Aluminum-powder resistance spot welding method for filling titanium-powder tempering nugget strength

A technology of resistance spot welding and aluminum alloy, applied in the direction of resistance welding equipment, welding medium, welding equipment, etc., can solve the problems of low solder joint strength, large welding current, difficulty in resistance spot welding, etc., and achieve inhibition of recovery and recrystallization, Improve the strength of solder joints and achieve the effect of microstructure

Inactive Publication Date: 2007-11-21
TIANJIN UNIV
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the good electrical and thermal conductivity of aluminum alloy, its surface often has a layer of dense oxide film, and its melting point temperature is more than three times the melting point temperature of aluminum alloy, which brings the resistance spot welding of aluminum alloy materials. great difficulty
Compared with ordinary carbon steel spot welding, aluminum alloy spot welding not only needs to use a larger welding current, the time is short, but also the strength of the welding spot is low, the welding quality is difficult to control, and it is far from meeting the requirements of continuous production, which seriously affects The application of aluminum alloy in the automotive industry, home appliances, aerospace and other fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Take two 30×10×0.8mm aluminum alloy plates, soak them in 10% NaOH solution for 10 minutes, then wash the surface of the aluminum alloy plates with water, and then put the aluminum alloy plates into 10% HNO 3 Soak in the solution for 10 minutes, wash the surface of the aluminum alloy plate with clean water and dry it, and determine 3 welding points on the surface-treated aluminum alloy plate along a straight line with a distance of 10mm between two welding points, and the welding area of ​​each welding point 18mm 2 , according to 0.0016g / mm on each welding spot between two aluminum alloy plates 2 Coating titanium powder, using a copper electrode with an end diameter of 4.5mm, and performing resistance spot welding with a welding current of 14000A, a welding time of 100ms and a welding pressure of 3000N, the tensile forces of the three welding points are: 1341.58N, 1357.49N and 1401.85N.

Embodiment 2

[0010] Take two 30×10×0.8mm aluminum alloy plates, soak them in 10% NaOH solution for 10 minutes, then wash the aluminum alloy surface with clean water, and then put the aluminum alloy plates into 10% HNO 3 Soak in the solution for 10 minutes, clean the surface of the aluminum alloy with clean water and dry it, and determine 3 solder joints on the surface-treated aluminum alloy plate along a straight line with a distance of 10mm between two solder joints, and the welding area of ​​each solder joint is 18mm 2 , according to 0.0023g / mm on each solder joint between two aluminum alloy plates 2 Coating titanium powder, using a copper electrode with an end diameter of 4.5mm, and performing resistance spot welding with a welding current of 14000A, a welding time of 100ms and a welding pressure of 3000N, the tensile forces of the three welding points are: 1825.84N, 1856.47 and 1899.89N.

Embodiment 3

[0012] Take two 30×10×0.8mm aluminum alloy plates, soak them in 10% NaOH solution for 10 minutes, then wash the surface of the aluminum alloy with clean water, and then put the aluminum alloy plates into 10% HNO 3 Soak in the solution for 10 minutes, clean the surface of the aluminum alloy with water and dry it. On the surface-treated aluminum alloy plate, the distance between two solder joints is 10mm along a straight line, and 3 solder joints are determined, and the welding area of ​​each solder joint is 18mm. 2 , according to 0.004g / mm on each welding spot between two aluminum alloy plates 2 Coating titanium powder, using a copper electrode with an end diameter of 4.5mm, and performing resistance spot welding with a welding current of 14000A, a welding time of 100ms and a welding pressure of 3000N, the tensile forces of the three welding points are: 1426.35N, 1486.47N and 1513.24.N.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention is concerned with aluminum alloy resistance spot welding method with filled titanium powder to melody the intension of melting core, belonging to aluminum alloy resistance spot welding technology. Dip the aluminum alloy plate into the NaOH liquid and clear with water and dip the plate into HNO3 liquid and clear with water and airing. Spread filled titanium powder at the welding spot of the two disposed aluminum alloy plate and carry the spot welding to the aluminum alloy plate with copper electrode with certain current, welding time and welding pressure. The method adds titanium powder in the core forming process of the resistance spot welding to form tiny compound spot of titanium powder among the metals and to restrain the restore and recrystallization of aluminum alloy. It refines the structure of melting core of aluminum alloy by enhancing the welding intension to over 2500 N.

Description

Technical field: [0001] The invention relates to an aluminum alloy resistance spot welding method filled with titanium powder to quench and temper nugget strength, which belongs to the aluminum alloy resistance spot welding technology. Background technique [0002] As we all know, resistance spot welding is one of the most important processing methods in the production of aluminum alloy sheets. However, due to the good electrical and thermal conductivity of aluminum alloy, its surface often has a layer of dense oxide film, and its melting point temperature is more than three times the melting point temperature of aluminum alloy, which brings the resistance spot welding of aluminum alloy materials. great difficulty. Compared with ordinary carbon steel spot welding, aluminum alloy spot welding not only needs to use a larger welding current, the time is short, but also the strength of the welding spot is low, the welding quality is difficult to control, and it is far from meet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K11/11B23K11/34B23K35/04B23K103/10
Inventor 罗震李青松单平王军董安
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap