X80 steel made pipe fittings and manufacture technique thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of manufacturing process and steel pipe, applied in the field of pipe fittings and its manufacturing process, X80 steel, which can solve the problems of reduced performance of pipe fittings and unsatisfactory requirements
Active Publication Date: 2008-06-25
BC P INC CHINA NAT PETROLEUM CORP +2
View PDF1 Cites 26 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] The technical problem to be solved by the present invention is to overcome the disadvantages of common X80 steel in the manufacturing process of pipe fittings due to repeated heating and cooling, which can lead to reduced performance of pipe fittings and cannot meet the requirements, and provide a kind of X80 steel, its application, and the manufacturing process of the pipe fittings , the strength of the pipe fittings is greater than 555Mpa, and the low-temperature impact toughness is greater than 90J, which can fully meet the technical requirements of X80 pipe fittings. It is an X80 steel grade pipe fitting suitable for oil and natural gas pipelines.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment ( 1
[0023] The composition is C 0.15%, Si 0.2%, Mn 1.6%, P 0.015%, S 0.01%, Cr 0.15%, Mo 0.25%, Cu 0.2%, Ni 0.35%, Nb 0.1%, Ti 0.02%, V 0.06% The control-rolled steel plate made of X80 steel is pressed into a Φ1219×60mm X80 tee, and the forming temperature is 980±20°C. The final heat treatment process is: quenching temperature 970±20°C, heat preservation for 90min, and brine cooling at 630±20°C. It can be seen from Table 1 that the performance of the tee reaches the technical indicators specified by the X80 steel tee.
Embodiment ( 2
[0025] X80 steel with composition of C 0.1%, Si 0.2%, Mn 1.8%, P 0.012%, S 0.008%, Mo 0.3%, Cu 0.1%, Ni 0.5%, Nb 0.05%, Ti 0%, V 0.05% Control rolled steel plate, pressed into Φ1016×42mm X80 tee, forming temperature is 880±20℃. The final heat treatment process is: quenching temperature 990±20°C, heat preservation 70min, 620±20°C brine cooling. It can be seen from Table 1 that the performance of the tee reaches the technical indicators specified by the X80 steel tee.
Embodiment ( 3
[0027] The composition is C 0.08%, Si 0.1%, Mn 1.6%, P0.01%, S 0.006%, Cr 0.3%, Mo0.15%, Cu 0%, Ni 0.3%, Nb 0.08%, Ti 0.04%, V 0.03% X80 steel is made of controlled-rolled steel plate, pressed into Φ813×30mm X80 tee, and the forming temperature is 900±20°C. The final heat treatment process is: quenching temperature 980±20°C, heat preservation 60min, 580±20°C brine cooling. It can be seen from Table 1 that the performance of the tee reaches the technical indicators specified by the X80 steel tee.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
strength
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a pipeline made of X80 steel and a method for manufacturing the same. The chemical compositions are that: 0.06 to 0.1 percent of C, 0.1 to 0.3 percent of Si, 1.4 to 2.0 percent of Mn, less than or equal to 0.015 percent of P, 0.01 percent of S, 0 to 0.45 percent of Cr, 0 to 0.3 percent of Mo, 0 to 0.3 percent of Cu, 0 to 0.5 percent of Ni, 0.05 to 0.15 percent of Nb, 0 to 0.06 percent of Ti, 0 to 0.06 percent of V, Ceq controlled between 0.36 and 0.44 percent, Pcm controlled between 0.17 and 0.23 percent. The pipeline manufactured with the controlled rolled steel plate of the compositions by means of controlling the forming temperature, hardening heat, drawing temperature, cooling velocity, etc. has low-temperature impact toughness more than 90 J, completely meets the technical requirement on the X80 pipelines and is suitable to be used as X80 steel pipelines for oil and gas pipelines.
Description
technical field [0001] The invention belongs to the field of iron and steel, and in particular relates to an X80 steel, a manufactured pipe fitting and a manufacturing process thereof. Background technique [0002] Pipeline transportation of oil and gas has the advantages of safety, reliability, economy, energy saving, and high efficiency compared with other means of transportation. Therefore, with the continuous development of the world's oil industry, the construction of oil and gas pipelines around the world is developing rapidly, and its requirements for pipe performance are also increasing. higher. [0003] At present, large-scale pipe fittings generally adopt the production process of quenching and tempering after hot-pressing with molds on a press. This process is mainly used to manufacture low-strength pipe fittings, and there are less production and research on pipe fittings above X70 and X80 steel, especially thick-walled pipe fittings. [0004] Domestically, X80...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more