Weft knitted fabric
A technology of weft knitting and weft direction, which is applied in weft knitting, knitting, textiles and papermaking, and can solve the problems of poor stretchability, poor wearing comfort, and hard hand feeling
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0092] [Example 1]
[0093] The PTT with reduced viscosity (ηsp / c)=0.8 was spun at a spinning speed of 1200 m / min at a spinning temperature of 265°C to obtain an undrawn yarn. Then, the undrawn yarn was stretched and twisted under the conditions of a hot roll temperature of 60°C, a hot plate temperature of 140°C, a stretching ratio of 3 times, and a stretching speed of 800 m / min to obtain a stretched yarn of 84 dtex / 36f. The strength, elongation, elastic modulus, elastic recovery rate at 10% elongation, and organic boiling water shrinkage rate of the stretched yarn are 2.9 cN / dtex, 45%, 24 cN / dtex, 94% and 14%, respectively.
Example Embodiment
[0100] [Example 2]
[0101] The two raw yarns obtained in Example 1 were combined into a 167dtex / 72f raw yarn, and the raw yarn was used to wale 22.0cm / 100 stitches in a No. 32 circular knitting machine (compared to the later described The fiber of Comparative Example 2 was knitted with the woven length of the fiber (condition length 10%) to produce 44 courses / 2.54 cm, 46 wales / 2.54 cm density of smooth fabric natural color cloth.
[0102] This woven natural color cloth was subjected to the same treatment as in Example 1 to obtain a fabric of 56 courses / 2.54 cm and 58 wales / 2.54 cm. The evaluation results of the obtained fabric are shown in Table 1.
Example Embodiment
[0107] [Example 3]
[0108] The two raw yarns obtained in Example 1 were combined to make a 167dtex / 72f raw thread, and the raw thread was woven on a No. 22 circular knitting machine with a length of 32.8cm / 100 wales (compared to that described later). The condition of the PET fiber of Comparative Example 3 (10% length) was knitted to produce a natural color fabric of a smooth fabric with a density of 32 courses / 2.54 cm, 36 wales / 2.54 cm.
[0109] This woven natural color cloth was treated in the same manner as in Example 1 to obtain a woven fabric of 40 courses / 2.54 cm and 44 wales / 2.54 cm. The evaluation results of the obtained woven fabric are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Bulk density | aaaaa | aaaaa |
Shrinkage | aaaaa | aaaaa |
Boiling water shrinkage | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap