Aluminium-nickel metal welding bond and process for preparing the same

A technology of metal welding and welding strips, applied in the direction of metal layered products, chemical instruments and methods, lamination devices, etc., can solve problems such as technical difficulties that cannot be solved, and achieve the effect of low cost and easy implementation

Inactive Publication Date: 2006-02-15
广东风华新能源股份有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technology cannot solve the technical problems in the actual production of nickel and aluminum welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium-nickel metal welding bond and process for preparing the same
  • Aluminium-nickel metal welding bond and process for preparing the same
  • Aluminium-nickel metal welding bond and process for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Such as figure 1 , shows an aluminum-nickel metal welding strip, the welding strip includes an aluminum thin strip 1 and a nickel thin strip 2 connected by fusion welding, the aluminum thin strip 1 and the nickel thin strip 2 are stacked to form a three-layer alternating interlayer structure, and the welding Both the uppermost and the lowermost layers of the strip are nickel thin strips 2 . The thickness of the thin nickel strips 2 on different levels is equal to 0.05mm. , the thickness of the aluminum strip 1 is 0.15 mm. .

[0022] The nickel thin strip 2 is made of pure nickel, and the aluminum thin strip is made of alloy aluminum with an aluminum content greater than 95%.

Embodiment 2

[0024] Such as figure 2 , shows an aluminum-nickel metal welding strip, the welding strip includes an aluminum thin strip 1 and a nickel thin strip 2 connected by fusion welding, the aluminum thin strip 1 and the nickel thin strip 2 are stacked to form a five-layer alternating interlayer structure, and The uppermost layer and the lowermost layer of the welding strip are nickel thin strips 2 .

[0025] The nickel strips 2 on the uppermost and lowermost layers have a thickness of 0.1 mm. The thickness of the thin aluminum strip 1 on the second upper layer and the second lower layer is 0.1mm, and the thickness of the nickel thin strip 2 in the middle is 0.08mm.

[0026] The nickel thin strip 2 is made of alloy nickel with a nickel content greater than 90%, and the aluminum thin strip is made of pure aluminum.

[0027] method embodiment

[0028] Such as image 3 , shows a kind of equipment and method for preparing the Al-Ni metal welding strip described in Example 1, the method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to aluminum-nickel welding belt, which comprises connected thin aluminum belt and thin nickel belt to form complex layers structure; particularly, both the top and lowest layers of welding belt are thin nickel belts. This invention can realize easily the fusion welding between the said belts with high strength, reliable effect.

Description

【Technical field】 [0001] The invention relates to a component of an electronic component, more specifically, the invention relates to a lead-out wire of an electronic component and a production process thereof. 【Background technique】 [0002] Currently on the market, some electronic components need to use aluminum or aluminum alloys as conductors or electrodes inside. Although aluminum is a metal material with good electrical conductivity and very cheap, the crystal phase structure of aluminum is very loose. In the exposed air environment, aluminum conductors are very easy to form a dense oxide layer on the surface. Although this layer of dense oxide layer can prevent the deep aluminum from being further oxidized, it also makes aluminum or aluminum alloy conductors, It is difficult for the electrodes to be directly welded to the pins and electrodes of circuit boards, wires or other electrical components by simple soldering tools. In order to overcome the above shortcomings, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/01B32B37/06
Inventor 李尹庆包有江詹发荣郑华杰
Owner 广东风华新能源股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap