Surface sizing agent and method for preparing same

A technology of surface sizing agent and initiator, applied in the field of papermaking, can solve the problems of difficult cleaning, high viscosity, no effect of paper wet strength, etc., achieve good surface strength and folding resistance, good emulsifying and dispersing properties, improve bonding The effect of fastness

Active Publication Date: 2008-04-16
CHINA BANKNOTE PRINTING & MINTING
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] (3) The viscosity of the PVA aqueous solution is relatively large, and a large amount of sizing liquid remains on the pressing roller, and then forms a film on the sizing roller, which is difficult to clean;
[0012] (4) The PVA film formed by hard hydrogen bonds has a high brittleness, which eventually leads to low folding resistance of the paper;
[0013] (5) It has almost no effect on impr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface sizing agent and method for preparing same
  • Surface sizing agent and method for preparing same
  • Surface sizing agent and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0078] Example 1

[0079] This embodiment is a soap-free emulsion surface sizing agent having a polymer of general formula I, wherein:

[0080] R is -CH 2 (CH 2 ) 6 CH 2 OH, X is Na + , n is 10~1000.

[0081] The surface sizing agent in this embodiment uses polyvinyl alcohol as the dispersant, four monomers of styrene, acrylate, acrylamide and maleic anhydride as the main raw materials. Under the action, the polymer surface sizing agent obtained by soap-free emulsion polymerization; wherein, the weight ratio of dispersant, monomer, initiator and crosslinking agent is:

[0082] Dispersant (polyvinyl alcohol): 50 parts;

[0083] Monomer: Styrene: 12 parts,

[0084] Acrylate: 18 parts,

[0085] Acrylamide: 10 parts,

[0086] Maleic anhydride: 8 parts;

[0087] Initiator (potassium persulfate): 2 parts;

[0088] Crosslinking agent (glyoxal): 15 parts.

[0089] Its preparation method mainly comprises the following steps:

[0090] (1), the preparation of polyvinyl alco...

Example Embodiment

[0093] Example 2

[0094] This embodiment is a soap-free emulsion surface sizing agent having a polymer of general formula I, wherein:

[0095] R is -CH 2 (CH 2 ) 16 CH 2 OH, X is K + , n is 10~1000.

[0096] The surface sizing agent in this embodiment uses polyvinyl alcohol as the dispersant, four monomers of styrene, acrylate, acrylamide and maleic anhydride as the main raw materials. Under the action, the polymer surface sizing agent obtained by soap-free emulsion polymerization; wherein, the weight ratio of dispersant, monomer, initiator and crosslinking agent is:

[0097] Dispersant (polyvinyl alcohol): 40 parts;

[0098] Monomer: Styrene: 20 parts,

[0099] Acrylate: 15 parts,

[0100] Acrylamide: 12 parts,

[0101] Maleic anhydride: 1 part;

[0102] Initiator (ammonium persulfate): 8 parts;

[0103] Crosslinking agent (glyoxal): 10 parts.

[0104] Its preparation method mainly comprises the following steps:

[0105] (1), the preparation of polyvinyl alcoho...

Example Embodiment

[0108] Example 3

[0109] This embodiment is a soap-free emulsion surface sizing agent having a polymer of general formula I, wherein:

[0110] R is -CH 2 (CH 2 ) 2 CH 2 OH, X is NH 4 + , n is 10~1000.

[0111] The surface sizing agent in this embodiment uses polyvinyl alcohol as the dispersant, four monomers of styrene, acrylate, acrylamide and maleic anhydride as the main raw materials. Under the action, the polymer surface sizing agent obtained by soap-free emulsion polymerization; wherein, the weight ratio of dispersant, monomer, initiator and crosslinking agent is:

[0112] Dispersant (polyvinyl alcohol): 60 parts;

[0113] Monomer: Styrene: 9 parts,

[0114] Acrylate: 21 parts,

[0115] Acrylamide: 5 parts,

[0116] Maleic anhydride: 15 parts;

[0117] Initiator (ammonium persulfate): 1 part;

[0118] Crosslinking agent (glutaraldehyde): 20 parts.

[0119] Its preparation method mainly comprises the following steps:

[0120] (1), the preparation of polyvin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a surface sizing agent which is soap-free emulsion of polymers with the following general formula I: (general formula I) wherein, R is selected from a saturated fatty alcohol group with carbon numbers of 1-18; X is selected from any one in Na<+>, K<+>, NH4<+>, etc; n is 10-1000. The sizing agent is a novel synthetic polymer surface sizing agent for paper, so surface sizing capability of paper can be greatly improved, binding fastness of paper and ink can be improved, surface strength of paper can be improved, etc.; besides, the invention also has the advantages that: few crust is provided during using process, cleaning is convenient, folding resistance of finished product is increased, wet strength is high, etc. The invention also discloses a preparation method of the sizing agent.

Description

technical field [0001] The invention belongs to the technical field of papermaking, in particular to a synthetic polymer surface sizing agent for papermaking. Background technique [0002] Sizing agents for papermaking refer to chemical additives added to improve the surface strength of paper and cardboard and prevent the diffusion and penetration of water-based liquids (such as writing ink). It is an important papermaking chemical with a large amount and a wide range of applications. [0003] According to the different ways of adding it in the papermaking process, the sizing agent for papermaking can be divided into two categories: (1) the sizing agent added to the pulp before the paper sheet is formed is called the pulp sizing agent; (2) ) is called a surface sizing agent that is applied to the surface of the cardboard after the paper sheet is formed. [0004] Since the sizing agent in the pulp is easily affected by production conditions (such as water quality, pH value,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/16D21H17/35D21H17/36
Inventor 田德卿沈一丁陈玉群李刚辉费贵强赵锦良
Owner CHINA BANKNOTE PRINTING & MINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap