Composite for manufacturing trash can and preparation method of composite

A technology for composite materials and trash cans, which is applied in the field of composite materials for manufacturing trash cans and its preparation. It can solve the problems of oil resistance, flammability, and dirt resistance, and achieve excellent oil resistance.

Inactive Publication Date: 2015-12-23
SUZHOU NETABHAPE COMPOSITE MATERIALS
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem solved: Aiming at the shortcomings of existing plastic trash cans such as aging, flammability, resistance to oil and dirt, the present invention provides a garbage can Composite material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A composite material for making garbage cans, which contains the following components in parts by mass: 35 parts of PVC resin, 10 parts of glass fiber, 10 parts of acrylonitrile-butadiene-styrene copolymer, 5 parts of ceramic fiber, ethyl orthosilicate 0.5 part of ester, 0.2 part of n-octyl phthalate, 0.1 part of phenyl phthalate, 0.1 part of diphenylamine, 2 parts of asbestos powder, 1 part of phosphite, 0.3 part of sodium alkylsulfonate, dimethyl 0.2 parts of silicone oil.

[0019] A preparation method for making a composite material for a trash can, the steps of the preparation method are as follows:

[0020] Step 1: Stir PVC resin, glass fiber, acrylonitrile-butadiene-styrene copolymer and ceramic fiber evenly in a high-speed mixer, and control the stirring speed to 600r / min;

[0021] Step 2: Then add ethyl orthosilicate, n-octyl phthalate, phenyl o-hydroxybenzoate, diphenylamine, asbestos powder, phosphite, sodium alkyl sulfonate, dimethyl Base silicone oil, heat...

Embodiment 2

[0024] A kind of composite material that is used for making trash cans, containing the following components in parts by mass: 55 parts of PVC resin, 25 parts of glass fiber, 25 parts of acrylonitrile-butadiene-styrene copolymer, 18 parts of ceramic fiber, ethyl orthosilicate 1.5 parts of ester, 0.8 part of n-octyl phthalate, 0.6 part of phenyl phthalate, 0.5 part of diphenylamine, 8 parts of asbestos powder, 7 parts of phosphite, 0.8 part of sodium alkylsulfonate, dimethyl 0.6 parts of silicone oil.

[0025] A preparation method for making a composite material for a trash can, the steps of the preparation method are as follows:

[0026] Step 1: Stir PVC resin, glass fiber, acrylonitrile-butadiene-styrene copolymer and ceramic fiber evenly in a high-speed mixer, and control the stirring speed to 800r / min;

[0027] Step 2: Then add ethyl orthosilicate, n-octyl phthalate, phenyl o-hydroxybenzoate, diphenylamine, asbestos powder, phosphite, sodium alkyl sulfonate, dimethyl Base ...

Embodiment 3

[0030] A composite material for making garbage cans, which contains the following components in parts by mass: 50 parts of PVC resin, 22 parts of glass fiber, 23 parts of acrylonitrile-butadiene-styrene copolymer, 15 parts of ceramic fiber, ethyl orthosilicate 1.3 parts of ester, 0.7 part of n-octyl phthalate, 0.5 part of phenyl phthalate, 0.4 part of diphenylamine, 7 parts of asbestos powder, 5 parts of phosphite, 0.7 part of sodium alkylsulfonate, dimethyl 0.5 parts of silicone oil.

[0031] A preparation method for making a composite material for a trash can, the steps of the preparation method are as follows:

[0032] Step 1: Stir PVC resin, glass fiber, acrylonitrile-butadiene-styrene copolymer, and ceramic fiber evenly in a high-speed mixer, and control the stirring speed to 700r / min;

[0033] Step 2: Then add ethyl orthosilicate, n-octyl phthalate, phenyl o-hydroxybenzoate, diphenylamine, asbestos powder, phosphite, sodium alkyl sulfonate, dimethyl Base silicone oil, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composite for manufacturing a trash can and a preparation method of the composite. The composite is prepared from, by mass, 35-55 parts of PVC resin, 10-25 parts of glass fibers, 10-25 parts of acrylonitrile-butadiene-styrene copolymer, 5-18 parts of ceramic fibers, 0.5-1.5 parts of tetraethoxysilane, 0.2-0.8 part of di-n-octyl ortho-phthalate, 0.1-0.6 part of phenyl salicylate, 0.1-0.5 part of diphenylamine, 2-8 parts of asbestos powder, 1-7 parts of phosphite ester, 0.3-0.8 part of alkyl sodium sulfonate and 0.2-0.6 part of simethicone. The trash can made of the composite is excellent in oil contamination resistance and dirt resistance, meanwhile, the trash can has antistatic, flame retardant, impact-resistant and aging-resistant performance, and the composite is a good material for manufacturing the trash for outdoor use.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a composite material for making trash cans and a preparation method thereof. Background technique [0002] The trash can is the place where the trash is placed. Most of the garbage cans are made of metal or plastic, and they are put into plastic bags when used. When there is too much garbage, the bags can be tied up and thrown away. Most trash cans have lids to prevent the smell of garbage from spreading, and some trash cans can be opened with a foot pedal. Trash cans are containers for "staining dirt and dirt" in people's lives, and they are also essential supplies in daily life. [0003] At present, most of the garbage cans on the market are made of plastic. Although the garbage cans made of plastic have the advantages of light weight, low cost, and high aesthetics, they are generally easy to age, flammable, not resistant to oil stains, and not durable. Dirty dow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L55/02C08L83/04C08K13/04C08K7/14C08K7/04C08K7/12C08K5/5415C08K5/12C08K5/134C08K5/18C08K5/524C08K5/42B29B9/06B29C47/92B29C48/92
Inventor 刘莉王爽邱晶
Owner SUZHOU NETABHAPE COMPOSITE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com