature-phase liquid crystal composition material and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0094] According to the composition of the liquid crystal composition in Table 1, the liquid crystal composition was prepared with reference to the above-mentioned method of the present invention, and poured into a test box for performance testing. The measured physical parameters are shown in Table 1.

[0095] The composition and test data of the liquid crystal composition of table 1 embodiment 1

[0096]

[0097]

[0098] In Example 1, the material has characteristics such as higher clearing point, wider wide-temperature phase working range, higher voltage retention rate and lower ion concentration, and is applied in vehicle-mounted liquid crystal displays to a large extent. The display quality of the car LCD is guaranteed.

Embodiment 2

[0100] According to the composition of the liquid crystal composition in Table 2, the liquid crystal composition was prepared with reference to the above-mentioned method of the present invention, and poured into a test box for performance testing. The results of the measured physical parameters are shown in Table 2.

[0101] The composition and test data of the liquid crystal composition of table 2 embodiment 2

[0102]

[0103]

[0104] In embodiment 2, this material has characteristics such as higher clearing point, wider wide temperature phase working range, and higher voltage retention rate and lower ion concentration, is applied in the vehicle-mounted liquid crystal display, improves to a great extent The display quality of the car LCD is guaranteed.

Embodiment 3

[0106] According to the composition of the liquid crystal composition in Table 3, the liquid crystal composition was prepared with reference to the above-mentioned method of the present invention, and poured into a test box for performance testing. The results of the measured physical parameters are shown in Table 3.

[0107] The composition and test data of the liquid crystal composition of table 3 embodiment 3

[0108]

[0109]

[0110] The clearing point of the material in Example 3 is higher, it has a wider working range of wide temperature phase, and excellent quality parameters.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a negative wide-temperature-phase liquid crystal composition material and application thereof, and belongs to the technical field of liquid crystal materials. The negative wide-temperature-phase liquid crystal composition material comprises, by mass, 1-34% of a monomeric compound with a structure as shown in a general formula I; 0.5-20% of a monomeric compound with a structure as shown in a general formula II; 2-68% of a monomeric compound with a structure as shown in a general formula III; and 2-86% of a monomeric compound with a structure as shown in a general formula IV. The material has a high clearing point, a low melting point and a wide phase temperature range, is suitable for a wide-temperature liquid crystal display, and is particularly suitable for a vehicle-mounted liquid crystal display. The negative wide-temperature-phase liquid crystal composition can significantly improve the problems of low display contrast, poor viewing feeling and the like of vehicle-mounted liquid crystal, and solves the problem of poor working stability of a display device caused by a harsh outdoor environment of the vehicle-mounted liquid crystal.

Description

technical field [0001] The invention relates to a negative wide temperature phase liquid crystal composition material and its application. The liquid crystal composition material can be used in the liquid crystal display industry, especially for vehicle-mounted liquid crystal display devices, so as to solve the problems caused by the harsh outdoor environment of vehicle-mounted liquid crystals. The problem of causing poor working stability of a display device belongs to the technical field of liquid crystal materials. Background technique [0002] With the rapid development of liquid crystal materials, the application fields of liquid crystal compounds have been significantly expanded to various display devices, electro-optic devices, electronic components, sensors and so on. For example, clocks, tablets, measuring machines, automotive panels, TV and computer monitors can be seen everywhere in life. According to the dielectric properties, liquid crystal materials are furthe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More