Method for manufacturing composite yarn

Abstract

The invention relates to a composite yarn making method, which is characterized by the following: (1) drafting the short fiber yarn by tridiaroller; setting a long yarn lead-in roller to drive by the driving system of former roller on the spinning machine; (2) entering the long yarn into long yarn lead-in roller and long yarn guide wheel then to enter into the former roller; (3) reaching the goal of drafting; (4) leading the chemical fiber long yarn through former roller with the drafted short yarn compound to enter into the feeder hook together; roiling the compound around the bobbin as cop. The invention solves the problem of quantitative adjustment chemical fiber long yarn and short fiber yarn tension ratio and entire spinning tension compatibility of shirting machine, which improves the spinning quality fundamentally by controlling the yarn cohesion closeness effectively. Otherwise, the method contains wider adjustment range, whose production fitness range is wide.

Description

Technical field [0001] The invention relates to a manufacturing method of composite yarn, which is compounded by chemical fiber filament and spun yarn. Background technique [0002] On May 10, 2002, the utility model patent specification with the authorized announcement number CN2377258Y disclosed a Sirofil spinning machine, which can not only complete the work of roving to become spun yarn after drafting, but also complete the normal withdrawal of spun yarn. Winding, feeding, tension adjustment and broken filament display control, and twisted and wound together with the drafted yarn to become a Sirofil two-component yarn. On September 1, 2004, the invention patent specification with the authorized announcement number CN1164813C disclosed a Sirofil spinning modulus compensation device, which makes filament and spun yarns with different modulus die before spinning. The quantity is close, so that the filament and spun yarn are wrapped uniformly and stably, so as to solve the proble...

AI Technical Summary

Problems solved by technology

[0003] The present invention mainly solves the problem that the tension ratio of chemical fiber filaments and spun yarns cannot be quantitatively adjusted, and provides a method that can quantitatively control the entry of chemical fiber filaments and spun yarns into the composite point according to different raw materials, different finenesses, and different elongation rates. Methods of manufacturing previously pretensioned composite yarns