Method for preparing electric insulating glue
A production method and electrical insulation technology, applied in the direction of organic insulators, rubber insulators, etc., can solve the problems of difficult filtration, electrical insulating glue containing many impurities, poor insulation performance of composite insulators and composite arrester jackets, etc., and achieve easy filtration and insulation performance. Good results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1
[0020] First, the methyl vinyl silicone rubber, fumed white carbon black and silicone oil are kneaded in a closed rubber mixer at a weight ratio of 4:3:1 until the three are uniformly mixed; the kneaded rubber is thinly passed out of the sheet , The thin-pass roll distance used for thin-pass is 0.5mm, and the number of thin-pass is 5 times; then it enters the oven and bake at the oven temperature of 150℃ for 2 hours and then it is baked and cooled to obtain the first mixed rubber material.
[0021] Secondly, the methyl vinyl silicone rubber, aluminum hydroxide, and silicone oil are kneaded by a closed rubber mixer at a weight ratio of 4:5:1 until the three are evenly mixed; the kneaded rubber material is thinly passed out into a thin sheet. The thin-pass roll distance used during the pass is 0.5mm, and the number of thin passes is 5; then it enters the oven and bake at a furnace temperature of 150°C for 2 hours, and then it is baked and cooled to obtain the secon...
Example Embodiment
[0026] Example 2
[0027] First, the methyl vinyl silicone rubber, fumed white carbon black and silicone oil are kneaded in a closed rubber mixer at a weight ratio of 4:3:1 until the three are uniformly mixed to obtain the first mixed rubber material.
[0028] Secondly, the methyl vinyl silicone rubber, aluminum hydroxide and silicone oil are kneaded in a closed rubber mixer at a weight ratio of 4:5:1 until the three are uniformly mixed to obtain a second mixed rubber material.
[0029] Finally, the first mixed rubber material and the second mixed rubber material are kneaded into a large mass at a weight ratio of 1:1, and then the mixed rubber material is re-mixed using an open rubber mixer. The roller distance of the open rubber mixer is 12mm, the obtained rubber material is filtered through the filter screen with the mesh number of 28, 28, 150 and 200, and the filtered rubber material is the electrical insulating rubber.
[0030] In this embodiment, when the third mixed rubber mater...
Example Embodiment
[0034] Example 3
[0035] First, the methyl vinyl silicone rubber, fumed white carbon black and silicone oil are kneaded in a closed rubber mixer at a weight ratio of 4:5:1 until the three are uniformly mixed; the kneaded rubber material is thinly passed out. , The thin-pass roll distance used for thin-pass is 2mm, and the number of thin-pass is 3; then it enters the oven and bake at 120℃ for 2 hours, and then it is baked and cooled to obtain the first mixed rubber material.
[0036] Secondly, the methyl vinyl silicone rubber, aluminum hydroxide and silicone oil are kneaded in a closed rubber mixer at a weight ratio of 2:8:0 until the three are evenly mixed; the kneaded rubber material is thinly passed out into a thin sheet. The thin pass roll distance used during the pass is 2mm, and the number of pass passes is 3 times; then it enters the oven and bake at a furnace temperature of 120°C for 3 hours, and then it is baked and cooled to obtain the second mixed rubber material.
[0037...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap