Heat treatment method of granulation ring mold

A heat treatment method and preparatory heat treatment technology, applied in heat treatment furnaces, heat treatment equipment, manufacturing tools, etc., can solve the problems of increased cost of granulated products, short service life, high manufacturing cost, etc., and achieve improved wear resistance and high comprehensive mechanical properties , cheap effect

Inactive Publication Date: 2010-06-30
GANSU AGRI UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the structure of the ring die on the granulator is relatively mature, but its wear is a technology that is difficult to solve for the ring die
Most of the existing granulation ring dies are made of high-quality alloy steel and high-chromium stainless steel. The materials are expensive and the manufacturing cost is high, which greatly increases the cost of granulation products. Ordinary metal materials are difficult to resist the abrasive wear on the ring die during the granulation process. The service life is short; the ring dies produced by many manufacturers have not solved this practical problem well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1, the described heat treatment method of a granulation ring die includes a heat treatment method of a granulation ring die, which is characterized in that: the material of the granulation ring die is 45 # For steel, its heat treatment method includes preliminary heat treatment and final heat treatment, wherein the preliminary heat treatment includes the following steps:

[0012] (1) Quenching stage: heat the granulation ring die to 840°C in a heating furnace, and keep it warm for 30 minutes, then water-cool it to 100°C, and keep it warm at 100°C for 10 minutes;

[0013] (2) Tempering stage: Heat the quenched granulation ring die to 550°C in a heating furnace, keep it warm for 20 minutes, and then water-cool to 25°C.

[0014] The final heat treatment includes the following steps:

[0015] (1) Quenching stage: heat the granulation ring die after preliminary heat treatment to 840°C in a heating furnace, and keep it warm for 6 minutes, then water-cool it to 100...

Embodiment 2

[0017] Embodiment 2, the described heat treatment method of a granulation ring die is characterized in that: the material of the granulation ring die is 45 steel, and the heat treatment method includes preliminary heat treatment and final heat treatment, wherein the preliminary heat treatment includes the following steps :

[0018] (1) Quenching stage: heat the granulation ring die to 840°C in a heating furnace, and keep it warm for 25 minutes, then water-cool it to 100°C, and keep it at 100°C for 15 minutes;

[0019] (2) Tempering stage: Heat the quenched granulation ring die to 550°C in a heating furnace, keep it warm for 25 minutes, and then water-cool to 25°C.

[0020] The final heat treatment includes the following steps:

[0021] (1) Quenching stage: heat the granulation ring die after preliminary heat treatment to 770°C in a heating furnace, and keep it warm for 5 minutes, then water-cool it to 100°C, and keep it at 100°C for 130 minutes;

[0022] (2) Tempering stage:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a heat treatment method of a granulation ring mold, which has the characteristics that the granulation ring mold is made of 45 steel; the heat treatment method comprises preheat treatment and final heat treatment, wherein the preheat treatment and the final heat treatment both comprise a quenching step and a tempering step; carbon constructional quality steel is selected as the material of the ring mold, and is ordinary and cheap; an optimized subcritical quenching heat treatment process is adopted for enhancing abrasion resistant performance of the ring mold; treated metallurgical structure is a composite phase of tempered martensite and retained austenite; the optimal combination of hardness and toughness is found; and the abrasion resistant performance of the material reaches a optimal level. The ring mold has high comprehensive mechanical performance and high anti-abrasion capability of abrasive materials, and can replace expensive alloy steel and stainless steel materials for finishing granulation procedures.

Description

Technical field: [0001] The invention relates to a heat treatment method of a granulation ring die. Background technique: [0002] At present, the structure of the ring die on the granulator is relatively mature, but its wear is a difficult technology for the ring die to solve. Most of the existing granulation ring dies are made of high-quality alloy steel and high-chromium stainless steel. The materials are expensive and the manufacturing cost is high, which greatly increases the cost of granulation products. Ordinary metal materials are difficult to resist the abrasive wear on the ring die during the granulation process. The service life is short; the ring dies produced by many manufacturers have not solved this practical problem well. Invention content: [0003] The purpose of the present invention is to avoid the deficiencies of the prior art and provide a granulation ring die heat treatment method. Therefore, the problems existing in the prior art are effectively so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/40C21D1/18
Inventor 吴劲锋张炜黄晓鹏韩天虎向金城赵武云张维国周天宝
Owner GANSU AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products