Method of using vanadium titanium rotary furnace steel slag as cement iron correction material

A converter steel slag and iron correction technology, applied in cement production and other directions, can solve the problems of sulfuric acid slag pollution, environmental impact, economic loss, etc., to achieve economic and social benefits, reduce cement production costs, and speed up comprehensive utilization. Effect

Inactive Publication Date: 2006-06-14
WASTE & OLD MATERIAL BRANCH OF PANGANG GROUP GANGCHENG ENTERPRISE CORP
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Panzhihua Iron and Steel Plant produces about 300,000 tons of steel slag every year. The current solution to this problem is to open up a slag yard and carry out slag dumping. However, as time goes by, the service life of the original slag yard is gradually shortening
For this reason, it is also necessary to find another land to open up a new slag yard, resulting in more economic losses and greater environmental pollution
On the other hand, the iron correction raw materials currently used by major cement plants have many problems such as sulfuric acid slag polluting the environment and high iron powder prices. For the further requirement of correcting raw materials, it is imminent to find a process that can replace iron correcting raw materials for cement production with vanadium-titanium converter steel slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of using vanadium titanium rotary furnace steel slag as cement iron correction material
  • Method of using vanadium titanium rotary furnace steel slag as cement iron correction material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The cement clinker obtained by mixing 5% steel slag powder, 69% limestone, 9% clay and other mixtures, grinding, calcining, cooling and grinding again, its compressive strength, stability, setting time It meets the requirements of the national standard of cement, and the proportion of steel slag powder is CaO: 39.5%; Fe 2 o 3 : 25.68%; SiO 2 : 13.69%; Al 2 o 3 : 3.86%; MFe≤1%; V 2 o 5 : 1.73%; TiO 2 ≤3%.

Embodiment 2

[0013] The cement clinker obtained by mixing 3% steel slag powder, 68% limestone, 7% clay and other mixtures, grinding, calcining, cooling and grinding again, its compressive strength, stability, setting time It meets the requirements of the national standard of cement, and the proportion of steel slag powder is CaO: 38.2%; Fe 2 o 3 : 22.86%; SiO 2 : 11.26%; Al 2 o 3 : 2.34%; MFe≤1%; V 2 o 5 : 1.568%; TiO 2 ≤3%.

Embodiment 3

[0015] The cement clinker obtained by mixing 3% steel slag powder, 70% limestone, 9% clay and other mixtures, grinding, calcining, cooling and grinding again, its compressive strength, stability, setting time It meets the requirements of the national standard of cement, and the proportion of steel slag powder is CaO: 38.2%; Fe 2 o 3 : 22.86%; SiO 2 : 11.26%; Al 2 o 3 : 2.34%; MFe≤1%; V 2 o 5 : 1.568%; TiO 2 ≤3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a method capable of using vanadium-titanium converter steel slag as cement iron correction raw material. Said method includes the following steps: cooling molten steel slag, breaking, magnetic separation to obtain steel slag powder, mixing steel slag powder, limestone and clay, grinding them, calcining, cooling and secondary grinding so as to obtain the invented cement clinker.

Description

technical field [0001] The invention relates to a method for processing converter steel slag and using it as a raw material for correcting cement iron quality, in particular to a method for using vanadium-titanium converter steel slag as a raw material for cement iron quality correction. Background technique [0002] The Panzhihua Iron and Steel Plant produces about 300,000 tons of steel slag every year. The current solution to this problem is to open up a slag yard and carry out slag dumping. However, as time goes by, the service life of the original slag yard is gradually shortening . For this reason, it is also necessary to find another land to open up a new slag yard, thereby causing more economic losses and greater environmental pollution. On the other hand, the iron correction raw materials currently used by major cement plants have many problems such as sulfuric acid slag polluting the environment and high iron powder prices. For the further requirement of correctin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/147
CPCY02P40/10
Inventor 陈启斌杨岳新戚明强钱强邹峰
Owner WASTE & OLD MATERIAL BRANCH OF PANGANG GROUP GANGCHENG ENTERPRISE CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com