Method for producing steel-scoria and mine-scoria cement by using steel-scoria ball milled waste mud

A technology for steel slag tailings and slag cement, applied in cement production and other directions, can solve the problems that steel slag cement is difficult to be widely recognized and affects the volume stability of steel slag cement.

Inactive Publication Date: 2008-05-07
LAIWU IRON & STEEL GRP
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high free calcium oxide and magnesium oxide contained in steel slag, which affects the volume stability of steel slag cement, it is difficult for steel slag cement to be widely recognized by the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0010] 2. Preparation method of steel slag tailings slag cement

[0011] The preparation method of steel slag tailings slag cement of the present invention, the steps are as follows:

[0012] (1) Use the steam produced by waste heat boilers in iron and steel enterprises as a heat source to heat-treat wet steel slag tailings at a temperature of 100°C-120°C, keep the water content of steel slag tailings below 4%, and break large pieces of gypsum to below 10mm ; Send the crushed steel slag tailings into the ball mill for grinding until the Blaine specific surface area is 450-470m 2 / kg;

[0013] (2) Grind silicate clinker, blast furnace slag and natural gypsum to Blaine specific surface area of ​​450-470m 2 / kg;

[0014] (3) The steel slag tailings processed in step (1) and the silicate clinker, blast furnace slag and natural gypsum processed in step (2) are dosed according to the following weight ratio: 20% to 40% of steel slag tailings, blast furnace slag 35% to 45%, silica...

specific Embodiment approach

[0020] The present invention will be further described below in conjunction with the examples, but not limited thereto.

[0021] The steel slag tailings used in the examples are the sludge produced by the converter steelmaking steel slag after wet ball mill grinding, water washing and iron selection, the silicate clinker is 525# ordinary Portland cement clinker, and the blast furnace slag is Blast furnace slag treated by granulation and water quenching, natural gypsum is ordinary natural dihydrate gypsum. The chemical composition of each raw material is shown in Table 1.

[0022] Table 1 raw material chemical composition table (mass percentage %)

[0023] raw material

Embodiment 1

[0024] Embodiment 1: steel slag tailings slag cement and preparation method thereof, the steps are as follows:

[0025] (1) Use the steam produced by the waste heat boiler of the iron and steel enterprise as a heat source to heat-treat the wet steel slag tailings at a temperature of 105°C, so that the water content of the steel slag tailings is about 3%, and the large pieces of gypsum are broken to less than 10mm; The final steel slag tailings are sent to a ball mill for grinding until the Blaine specific surface area is 460m 2 / kg;

[0026] (2) Grind silicate clinker, blast furnace slag and natural gypsum to Blaine specific surface area of ​​460m 2 / kg;

[0027] (3) The steel slag tailings, silicate clinker, blast furnace slag and natural gypsum processed through steps (1) and (2) are proportioned according to the following weight ratio: 40% of steel slag tailings, 35% of blast furnace slag, silicate 20% of clinker and 5% of natural gypsum are mixed in a mixer. Product pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production method of steel slag mud slag cement and applying the steel slag ball trail cement in the steel slag mud slag cement. The method comprises the steps as follows: firstly, the steel slag ball trail cement with high water content is dried and dehydrated through heat treatment so as to lower the water content of the steel slag trail cement to be below 4 percent; broken steel slag trail cement is delivered to a ball mill to have powder milling and silicate clinker, blast furnace slag and natural gypsum are matched according to a certain proportion then are mixed in a mixer, thereby producing the steel slag scoria cement of different labels. Adopting the solid castoff of steel enterprises effectively, the invention changes the waste into treasure by a simple production art. The production cost of cement is remarkably reduced.

Description

technical field [0001] The utility model relates to a method for producing steel slag slag cement by using steel slag ball mill tailings, which is a new invention in the field of building materials, in particular to a method for producing steel slag slag cement. Background technique [0002] Steel slag is a by-product produced in the steelmaking process of iron and steel enterprises, most of which are converter steel slags. At present, most of the converter steel slags of major domestic steel companies still adopt extensive wet treatment methods, that is, red hot steel slag is pumped with water. After quenching and cracking into block slag, the slag field is crushed, magnetically separated and screened. When the iron content (TFe content is about 20%) of the tailing slag after magnetic separation is high, except for a small part, it is used for the production of steel slag powder preparation Apart from cement, most of the tailings are used for road construction and landfill,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B7/147C04B7/21
CPCC04B7/153Y02P40/10C04B7/19C04B7/21
Inventor 刘智伟孙庆亮李志峰许倩王玮种振宇孙业新董晓春管山吉江丹刘永恒
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com