Manual repair technique of coking chamber wall

A carbonization chamber and furnace wall technology, applied in the coking field, can solve the problems of affecting production and high cost, and achieve the effects of not wasting resources, reducing costs and improving service life

Active Publication Date: 2009-03-11
MCC BAOSTEEL TECH SERVICE
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the furnace is shut down for overhaul, it will not only be costly, but also affect production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manual repair technique of coking chamber wall
  • Manual repair technique of coking chamber wall
  • Manual repair technique of coking chamber wall

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0017] for figure 1 The carbonization chamber furnace wall 1 of the melted part 2 shown can be repaired by the following steps:

[0018] First, if figure 1 As shown, the repair personnel wear heat-insulating clothes, heat-insulating gloves and masks, and then remove the door of the carbonization chamber with a coke pusher. The heat shield 4 is vertically pushed into the part to be repaired in the carbonization chamber, and the top of the heat shield is fixed on the furnace frame 5, so that the part to be repaired is surrounded by an inverted "L"-shaped 90-degree heat shield;

[0019] Secondly, if figure 2 As shown, clean the graphite and sundries at the bottom of the furnace, spread the heat insulation blanket 3 and the walkway board, and then stick the heat insulation blanket on the furnace wall to be repaired and the furnace wall 1 around...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for manually mending the furnace wall of a carbonization chamber. The process comprises the following: (1) a step of fixing a heat isolation rack: according to a mending part, the heat isolation rack is manufactured; the surface of the heat isolation rack is coated by a heat isolation blanket; the heat isolation rack is pushed to the part of the furnace wall needing mending in the carbonization chamber; and the top of the heat isolation rack is fixed on a furnace frame; (2) a step of paving the heat isolation blanket; graphite and impurities on the bottom of the furnace are cleaned up; the heat isolation blanket and a passage plate are paved; and the heat isolation blanket is stuck on the furnace wall to be treated mended and the furnace wall on the periphery of the heat isolation rack; (3) a step of constructing the inside of the furnace of the carbonization chamber: after the furnace walls at two sides are stuck with the heat isolation blanket, no naked fire is determined to eject; and the mending construction is carried out; and (4) a step of detaching and mending a melting loss part. The mending process can carry out mending in the carbonization chamber under the environment of high temperature of 1,000 DEG C around, reduce cost, improve the service life of the coke furnace, does not influence production and is a feasible and effective method.

Description

technical field [0001] The invention belongs to the technical field of coking, and in particular relates to a process for artificially repairing the furnace wall of a carbonization chamber of a coke oven. Background technique [0002] The structure of the coke oven is composed of furnace roof, combustion chamber, carbonization chamber and flue. The temperature in the carbonization chamber is about 1300 degrees Celsius, mainly for coking. The carbonization chamber is mainly for storing coal. During the coking process, the tar and graphite produced adhere to the wall of the carbonization chamber. The long-term accumulation will collide with the entrance and exit of the coke pushing device, and the quality problems of the silica bricks on the wall of the carbonization chamber itself and Unavoidable errors made by the operator during the temperature adjustment process lead to serious melting loss of the silica bricks on the wall of the carbonization chamber. Due to the charact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10B29/02
Inventor 马汉林王进忠陈义
Owner MCC BAOSTEEL TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com