Polished metal brick and production process thereof

A production process and metal technology, applied in the field of throwing metal bricks and their production processes, can solve the problems of poor dirt resistance and poor wear resistance, and achieve the effect of high dirt resistance.

Inactive Publication Date: 2012-10-03
台山市海棠陶瓷有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polished tiles are wear-resistant and bright, but not dirt-resistant, while glazed tiles have rich colors and patterns, but their wear resistance is worse than polished tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] (1) 15 parts of stucco, 7 parts of white clay, 3 parts of talc, 20 parts of feldspar, 10 parts of blank

[0017] Porcelain stone, 30 parts of porcelain sand and 15 parts of high-temperature sand are mixed into the ball mill and wet ball milled for 7 hours. After passing through an 80-mesh sieve, they are stirred in a mixing tank for 12 hours. After being dried into powder by a spray tower, they are pressed into shape by a press equipment. , combined into a drying kiln for drying to obtain a green body;

[0018] (2) Mix 3 parts of kaolin, 10 parts of calcite, 5 parts of burnt talc, 30 parts of feldspar, 5 parts of calcined zinc oxide, 5 parts of calcined aluminum, and then mix 42 parts of inert metal powder into the glaze, add copper powder or silver powder, and pass through Wet ball milling in a ball mill for 5 hours, and passing through a 100-mesh sieve to obtain glaze slurry;

[0019] (3) Apply 1 part of the glaze slurry prepared in the above (2) to 60 parts of the b...

Embodiment 2

[0023] (1) Mix 10 parts of stucco, 10 parts of white mud, 1 part of talc, 10 parts of feldspar, 12 parts of porcelain stone, 40 parts of porcelain sand and 17 parts of high-temperature sand into the ball mill for wet ball milling for 7 hours, and pass through 100 mesh After sieving, stir in a mixing tank for 24 hours, dry it into a powder through a spray tower, press it through a press equipment, and put it into a drying kiln for drying to obtain a green body;

[0024] (2) Mix 3 parts of kaolin, 10 parts of calcite, 5 parts of burnt talc, 50 parts of feldspar, 5 parts of calcined zinc oxide, 5 parts of barium carbonate, 10 parts of calcined aluminum, and 12 parts of inert metal powder into the glaze, and add rhodium powder or ruthenium powder, after wet ball milling in a ball mill for 4 hours, and passing through a 150 mesh sieve, the glaze slurry is obtained;

[0025] (3) Apply 1 part of the glaze slurry prepared in the above (2) to 80 parts of the body prepared in the above ...

Embodiment 3

[0029] (1) Mix 8 parts of stucco, 5 parts of white mud, 2 parts of talc, 15 parts of feldspar, 15 parts of porcelain stone, 35 parts of porcelain sand and 20 parts of high-temperature sand into the ball mill for wet ball milling for 8 hours, and pass through 110 mesh After sieving, stir in a mixing tank for 36 hours, dry it into a powder through a spray tower, press it through a press equipment, and put it into a drying kiln for drying to obtain a green body;

[0030] (2) Mix 6 parts of kaolin, 15 parts of calcite, 10 parts of calcite, 40 parts of feldspar, 2 parts of calcined zinc oxide, 15 parts of calcined aluminum, and then 12 parts of inert metal powder into the glaze, add copper powder, and pass through the ball mill Wet ball milling for 5 hours and passing through a 130-mesh sieve to obtain the glaze slurry;

[0031] (3) Apply 1 part of the glaze slurry prepared in the above (2) to 70 parts of the green bodies prepared in the above (1) by printing;

[0032] (4) Place t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses polished metal bricks and a production process thereof. The polished metal bricks are made from a green brick material and a glaze slip in a weight ratio of 60-80: 1. The green brick material comprises the following components in percentage by weight: 8 to 15 percent of plaster, 5 to 10 percent of white mud, 1 to 3 percent of talcum, 10 to 20 percent of feldspars, 10 to 15percent of pottery stone, 30 to 50 percent of ceramic sands and 15 to 20 percent of high-temperature sands; and the glaze slip comprises the following components in percentage by weight: 3 to 10 percent of kaoline, 10 to 20 percent of calcspar, 5 to 15 percent of calcined talcum, 30 to 50 percent of feldspars, 2 to 5 percent of calcined zinc oxide, 0 to 10 percent of barium carbonate, 5 to 15 percent of calcined aluminum and 12 to 42 percent of one or more than one inert metal powder selected from the group of copper, silver, palladium, rhodium, ruthenium, iridium or osmium. The production process comprises the following steps of: subjecting the green brick material to wet-method ball milling, screening, stirring and spray drying sequentially, the press molding the green brick material and drying the molded green brick material to obtain green bricks; subjecting a glaze to wet-method ball milling and screening to obtain the glaze slip; applying the glaze slip on the green bricks; and sequentially sintering, polishing and grinding the green bricks applied with the glaze slip to obtain the product. The polished metal bricks are wearable, shinning and dirt durable and have the effect of metal luster.

Description

technical field [0001] The invention relates to a ceramic tile and a production process thereof, in particular to a polished metal tile and a production process thereof. Background technique [0002] There are two main types of decorative tiles currently on the market: polished tiles and glazed tiles. Polished tiles are wear-resistant and bright, but not dirt-resistant, while glazed tiles have rich colors and patterns, but their wear resistance is worse than polished tiles. At the same time, with the increasing development of the economy and the improvement of people's living standards, as well as the diversification of needs and the continuous improvement of aesthetics, the pursuit of novelty, individuality, quality, and taste has become increasingly significant, especially the demand for new and noble decorative materials. Among them, decorative materials with metallic luster are very in line with consumers' needs for novelty and nobility. Therefore, it is the research g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/34C04B41/88
Inventor 唐硕度
Owner 台山市海棠陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap