Kation S and anion N doped one-dimensional nano-structured Ti0* photocatalyst and method of producing the same

A nanostructure, photocatalyst technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problem of inability to use visible light to degrade environmental pollutants, achieve excellent visible light catalytic activity, and is conducive to Reactivity, effect of reducing treatment cost

Active Publication Date: 2008-04-02
ZHEJIANG ZHONGDE IND
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Publication number: CN1699636 (invention title: preparation method of one-dimensional single crystal titanium dioxide nanomaterial) discloses a method of combining hydrothermal su...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kation S and anion N doped one-dimensional nano-structured Ti0* photocatalyst and method of producing the same
  • Kation S and anion N doped one-dimensional nano-structured Ti0* photocatalyst and method of producing the same
  • Kation S and anion N doped one-dimensional nano-structured Ti0* photocatalyst and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 2.0 g nano-TiO 2 The powder is placed in 70ml of 10mol / L NaOH solution, and continuously stirred to obtain 2 mixed solution. Transfer the above solution to a 100ml autoclave, keep the temperature at 150°C for 24 hours, cool, pour off the supernatant, and wash with 0.05mol / L hydrochloric acid solution and deionized water to obtain a white precipitate of hydrotitanic acid. Prepare the above hydrotitanic acid and doping source thiourea in a certain ratio (1:2) with absolute ethanol to form a mixed suspension, stir evenly, ultrasonically treat, and dry at 80°C for 10 hours to obtain a homogeneous mixture of hydrotitanic acid and thiourea . The above mixture was placed in a tube furnace and calcined at 400 °C for 2 h under anaerobic conditions to obtain cation S and anion N double-doped one-dimensional nanostructured TiO 2 , the doping amount of sulfur is 0.9%, the doping amount of nitrogen is 1.2%, the crystal form is anatase, and the shape is a nanotube with a length of...

Embodiment 2

[0042] 3.0 g nano-TiO 2 The powder is placed in 60ml of 12mol / L KOH solution and continuously stirred to obtain 2 mixed solution. Transfer the above solution to a 100ml autoclave, keep the temperature at 180°C for 36 hours, cool, pour off the supernatant, wash with 6.5mol / L sulfuric acid solution and deionized water, and obtain a white precipitate of hydrotitanic acid. Prepare the above hydrotitanic acid and doping source thiourea in a certain ratio (1:4) with absolute ethanol to form a mixed suspension, stir for a certain period of time, ultrasonically treat, and dry at 100°C for 8 hours to obtain a uniform mixture of hydrotitanic acid and thiourea mixture. The above mixture was placed in a tube furnace and calcined at 500 °C for 1.5 h under aerobic conditions to obtain cation S and anion N double-doped one-dimensional nanostructured TiO 2 , the doping amount of sulfur is 1.5%, the doping amount of nitrogen is 1.8%, the crystal form is anatase, and the shape is a nanowire ...

Embodiment 3

[0045] 5.0 g TiO 2 Colloid is placed in the 15mol / LNaOH solution of 140ml, keeps stirring, obtains containing TiO 2 Colloidal mixed solution. Transfer the above solution to a 200ml autoclave, keep the temperature at 120°C for 48 hours, cool, pour off the upper clear layer, wash with 3.0mol / L nitric acid solution and deionized water, and obtain a white precipitate of hydrotitanic acid. The above-mentioned hydrotitanic acid and doping source thiourea were formulated into a mixed suspension with absolute ethanol in a certain ratio (1:1), stirred for a certain period of time, ultrasonically treated, and dried at 60°C for 12 hours to obtain a homogeneous mixture of hydrotitanic acid and thiourea. mixture. The above mixture was placed in a tube furnace and calcined at 550 °C for 3 h under aerobic conditions to obtain cation S and anion N double-doped one-dimensional nanostructured TiO 2 , the doping amount of sulfur is 0.5%, the doping amount of nitrogen is 0.8%, the crystal form...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses optical catalyst of one dimension nanometer structure TiO2 adulterated with cation S and anion N, the preparation method is as follows: (1) with water-thermal method, nanometer TiO2 powder, TiO2 colloid or Ti(OH)4 and alkaline solution is mixed together to form mixed suspension for water-thermal reaction; (2) cooling is adopted, sediment is filtered and cleaned and then white hydrogen titanium acid is realized; (3) hydrogen titanium acid, thiourea and solution is mixed to form mixed suspension, ultrasound treatment is conducted for stirring, and uniform mixture of hydrogen titanium acid and thiourea is realized after drying; (4) uniform mixture of hydrogen titanium acid and thiourea is calcinated and then optical catalyst of one dimension nanometer structure TiO2 adulterated with cation S and anion N is realized. Catalyst provided by the invention has one dimension structure and lavish active point position and is good for improvement of reaction activity, moreover, catalyst can accelerate mass transfer of pollutant to catalyst, and therefore photocatalysis rate is improved; special one dimension structure and non-metal dual adulteration of the invention lead to good visible-light catalytic activity.

Description

technical field [0001] The invention relates to a cation S and anion N double-doped one-dimensional nanostructure TiO 2 The preparation method and application of photocatalytic degradation of organic matter. The catalyst is mainly used in the technical field of indoor air pollution control. Background technique [0002] Indoor air pollution is 5-10 times higher than outdoor, and people spend 80-90% of their time indoors. To some extent, the impact of air pollution on human health is mainly indoors. According to the survey provided by China Standardization Association: 60% of diseases are caused by indoor air pollution. In the late 1990s, with the domestic housing reform and the improvement of people's living standards, especially the rapid development of the building materials industry and the rise of decoration, the pollution caused by decoration materials has become the main form of indoor pollution. [0003] Western developed countries have promulgated laws and regulat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J21/06A61L9/22
Inventor 吴忠标董帆赵伟荣王海强郭森
Owner ZHEJIANG ZHONGDE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap