Casting extruding compound shaping method of magnesium alloy automobile hub

A technology for composite forming of automobile hubs, which is applied in the direction of wheels, web-type wheels, vehicle parts, etc., can solve the problems of high production cost, complicated process, and many equipments, and achieve the goals of small grain size, simplified process, and reduced production cost Effect

Inactive Publication Date: 2006-04-26
ZHONGBEI UNIV
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method makes the wheel hub made of magnesium alloy material have good structure and mechanical properties, but the process is complicated, more equipment is required, the investment is large, and the production cost is very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Casting extruding compound shaping method of magnesium alloy automobile hub

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] figure 1 Shown is the automobile wheel hub, which is a typical part of ring and disk parts, and its structure and shape are very complex. The magnesium alloys suitable for casting and extrusion composite forming automobile hubs include Mg-Mn, Mg-AL-Zn and Mg-Zn- Alloys such as Zr. In this specific implementation, the Mg-Zn-Zr alloy MB15 magnesium alloy is selected.

[0012] Magnesium alloy automobile wheel hub cast-extrusion composite forming method, its specific process and steps are as follows:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a casting-extrusion compound forming method for a magnesium alloy automobile wheel hub, which adopts a casting process to make a billet with a reasonable original structure and shape, and is characterized in that there are pre-forming, upsetting extrusion forming, isothermal extrusion, and fine shaping processes; wherein: casting After the billet and pre-forming, the pre-allocation required for the extrusion process that fills the mold cavity is left; the critical deformation control method is used to control the deformation degree, deformation rate and deformation temperature in the process of upsetting extrusion forming and isothermal extrusion. And control it within the scope of its permission; spray graphite lubricant in the mold. In order to prevent the grain growth caused by reheating and reduce the mechanical properties, the temperature of the forming blank gradually decreases with the increase of the process. The wheel hub produced by the method has fine crystal grains, good mechanical performance and surface quality. It is also suitable for use in the manufacture of other magnesium alloy ring and disc parts.

Description

1. Technical field [0001] The invention belongs to the casting and extruding forming technology of magnesium alloy, in particular to the casting-extruding composite forming method of magnesium alloy automobile wheel hub and ring or disc-shaped parts. 2. Background technology [0002] With the development of the domestic automobile industry, especially the continuous innovation of high-end automobiles, in order to reduce the weight of the automobile itself, improve fuel efficiency, reduce emission pollution, and ensure automobile safety, magnesium alloy materials are increasingly favored by automobile manufacturers. and has begun to be applied. For ring-disc parts such as automobile wheels, gravity casting, ingot-die forging, ingot-die forging-rolling and other methods are currently used to manufacture them. For example: "Research on Magnesium Alloy Automobile Wheel Casting" published in "Casting Technology" magazine in May 2001, the conclusion of the research on the product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21K1/40B21C23/00B60B3/06C22F1/06
Inventor 张治民王强李保成张星李国俊
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com