Methanol electro-oxidizing-catalyzing electrode, preparing process and application thereof

A catalytic electrode and electro-oxidation technology, applied in the direction of material electrochemical variables, etc., can solve the problems of molecular chain growth difficulties, low polymerization oxidation potential, polymer overoxidation, etc., to achieve lower methanol oxidation potential, small adsorption capacity, and high conductivity small effect

Inactive Publication Date: 2005-09-14
XIAMEN UNIV
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the polymerization oxidation potential of aniline monomers with electron-donating substituents is low. When chemical oxidation polymerization is used, it is easy to cause polymer overoxidation in a strong oxidative polymerization medium, and if the monomer is oxidized to a quinone structure, it is difficult to carry out the integration with The coupling of active growing chains leads to difficulty in molecular chain growth and low molecular weight of products, so the selection of polymerization conditions and methods is very important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Methanol electro-oxidizing-catalyzing electrode, preparing process and application thereof
  • Methanol electro-oxidizing-catalyzing electrode, preparing process and application thereof
  • Methanol electro-oxidizing-catalyzing electrode, preparing process and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Dissolve PDMAn(HCl) in DMF to make a DMF solution with a concentration of 3.0mg / mL, and use a micro-vortex mixer to aid in dissolution; take a certain amount of polymer solution and coat it on the surface of a platinum disk electrode, and place it in an infrared rapid drying box Internal drying for 15 minutes, the polymer film modified electrode is obtained, and the adhesion amount of the polymer on the electrode surface is 0.3 mg·cm -2 .

[0032] In the single-chamber electrolytic cell, the polymer membrane modified electrode is used as the working electrode, the platinum sheet electrode is used as the auxiliary electrode, and the saturated calomel electrode is used as the reference electrode. The experiment was carried out on a CHI660 electrochemical comprehensive tester, and its attached computer software can be used for the collection and processing of experimental data. The above-mentioned PDMAn(HCl) polymer membrane modified electrode was placed in 1.0 mg / mL H 2...

Embodiment 2

[0037] PDMAn(HClO 4 ) was dissolved in DMF, and dissolved with a micro-vortex mixer with a concentration of 5.0 mg / mL; a certain amount of polymer solution was coated on the surface of a platinum disk electrode, and dried in an infrared rapid drying oven for 15 minutes to obtain the polymer Membrane modified electrode, the adhesion amount of polymer on the electrode surface is 0.6mg·cm -2 .

[0038] In the single-chamber electrolytic cell, the polymer membrane modified electrode is used as the working electrode, the platinum sheet electrode is used as the auxiliary electrode, and the saturated calomel electrode is used as the reference electrode. The experiment was carried out on a CHI660 electrochemical comprehensive tester, and its attached computer software can be used for the collection and processing of experimental data. The above PDMAn (HClO 4 ) polymer membrane modified electrode placed in 1.0mg / mL H 2 PtCl 6 In the 1.0mol / L HCl solution, the potential cycle scann...

Embodiment 3

[0040] Dissolve PDMAn (TSA) in DMF, and use a micro-vortex mixer to aid dissolution, with a concentration of 13.0 mg / mL; take a certain amount of polymer solution and coat it on the surface of a platinum disk electrode, and dry it in an infrared rapid drying oven for 15 minutes. The polymer film modified electrode was obtained, and the adhesion amount of the polymer on the electrode surface was 0.8 mg·cm -2 .

[0041] In the single-chamber electrolytic cell, the polymer membrane modified electrode is used as the working electrode, the platinum sheet electrode is used as the auxiliary electrode, and the saturated calomel electrode is used as the reference electrode. The experiment was carried out on a CHI660 electrochemical comprehensive tester, and its attached computer software can be used for the collection and processing of experimental data. The above-mentioned PDMAn (TSA) polymer membrane modified electrode was placed in 1.0 mg / mL H 2 PtCl 6 In a 1.0mol / L HCl solution,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Adhesion amountaaaaaaaaaa
Login to View More

Abstract

The invention discloses a menthol electro oxidation catalyst electrode, its process method and application, wherein the electrode relates to a metallization membrane modification electrode and is used as an electrochemical sensor for catalyzing menthol electro oxidation.A charged strong electron donating group polyaniline derivant poly-2,5-dimethoxybenzamine metallization membrane modification electrode comprises inert electrode base, conductive polymer membrane and catalyzer, wherein, polymer adhesion amount on the surface of base electrode is 0.3-1.0mgíñcm-2.The method comprises following steps: mixing PDMAn mixed with alcaine in N,N-dimethyl formamide or tetrahydrofuran to get 1.0í½10.0mg / mL liquor; coating liquor on electrode surface and drying it; changing coating times to adjust polymer adhesive materials; placing electrode in HCI liquor; conducting periodic scan or directional scan and changing times to get modification electrode with different platinum deposit rate.

Description

technical field [0001] The invention relates to a metallized film modified electrode, in particular to a polyaniline derivative poly2,5-dimethoxyaniline metallized film modified electrode with a strong electron-donating group and its preparation method, and it is used as a catalyst for methanol Electrochemical sensors for electrooxidation. Background technique [0002] Methanol, a chemical raw material, is a poisonous substance. When the human body ingests too much at one time, it will cause severe poisoning symptoms such as vomiting, abdominal pain, visual impairment, and shortness of breath, and eventually cause people to lose consciousness and die. Counterfeit alcohol made from methanol-containing industrial alcohol has blinded or killed many consumers. At present, the determination of methanol content mainly adopts gas chromatography, spectrophotometry and electrocatalysis. [0003] Depositing platinum (Pt) on a carrier to prepare an electrochemical catalyst suitable f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/02G01N27/30
Inventor 戴李宗许一婷陈江枫吴辉煌
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com