Production line for magnesium strip and method thereof

A production line, magnesium strip technology, applied in the direction of manufacturing tools, metal rolling, metal rolling, etc., can solve the problems of equipment consumption, can not be put into production economically, and achieve the effect of reducing temperature loss and saving investment

Inactive Publication Date: 2011-09-07
THYSSENKRUPP STEEL EURO AG
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the problem with this is that this type of magnesium sheet can only be deformed when it is heated
Since the outlay of equipment, both the costs associated with its manufacture and the costs associated with the operation of the heating plant, is so significant that such equipment cannot practically be put into production economically

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production line for magnesium strip and method thereof
  • Production line for magnesium strip and method thereof
  • Production line for magnesium strip and method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] A production line 1 for manufacturing magnesium strip M includes a strip casting device 2, a bell annealing furnace 3 and a final rolling device 4 arranged coaxially successively along the feeding direction.

[0029] The strip casting device 2 is constituted according to the disclosed method, including a molten material bin 5, from which the molten magnesium is transported into the nozzle 6, and meanwhile, the nozzle of the nozzle 6 can extend to the location of the casting Between the two rolls 7,8 of the roll machine 9, there is a rolling gap 10 formed by the rolls 7,8, so that the molten magnesium ejected from the nozzle 6 is approximately horizontally and purposefully sent into the Rolling gap 10.

[0030]The molten magnesium in contact with the circumferential surfaces of the rollers 7, 8 solidifies into a casting at the contact point and is then rolled into a magnesium strip M at the narrowest point of the rolling nip 10. For precise transport of the magnesium st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The production line produces a thin magnesium strip (M). It has a winding device (18) to produce a coil (C) of the strip. It also has at least one device (13) to feed additional metal strip (S1, S2) into the winding device (18) and a device (14) to connect one end of the additional metal strip to one end of the main magnesium strip (M).

Description

technical field [0001] The invention relates to a production line and method for manufacturing magnesium strips. Background technique [0002] Due to the low density, the weight of magnesium is particularly low. At the same time, magnesium has similar strength properties to aluminum, so it is particularly advantageous to use magnesium to manufacture vehicle bodies, especially automobile bodies, because for body, always It is required to have lighter weight and higher strength and rigidity. [0003] In the article "Magnesium-Flachprodukte: Wirtschaftliches Verfahren für industrielle Fertigungentwickelt" by B. Engl published in the journal "in stahl und eisen 125 (2005) Nr. 4, Seiten 66-68", a cost-effective A method for inexpensively manufacturing magnesium panels. For this purpose, firstly, the magnesium melt is continuously cast into prefabricated strips with a maximum thickness of 50 mm, after taking into account a determined minor thickness, and at a defined rolling tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B39/00B21B15/00B65H18/28
CPCB22D11/0694B21B3/003B21B1/46
Inventor 安德列亚斯·克佩伯恩哈德·恩格尔迪特马尔·皮耶萨克曼弗雷德·宾格尔埃德加·拉文
Owner THYSSENKRUPP STEEL EURO AG