Novel lead-acid storage battery clapboard and preparation method thereof

A lead-acid storage battery and separator technology, which is applied to battery components, circuits, electrical components, etc., can solve the problems of battery scrapping, puncture or breakage, battery failure, etc., to improve life, increase wet strength, improve The effect of toughness

Inactive Publication Date: 2010-04-21
YIHECHENG GRP CO LTD
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of separator has low wet strength, and it is easy to cause the separator to penetrate and cause the...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Pulping: Take 41kg of superfine glass fiber cotton with a diameter of 0.6-1.0um, 7kg of two-component organic fibers (purchased from Woongjin Chemical Co.Ltd), 0.5kg of sulfuric acid, and wet strength agent PPE0. 1kg, add ultra-fine glass fiber cotton, two-component organic fiber, and wet strength agent to the low-consistency pulper, add 2m 3 Add deionized water, then add sulfuric acid, adjust the beating concentration to 2%, make it disintegrate into a slurry with evenly dispersed fibers, add it to the thick stock tank for subsequent use; (2) slurry processing and transportation: the pulp in the thick stock tank The material is diluted with water to form a slurry with a mass concentration of 2.4‰, pumped into the slurry storage tank, slag is removed during the dilution and pouring process, and transported to the paper machine; Such as 0.5mm by adjusting the network speed 40HZ, traffic 40m 3 / h, vacuum degree 0.04Mpa, pressing device and other wet paper forming; (4...

Embodiment 2

[0026] (1) Pulping: Take 41kg of superfine glass fiber cotton with a diameter of 1.0-1.5um, 7kg of bicomponent organic fibers (purchased from Woongjin Chemical Co.Ltd), 0.5kg of sulfuric acid, and wet strength agent PPE0. 1kg, add ultra-fine glass fiber cotton, two-component organic fiber, and wet strength agent to the low-consistency pulper, add 2m 3 Add deionized water, then add sulfuric acid, adjust the beating concentration to 1.5%, make it disintegrate into a slurry with evenly dispersed fibers, add it to the thick stock tank for subsequent use; (2) slurry processing and transportation: the pulp in the thick stock tank The material is diluted with water to form a slurry with a mass concentration of 2.4‰, pumped into the stock tank, removed during the dilution process, and transported to the paper machine; Speed, flow rate, vacuum degree, pressing device and other wet paper forming; (4) Drying box drying: wet paper enters the drying box with an adjusted temperature of 150°...

Embodiment 3

[0028] (1) Pulping: Take 38kg of superfine glass fiber cotton with a diameter of 0.6-1.0um, 10kg of two-component organic fibers (purchased from Woongjin Chemical Co.Ltd), 0.5kg of sulfuric acid, and wet strength agent PPE0. 2kg, add ultra-fine glass fiber cotton, two-component organic fiber, and wet strength agent to the low-consistency pulper, add 2m 3 Add deionized water, then add sulfuric acid, adjust the beating concentration to 1.5%, make it disintegrate into a slurry with evenly dispersed fibers, add it to the thick stock tank for subsequent use; (2) slurry processing and transportation: the pulp in the thick stock tank The material is diluted with water to form a slurry with a mass concentration of 2.4‰, pumped into the stock tank, removed during the dilution process, and transported to the paper machine; Speed, flow rate, vacuum degree, pressing device and other wet paper forming; (4) Drying box drying: wet paper enters the drying box with an adjusted temperature of 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel lead-acid storage battery clapboard, which belongs to the technical field of storage batteries. The novel lead acid storage battery clapboard consists of the following raw materials in part by weight: 38 to 41 parts of superfine glass cellucotton, 7 to 10 parts of bicomponent organic fiber, 0.5 to 0.6 part of sulfuric acid, and 0.1 to 0.2 part of wet strength agent; and the novel lead acid storage battery clapboard is prepared through the processes of pulping, processing and conveying of sizing materials, paper-making from paper pulp for the clapboard, drying by a drying box, reeling, clapboard processing and the like. The lead-acid storage battery clapboard has the advantages of high porosity, low resistance, high wet strength and good anti-puncture capability, and compared with a pure glass fiber clapboard, the wet strength is improved by nearly 70 percent, the anti-puncture capability is improved by about 45 percent, and the wet resilience force is improved by 5 to 11 percent.

Description

Technical field: [0001] The invention relates to a lead-acid storage battery separator and a preparation method thereof, belonging to the technical field of storage batteries. Background technique: [0002] The separator is an important part of the lead-acid battery, known as the "third electrode". It is placed between the positive and negative plates of the battery, which can prevent the short circuit of the positive and negative electrodes in the electrolyte, and at the same time ensure that the electrolyte is in the positive and negative electrodes. There is good electrical conductivity between negative electrodes, and it also has the functions of reducing plate bending, preventing active material from falling off, good liquid retention, and gas passage. With the use of lead-acid batteries becoming more and more extensive, especially the rapid development of electric vehicles, the performance requirements for power batteries are getting higher and higher. As one of the fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M2/16H01M50/403H01M50/446H01M50/489
CPCY02E60/12Y02E60/10
Inventor 陈希峰李爱敏潘文法潘新仕陈一威
Owner YIHECHENG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap