Polylactic acid/thermoplastic starch extrusion blow molding film and its producing method and application

A thermoplastic starch, extrusion blow molding technology, applied in the field of biodegradable polymer materials, to achieve the effects of easy handling, cost reduction and simple process

Active Publication Date: 2008-08-06
江苏橙桔生物降解塑料有限公司
View PDF4 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no successful preparation of high-strength biodegradable polymer blown film materials composed of polylactic acid and starch or modified starch.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The present invention will be further described below in conjunction with the embodiment in the table:

[0038]

Ingredients (parts by weight)

Reality

apply

example

one

Reality

apply

example

two

Reality

apply

example

three

Reality

apply

example

Four

Reality

Shi

example

Fives

Reality

apply

example

six

Reality

apply

example

seven

Reality

apply

example

Eight

Reality

apply

example

Nine

Reality

apply

example

ten

Polylactic acid (weight average molecular weight

200,000)

80

80

70

65

60

55

50

40

20

80

therm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weight distributionaaaaaaaaaa
crystallinityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polylactic acid / thermoplastic starch extrusion blown film, a relative production method and an application. The invention mixes polylactic acid, the copolymer fatty group-aromatic polyester, thermoplastic starch, flexibilizer, nucleating agent, lubricant, anti-oxidant, reinforcing agent and anti-ultraviolet agent into a twin-screw extruder, at suitable operation temperature and screw rod rotation speed, to be extruded and granulated, and uses extrusion blowing method to produce polylactic acid / thermoplastic starch extrusion blown film product. The inventive polylactic acid / thermoplastic starch extrusion blown film can be used as packaging film, clingfilm, one-time film and agricultural film. And the production method has simple process, easy operation, low cost, degradable property, easy treatment and reduced white pollution.

Description

technical field [0001] The invention belongs to the field of biodegradable polymer materials, in particular to a polylactic acid / thermoplastic starch extruded blown film and its production method and application. Background technique [0002] There are more and more materials such as packaging film bags, plastic wrap bags, disposable film bags (such as garbage bags, tablecloths, cleaning bags), agricultural films (mulch film, covering film, shed film) and other materials used in human daily life. Most of them are petroleum-based plastics. Although they are cheap, they have poor degradability and become a source of pollution that damages the environment after use. [0003] When environmental protection became a hot spot of social concern, more and more degradable plastic products began to emerge. However, most of the current degradable products are not perfect and failed to achieve the expected effect. At present, the degradable masterbatches made at home and abroad include:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08L67/04C08L3/02C08K5/20B29C49/04C08K3/34C08L71/08C08L1/28
Inventor 邹俊周海骏郭伟杰汤继俊朱治愿
Owner 江苏橙桔生物降解塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products