90 DEG C flexible polyvinyl chloride elastomer sheath material

A soft polyvinyl chloride and polyvinyl chloride resin technology, applied in the field of 90 ℃ soft polyvinyl chloride elastomer sheath material, can solve the problem of softness and aging resistance, poor durability, low molecular plasticizer migration, Easy to plastic deformation and other problems, to achieve the effect of excellent migration resistance, good processing performance and high cost performance

Pending Publication Date: 2021-12-21
杭州永通新材料有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to prepare PVC with lower hardness, the traditional method is to add a large amount of low-molecular-weight plasticizers to reduce its hardness and increase its flexibility. However, this method will reduce the mechanical properties an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 90 DEG C flexible polyvinyl chloride elastomer sheath material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] This 90℃ soft polyvinyl chloride elastomer sheathing material includes the following components:

[0050] Polyvinyl chloride resin: 100 parts,

[0051] Plasticizer: 50 parts,

[0052] Filler: 20 parts,

[0053] Processing modifier: 20 parts,

[0054] Flame retardant: 15 parts,

[0055] Stabilizer: 8 parts,

[0056] Lubricant: 1.5 parts,

[0057] Antioxidant: 1 part.

[0058] The polyvinyl chloride resin is a polyvinyl chloride resin with an average degree of polymerization of 1300.

[0059] The plasticizer is one or more of trioctyl trimellitate, polyester plasticizer, dioctyl sebacate, dioctyl terephthalate, and epoxidized soybean oil.

[0060] The filler is one or more of nano calcined kaolin, nano calcium carbonate, superfine ground calcium carbonate, talcum powder and white carbon black.

[0061]The processing modifier is one or more of acrylate core-shell copolymer, chlorinated polyethylene, nitrile rubber, EPDM rubber, ethylene-butylene copolymer, ethylene...

Embodiment 2

[0078] This 90℃ soft polyvinyl chloride elastomer sheathing material includes the following components:

[0079] Polyvinyl chloride resin: 100 parts,

[0080] Plasticizer: 80 parts,

[0081] Filler: 50 parts,

[0082] Processing modifier: 50 parts,

[0083] Flame retardant: 40 parts,

[0084] Stabilizer: 16 parts,

[0085] Lubricant: 5 parts,

[0086] Antioxidant: 3 parts.

[0087] The polyvinyl chloride resin is a polyvinyl chloride resin with an average degree of polymerization of 2500.

[0088] The plasticizer is one or more of trioctyl trimellitate, polyester plasticizer, dioctyl sebacate, dioctyl terephthalate, and epoxidized soybean oil.

[0089] The filler is one or more of nano calcined kaolin, nano calcium carbonate, superfine ground calcium carbonate, talcum powder and white carbon black.

[0090] The processing modifier is one or more of acrylate core-shell copolymer, chlorinated polyethylene, nitrile rubber, EPDM rubber, ethylene-butylene copolymer, ethylen...

Embodiment 3

[0107] This 90℃ soft polyvinyl chloride elastomer sheathing material includes the following components:

[0108] Polyvinyl chloride resin: 100 parts,

[0109] Plasticizer: 60 parts,

[0110] Filler: 33 parts,

[0111] Processing modifier: 32 parts,

[0112] Flame retardant: 31 parts,

[0113] Stabilizer: 11 parts,

[0114] Lubricant: 3 parts,

[0115] Antioxidant: 2 parts.

[0116] The polyvinyl chloride resin is a polyvinyl chloride resin with an average degree of polymerization of 1900.

[0117] The plasticizer is one or more of trioctyl trimellitate, polyester plasticizer, dioctyl sebacate, dioctyl terephthalate, and epoxidized soybean oil.

[0118] The filler is one or more of nano calcined kaolin, nano calcium carbonate, superfine ground calcium carbonate, talcum powder and white carbon black.

[0119] The processing modifier is one or more of acrylate core-shell copolymer, chlorinated polyethylene, nitrile rubber, EPDM rubber, ethylene-butylene copolymer, ethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a 90 DEG C flexible polyvinyl chloride elastomer sheath material, and belongs to the technical field of new materials. The problem of poor stability in the prior art is solved. The 90 DEG C flexible polyvinyl chloride elastomer sheath material comprises the following components: 100 parts of polyvinyl chloride resin, 50 to 80 parts of a plasticizer, 20 to 50 parts of a filler, 20 to 50 parts of a processing modifier, 15 to 40 parts of a flame retardant, 8 to 16 parts of a stabilizer, 1.5 to 5 parts of a lubricant and 1 to 3 parts of an antioxidant. The 90 DEG C flexible polyvinyl chloride elastomer sheath material has high stability.

Description

technical field [0001] The invention belongs to the technical field of new materials and relates to a 90°C soft polyvinyl chloride elastomer sheathing material. Background technique [0002] With the emergence and development of polymer materials, fire accidents are also increasing. The flame retardant technology of polymer materials has emerged at the historic moment. The insulation and sheath of wires and cables are mostly made of polymer flame retardant materials. Serialization, diversification and performance evaluation The introduction of flame retardant test standards has promoted the development of flame retardant cable technology. [0003] Due to the lessons of cable fires, flame retardant cable technology has made great progress in recent years, and flame retardant cables have become an inevitable trend in cable development, thus actively promoting the flame retardant of PVC materials and the development of new products. [0004] Polyvinyl chloride (PVC) resin is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L51/00C08L23/28C08L9/02C08L23/16C08L23/08C08K13/06C08K13/04C08K13/02C08K3/26C08K3/34C08K3/38C08K3/22C08K5/12C08K5/09C08K7/26H01B3/44
CPCC08L27/06H01B3/443C08L2201/02C08L2203/202C08K2003/2265C08K2003/2224C08K2003/2227C08K2003/387C08L51/00C08L23/286C08L9/02C08L23/16C08L23/0815C08K13/06C08K13/04C08K13/02C08K3/26C08K3/34C08K3/2279C08K3/38C08K3/22C08K5/12C08K5/09C08K7/26
Inventor 刘云龙周方鸣程国中
Owner 杭州永通新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap