Ventilated round clutch rubber airbag and preparation method thereof

A technology of rubber airbags and clutches, which can be applied to other household appliances, applications, household appliances, etc., can solve the problems of not being able to achieve quantification due to demand, increase production costs, consume large energy, etc., achieve low density, increase density, and reduce costs. low effect

Pending Publication Date: 2019-07-05
HENAN DALIN RUBBER & TELECOMM APP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the vulcanization mode adopted by most enterprises at home and abroad is: use traditional vulcanization tanks for vulcanization, and use boilers to provide steam to vulcanize products, because vulcanization tanks cannot be quantitatively determined, especially in certain types of orders When the quantity is small or the demand for a certain product is small, the vulcanization of the vulcanization tank will consume a lot of energy, resulting in waste of resources and increased production costs
In addition, due to the large size of the vulcanization tank itself, the whole process from loading to unloading requires the cooperation of multiple people, which wastes manpower and poses a great safety hazard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Embodiment 1: a kind of ventilated circular clutch rubber air bag, comprise each raw material of following weight portion: comprise each raw material of following weight portion: 15 parts of butadiene rubber, 35 parts of polyurethane rubber, 15 parts of chloroprene rubber, 8 parts of zinc oxide , 2 parts of stearic acid, 3 parts of paraffin, 25 parts of carbon black N774, 1.5 parts of anti-aging agent A, 1.5 parts of anti-aging agent D, 0.5 parts of anti-aging agent 4010NA, 2.5 parts of graphene, 3 parts of petroleum pitch, 0.5 parts of accelerator M , accelerator TMTD 1.5 parts, sulfur 1.5 parts.

[0044] The above-mentioned preparation method of the ventilated circular clutch rubber airbag includes six process steps such as rubber mixing, calendering and cutting, extrusion, molding, vulcanization, and packaging. The specific processing steps are as follows:

[0045] A. Rubber mixing process:

[0046] ① Ingredients: According to the weight requirements of the producti...

Embodiment 2

[0068] Embodiment 2, the preparation method of this embodiment and embodiment 1 are basically the same, and the similarities will not be repeated. The difference is: a kind of ventilated round clutch rubber airbag, including each raw material of the following parts by weight: 25 parts of butadiene rubber , 55 parts of polyurethane rubber, 25 parts of neoprene rubber, 12 parts of zinc oxide, 3 parts of stearic acid, 5 parts of paraffin, 30 parts of carbon black N774, 2.5 parts of antioxidant A, 2.5 parts of antioxidant D, 1.5 parts of antioxidant 4010NA , 3.5 parts of graphene, 5 parts of petroleum pitch, 1.5 parts of accelerator M, 2.5 parts of accelerator TMTD, and 2.5 parts of sulfur.

Embodiment 3

[0069] Embodiment 3, the preparation method of the present embodiment and embodiment 1 are basically the same, and the similarities will not be repeated. The difference is: a kind of ventilated circular clutch rubber airbag, including each raw material of the following parts by weight: 18 parts of butadiene rubber , 46 parts of polyurethane rubber, 22 parts of neoprene rubber, 9 parts of zinc oxide, 2.5 parts of stearic acid, 4 parts of paraffin, 26 parts of carbon black N774, 2.2 parts of antioxidant A, 1.9 parts of antioxidant D, 1.2 parts of antioxidant 4010NA , 3.2 parts of graphene, 3.5 parts of petroleum pitch, 0.7 parts of accelerator M, 1.6 parts of accelerator TMTD, and 2.3 parts of sulfur.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ventilated round clutch rubber airbag, which comprises the following raw materials in parts by weight: 15-25 parts of cis-butadiene rubber, 35-55 parts of urethane rubber, 15-25 parts of chloroprene rubber, 8-12 parts of zinc oxide, 2-3 parts of stearic acid, 3-5 parts of paraffin, 25-30 parts of carbon black N774, 1.5-2.5 parts of anti-aging agent A, 1.5-2.5 parts of anti-aging agent D, 0.5-1.5 parts of anti-aging agent 4010NA, 2.5-3.5 parts of graphene, 3-5 parts of petroleum pitch, 0.5-1.5 parts of accelerator M, 1.5-2.5 parts of accelerator TMTD, and 1.5-2.5 partsof sulfur. The preparation method comprises six process steps of rubber mixing, calender cutting, extrusion, molding, vulcanization and packaging. The vulcanization temperature, time and pressure areadjusted in the vulcanization process, thereby fundamentally solving the problem of labor consumption and time consumption. In addition, because liquid water is low in cost and can be recycled, the production cost of an enterprise can be significantly reduced.

Description

[0001] 1. Technical field: [0002] The invention relates to a production process of rubber products, in particular to a ventilated circular clutch rubber airbag and a preparation method thereof. [0003] 2. Background technology: [0004] The clutch rubber airbag is a kind of inner membrane of different shapes with good expansion and contraction functions, which is made of rubber as the main material, matched with high-strength fiber cloth, and processed after various processes such as vulcanization. Due to reasons such as raw material ratio, elasticity and high thermal conductivity requirements, the current clutch rubber airbags are unsatisfactory in tear resistance, wear resistance, aging resistance and thermal and electrical conductivity. At present, the ventilated circular clutch rubber airbag is commonly used in the market. Its production process includes six processes including rubber mixing, calendering and cutting, extrusion, molding, vulcanization, and packaging. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L9/00C08L11/00C08K13/02C08K3/22C08K5/09C08K3/04C08K3/06B29D22/02
CPCB29D22/02C08K2003/2296C08K2201/001C08L75/04C08L2205/035C08L9/00C08L11/00C08K13/02C08K3/22C08K5/09C08K3/04C08K3/042C08K3/06
Inventor 张极玲侯淼予高道旭张延勇赵连合张志伟
Owner HENAN DALIN RUBBER & TELECOMM APP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products