Single-component acrylate water-based coating with anti-corrosion and wear-resisting properties

A technology of acrylate and water-based coatings, applied in anti-corrosion coatings, etc., can solve the problems of low crosslinking degree and poor performance of acrylic acid emulsion, achieve excellent chemical corrosion resistance, convenient construction, and increase crosslinking density Effect

Inactive Publication Date: 2018-06-26
宁波宣伯涂料科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problem of poor performance due to the low crosslinking degree of the acrylic angzi emulsion in the prior art, the present invention provides a one-component acrylate water-based coating with anti-corrosion and wear-resistant properties, wherein the prepared by the present invention has Anti-corrosion and wear-resistant one-component acrylate water-based coatings have the advantages of high hardness, high wear resistance and corrosion resistance, and fast hardening speed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A kind of one-component acrylic ester water-based paint with anti-corrosion and wear-resistant properties, made of the following components by weight

[0061] HYD-5816 200 copies

[0062] 1 part propylene glycol

[0063] Titanium dioxide 20 parts

[0064] Precipitated barium sulfate 10 parts

[0065] 20 parts of benzyl alcohol

[0066] COATEX PE737 5 parts

[0067] Polyether silicone oil defoamer 1 part

[0068] BD-3032 0.1 parts

[0069] KLN-15B 0.1 part

[0070] AMP-95 0.5 parts

[0071] Hydroxyethyl cellulose 0.1 parts

[0072] 2020 0.1 share

[0073] ATX-01 0.1 parts.

Embodiment 2

[0075] A kind of one-component acrylic ester water-based paint with anti-corrosion and wear-resistant properties, made of the following components by weight

[0076] HYD-5816 250 copies

[0077] 1 part propylene glycol

[0078] Titanium dioxide 20 parts

[0079] Precipitated barium sulfate 15 parts

[0080] Dodecyl alcohol ester 20 parts

[0081] ECODIS 40 6 parts

[0082] Silicone oil emulsion defoamer 2 parts

[0083] Polysiloxane 0.5 parts

[0084] Bordeaux mixture 0.1 part

[0085] AMP-95 1 part

[0086] Hydroxymethylcellulose 0.05 parts

[0087] Hydroxyethyl cellulose 0.05 part

[0088] 2020 0.1 share

[0089] ATX-01 0.2 parts.

Embodiment 3

[0091] A kind of one-component acrylic ester water-based paint with anti-corrosion and wear-resistant properties, made of the following components by weight

[0092] HYD-5816 300 copies

[0093] 2 parts propylene glycol

[0094] Titanium dioxide 20 parts

[0095] Precipitated barium sulfate 20 parts

[0096] 30 parts of ethylene glycol butyl ether

[0097] COATEX P90 8 servings

[0098] Polyether silicone oil defoamer 2.5 parts

[0099] Sodium dodecylbenzenesulfonate 0.5 parts

[0100] KLN-16B 0.3 parts

[0101] AMP-95 1.1 parts

[0102] 0.3 parts of hydroxyethyl cellulose

[0103] 2020 0.3 copies

[0104] ATX-01 0.3 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a single-component acrylate water-based coating with anti-corrosion and wear-resisting properties, and belongs to the field of coating preparation. The single-component acrylate water-based paint with anti-corrosion and wear-resisting properties is prepared from the following components in parts by weight: 200-400 parts of a special acrylate emulsion, 1-10 parts of propylene glycol, 20-40 parts of titanium dioxide, 10-20 parts of precipitated barium sulfate, 20-50 parts of a film-forming assistant, 5-10 parts of a dispersing agent, 1-5 parts of a defoaming agent, 0.1-1part of a wetting agent, 0.1-1 part of a bactericide, 0.5-2 parts of a multifunctional assistant, 0.1-1 part of a thickening agent, 0.1-1 part of a leveling agent and 0.1-1 part of an acrylic thickening agent. The coating provided by the invention has good water resistance, corrosion resistance and wear resistance, the drying time is fast, the air permeability is good, the coating film does not bubble or fall off, and the coating can be used in an environment of -200-950 DEG C, and can be used in industrial anticorrosion fields such as floor coatings, metal anticorrosive coatings, ship coatings and the like.

Description

technical field [0001] The invention relates to an acrylic paint, in particular to a one-component acrylic water-based paint with anti-corrosion and wear-resistant properties. Background technique [0002] With the rapid development of the economy, my country's industrial coatings have achieved rapid development. Floor coatings have been paid attention to and widely used for their excellent physical and mechanical properties, electrical insulation properties, and chemical corrosion resistance, and their consumption has continued to increase year by year. However, at present, about 80% of domestic floor coatings are solvent-based coatings. The content of organic solvents is large. During production and use, organic solvents volatilize into the atmosphere, causing serious waste of resources and environmental pollution, affecting people's physical and mental health, and accompanied by Great security risk. With the increasing international environmental protection and stricter ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/08C09D7/61C09D7/63C09D7/65
CPCC09D133/04C08K2003/2241C08K2003/3045C08L2205/025C08L2205/035C08L2207/53C09D5/08C08L1/284C08L83/12C08K13/02C08K3/30C08K3/22C08K5/053C08L83/04
Inventor 郭虹郝迎军
Owner 宁波宣伯涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products