Low-light marble ceramic tile with uniform luminosity and preparation method of low-light marble ceramic tile

A technology for ceramic tiles and marble, which is applied to the field of low-gloss marble ceramic tiles and the preparation thereof, can solve the problem of high polishing amount of the surface of ceramic tiles, and achieve the effects of reducing gloss, clear and rich colors, and simple preparation process.

Active Publication Date: 2022-04-05
清远市简一陶瓷有限公司 +1
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the amount of polishing on the surface of ceramic tiles is relatively high, resulting in a large amount of waste residue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-light marble ceramic tile with uniform luminosity and preparation method of low-light marble ceramic tile
  • Low-light marble ceramic tile with uniform luminosity and preparation method of low-light marble ceramic tile
  • Low-light marble ceramic tile with uniform luminosity and preparation method of low-light marble ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～9、 comparative example 1～2

[0024] The contents of each component in the surface glaze and dry glaze of the marble ceramic tiles of Examples 1-9 and Comparative Examples 1-2 are shown in Table 1.

[0025] The basic surface glaze of the ceramic tiles of Examples 1-9 and Comparative Examples 1-2 is composed of the following components in mass percentage: SiO 2 48.33%, Al 2 o 3 26.31%, CaO 6.43%, MgO 3.09%, K 2 O 1.77%, Na 2 O 3.22%, ZnO 0.06%, FeO 3 0.2%, TiO 20.1%, BaO 3.69%, P 2 o 5 0.04%, ZrO 2 0.02%, loss on ignition 6.71%, and the remainder impurities.

[0026] The aluminum water of the marble ceramic tiles of Examples 1-9 and Comparative Examples 1-2 is composed of the following components in mass percentage: 51.59% of aluminum oxide dry powder, 0.39% of sodium tripolyphosphate, 0.31% of sodium carboxymethylcellulose, water 47.72%.

[0027] The polished glaze of the marble ceramic tiles of Examples 1 to 9 and Comparative Examples 1 to 2 is composed of the following components in mass p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-light marble ceramic tile with uniform luminosity and a preparation method thereof, and relates to the technical field of ceramic tiles. The low-light marble ceramic tile with uniform luminosity comprises a green body and a glaze layer, the glaze layer is formed by superposing a cover glaze layer, an ink-jet printing layer and a dry granular glaze layer from bottom to top; the cover glaze layer is prepared from the following components in percentage by mass: 98.68 to 99.34 percent of basic cover glaze and 0.66 to 1.32 percent of molten aluminum; the ink-jet printing layer is used for printing corresponding patterns and colors on the green brick coated with the cover glaze layer by an ink-jet printer according to surface effect requirements; the dry granular glaze layer is prepared from the following components: stamp-pad ink, printing paste, dry granules and polishing glaze; the weight ratio of the dry granules to the polishing glaze in the dry granule glaze layer is (1-6): (15-45). The marble ceramic tile provided by the invention has the advantages of soft and comfortable effect, good wear resistance, simple preparation process, low cost, no need of changing the existing production line, and simple popularization.

Description

technical field [0001] The invention relates to the technical field of ceramic tiles, in particular to a low-gloss marble ceramic tile with uniform luminosity and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the requirements for home decoration effects are getting higher and higher. In recent years, ceramic tiles have been widely used and can be used in various places, including family living space, office space, public areas, etc. There is a huge demand for ceramic tiles that play a decorative role. Divided by gloss, there are matt ceramic tiles, soft light ceramic tiles and bright ceramic tiles on the market; the so-called matt ceramic tiles generally refer to bricks with a gloss of 10 to 30 degrees; Bricks with a degree of 30 to 60 degrees; bright ceramic tiles refer to bricks with a glossiness > 60 degrees; bright bricks are mainly polished bricks and full glazed tiles. Traditional ceramic tiles have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C03C8/00C03C8/04
Inventor 黄少卿邓波区邦熙李道杰李志豪
Owner 清远市简一陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap