Filled polyamide molding material with low water absorption rate

A technology for filling polyamide, polyamide molding, used in transmission systems, electrical components, etc.

Inactive Publication Date: 2008-08-13
EMS CHEM AG
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the water absorption of the molding material, no information is given

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0052] Table 1 characterizes the materials used in Examples and Comparative Examples.

[0053] Table 1

[0054] Material

Product name

Relative viscosity, 20℃,

0.5wt.-% meta-formazan

phenol

Component weight ratio

manufacturer

PA 614

-

1.93

-

EMS-CHEMIE

AG, Switzerland

PA6I / 6T

GRIVORY G21

1.52

2 / 1

EMS-CHEMIE

AG, Switzerland

[0055] glass fiber

Vetrotex

EC10-4, 5MM

99B

-

-

Saint-Gobain

Vetrotex, France

carbon fiber

Tenax

HTA 5N51 6MM

-

-

Toho Tenax

Europe GmbH,

Germany

potassium carbonate

Millicarb-OG

-

-

Plüss-Staufer

AG, Switzerland

PA66

Radipol A45

2.7

in H 2 SO 4 middle, 1

wt.-%

-

Radi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to filled polyamide molding materials, in particular polyamide molding materials with medium filler content, which are producible from a polyamide blend and for example by compounding with chopped or endless fibers on two-screw extruders, and have a combination of reduced water absorption and good mechanical properties, which results in very good dimensional stability and reduced variation of the electrical properties of the produced molded part, such as an antenna housings of stationary or mobile communication devices. The thermoplastic polyamide molding materials according to the present invention are suitable for manufacturing molded parts and other semi-finished or finished parts, for example by extrusion, injection molding, pressing, direct process or direct compounding, respectively, wherein the compounded polyamide molding material is directly processed by injection molding or other shaping methods.

Description

technical field [0001] The present invention relates to filled polyamide molding materials, especially polyamide molding materials with a moderate filler content, which are produced from polyamide mixtures and, for example, on a twin-screw extruder by mixing with chopped fibers or Manufactured from a mixture of endless fibers and exhibits a combination of reduced water absorption and good mechanical properties, which leads to excellent dimensional stability of the molded parts produced, e.g. antenna housings for fixed or mobile communication devices And the change of electrical properties is reduced. [0002] The thermoplastic polyamide molding materials according to the invention are suitable for the production of molded parts and other semi-finished or finished parts, for example produced by extrusion, injection molding, stamping, direct processing or direct mixing, respectively, wherein the mixed polyamide injection molding materials Direct processing by injection molding ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/06C08K7/00C08J5/00H04B1/02H04B1/08B29B7/90
CPCC08L77/06C08L77/02C08L77/04C08L77/10C08L2205/02C08L2666/20C08L77/00C08K7/04C08J5/00C08K3/00
Inventor 奥纳夫·雷克辛艾蒂安·艾佩里
Owner EMS CHEM AG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com