Drill bit for taphole of blast furnace and method for producing same

A manufacturing method and blast furnace tapping technology, which are applied to blast furnaces, blast furnace details, blast furnace parts and other directions, can solve the problem of unreasonable drill bit structure, shape or size, can not guarantee that the drill bit can open the iron hole at one time, and cannot guarantee that the drill bit will not be melted and damaged by molten iron. and other problems, to achieve the effect of not easy to break, improved flexural strength and toughness, and accelerated cutting speed

Active Publication Date: 2005-12-07
BAOSHAN IRON & STEEL CO LTD +1
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The "one-time opening method" is generally used in the existing blast furnaces at home and abroad, but most of them have the following deficiencies or shortcomings: (1) The shape or size of the drill bit structure is unreasonable, such as figure 1 , figure 2 As shown, the edges and corners of the blade 30 o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Drill bit for taphole of blast furnace and method for producing same
  • Drill bit for taphole of blast furnace and method for producing same
  • Drill bit for taphole of blast furnace and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] see image 3 , Figure 4 , the blast furnace taphole opening machine drill bit of the present invention comprises a base 3, 3 blades 5; the center of the base 3 is provided with a φ12.5mm air hole 2; 3 blades 5 are formed on the drill base 3 120 ° (as with 4 blades, then 90 ° arrangement) evenly arranged; the head of the blade 5 is a trapezoidal structure inclined to the central air hole 2 (the central axis of the drill bit is inclined), and the height h of the outer edge of the drill bit is 13-16 mm; the base 3 between the blades 5 is provided with a side air passage 4, which communicates with the central vent hole 2 and forms an angle α of 60° with the central vent hole 2, Caliber φ8~10mm; blade 5 head forms an angle β, angle β is 45°; described blade 5 trapezoid top width t is 8mm, and bottom width T is 25mm.

[0033] There is a straight pipe connection section 1 of a certain length at the bottom of the drill base 3, and the connection section 1 does not process ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a drill bit for taphole of blast furnace, which comprises a base and three blades, the base is provided with a venting hole in the center, and side air passages in communication with the central venting hole, the blades are in uniform distribution on the base, the head of the blades are of trapezoidal structure inclining toward the central venting hole, the exterior height of the drilling bit is 13-16 mm. The invention also discloses the process for making the dill bit.

Description

technical field [0001] The invention belongs to the technical field of ironmaking, and in particular relates to a drill bit for a blast furnace taphole opening machine drill rod and a manufacturing method thereof. technical background [0002] The slag and iron operation in front of the blast furnace is a very important link in the blast furnace production. The timely opening of the slag and iron can not only maintain the stability of the blast furnace production, but also maximize the ability of the blast furnace to resist the influence of external adverse factors. The blast furnace production process requires that the liquid level of slag and iron in the hearth is relatively low and relatively stable, otherwise there will be abnormal furnace conditions such as irregular feeding, wind pressure fluctuations, furnace temperature fluctuations, and even material collapse and slippage, which will endanger the normal production of the blast furnace. Therefore, the front operation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B7/12
Inventor 徐万仁敖爱国张永忠钱光华朱勇兴
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap