A vacuum glass and manufacturing method technology, applied in glass manufacturing equipment, glass molding, glass reshaping, etc., can solve the problems of vacuum glass stress concentration and stress unevenness, and achieve average plane stress, same performance, and convenient operation Effect

Inactive Publication Date: 2009-10-28
左树森
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the prior art and provide a method for manufacturing vacuum glass with uniform stress that can effectively solve the problems of stress concentration and uneven stress in vacuum glass. The vacuum glass manufactured by this method has a simple, scientific and reasonable process. Lower manufacturing cost and longer service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described in detail below through the specific examples, the following examples are only descriptive, not restrictive, and cannot limit the protection scope of the present invention with this.

[0024] A method for manufacturing stress uniform vacuum glass, the steps of the preparation method are:

[0025] (1). Set bonding points on the substrate glass:

[0026] Put a piece of glass as the substrate glass on the workbench, and set the bonding points uniformly on the plane. The bonding points can be arranged by a bushing mold or a silk screen. The spacing of the bonding points is 15-50mm. The diameter is 0.2-2mm, the height is 0.05-1mm, and it is in the form of dots or other shapes. The adhesive used for this bonding point is a glass adhesive commonly used in this industry.

[0027] (2). Bonding low melting point glass powder and solid support:

[0028] Stick low-melting point glass powder on the bonding point set on the substrate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a fabricating method of vacuum glass with uniform stress, which comprises the following steps: firstly, arranging bonding points on substrate glass; secondly, bonding low melting glass powder and solid support; thirdly, combining sheet and arranging a seal edge; fourthly, heating the sheet in a heating furnace; and fifthly, vacuumizing and sealing so that the vacuum glass can be obtained. The invention has simple process, convenient operation, low cost, high yield and high production efficiency, reduces the breakage rate to be less than 10 percent and is easy to realize the industrial massive production. The fabricated vacuum glass has uniform and consistent stress, good quality, high strength and long service life, is the creative development on the fabricating process of the vacuum glass, and has great promotion function on the development of the vacuum glass industry.

Description

technical field [0001] The invention belongs to the field of vacuum glass, in particular to a method for manufacturing vacuum glass with uniform stress. Background technique [0002] The sound insulation, heat insulation and thermal insulation properties of vacuum glass are much better than ordinary glass or interlayer glass, and its application prospect is very broad. There are following shortcoming in the manufacturing method of existing vacuum glass: 1. adopt artificially to bond uniformly distributed, spaced solid support column on flat glass, this solid support adopts metal nail, ball and glass nail, ball etc., and its stability is difficult Guaranteed, the bonding efficiency is low, time-consuming, and labor costs are too high; 2. Because the flatness of the two pieces of glass is difficult to keep consistent, the support effect of the solid support is poor, and the support stress of the glass is uneven, especially in vacuum glass. After vacuuming, local stress will b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03B23/203C03B23/24
Inventor 左树森
Owner 左树森
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap