Purpose of heavy metal sludge, acid pellet and preparation method and purpose thereof
A technology for heavy metal sludge and sludge oxidation, which is applied to blast furnaces, furnace types, furnaces, etc., can solve the problem of inability to effectively deal with comprehensive utilization of stainless steel cold-rolled heavy metal sludge, so as to facilitate the smooth flow of the process and ensure the grade of the furnace , The effect of reducing the cost of raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0061] Example 1:
[0062] After the stainless steel cold-rolled heavy metal sludge is dried and pulverized, 25% of the heavy metal sludge (weight percentage of the total weight of the raw materials used to make sludge oxidation pellets, the same below), iron powder 50%, carbon powder 4% , The compounding binder is 6% and the moisture content is 15%. After mixing uniformly, green balls are produced. The pressure of the balls is 3500N, and the particle size of the pellets is 15mm.
[0063] Among them, the stainless steel cold-rolled heavy metal sludge is the enriched heavy metal sludge produced in the two-step precipitation method of "chemical reduction + liquid caustic soda + lime milk". The chemical composition and weight percentage of the dry basis of the stainless steel cold-rolled heavy metal sludge are : T.Fe: 38.5%; Cr 2 O 3 : 3.5%; NiO: 0.5%; CaO: 35.5%; Al 2 O 3 :3.8%; SiO 2 :5.4%; CaF 2 : 5.9%; MgO: 0.2%; Na 2 O+K 2 O: 3.6%; S: 2.5%; P<0.1%; the balance is impurities. The...
Example Embodiment
[0068] Example 2:
[0069] After the stainless steel cold-rolled heavy metal sludge is dried and crushed, the weight of the heavy metal sludge is 50% (the weight percentage of the total weight of the raw materials used to make the sludge oxidation pellets, the same below), iron fine powder 30%, carbon powder 5 %, 2% of the composite binder, and 13% of the moisture content. After being evenly mixed, green balls are produced. The pressure of the balls is 3000N, and the particle size of the pellets is 12.5mm.
[0070] Among them, the stainless steel cold-rolled heavy metal sludge is the enriched heavy metal sludge produced by the two-step precipitation method of "chemical reduction + liquid caustic soda + lime milk". The chemical composition and weight percentage of the dry basis of the stainless steel cold-rolled heavy metal sludge are : T.Fe: 39.8%; Cr 2 O 3 : 4.9%; NiO: 1.0%; CaO: 29.5%; Al 2 O 3 : 2.4%; SiO 2 :3.5%; CaF 2 : 11.9%; MgO: 0.1%; Na 2 O+K 2 O: 4.6%; S: 1.5%; P<0.1%; th...
Example Embodiment
[0076] Example 3:
[0077] After the stainless steel cold-rolled heavy metal sludge is dried and pulverized, the weight of heavy metal sludge is 5% (weight percentage, the same below), iron powder 60%, carbon powder 15%, composite binder 8%, moisture 12% After mixing uniformly, green pellets are produced. The pelletizing pressure is 4000N and the pellet size is 15mm.
[0078] Among them, the stainless steel cold-rolled heavy metal sludge is a mixed sludge produced by the lime milk one-step precipitation method. The chemical composition and weight percentage of the dry basis of the stainless steel cold-rolled heavy metal sludge are: T.Fe: 12.5%; Cr 2 O 3 : 2.9%; NiO: 0.4%; CaO: 44.5%; Al 2 O 3 :4.4%; SiO 2 :5.2%; CaF 2 :17.9%; MgO: 0.4%; Na 2 O+K 2 O: 4.5%; S: 4.8%; P: 0.1%; the balance is impurities.
[0079] The formula of the composite binder: Bentonite 50% (weight percentage, the same below), slaked lime 15%, sodium carbonate 5%, PAM 10%, CMC-Na 10%, modified starch 10%.
[0080] T...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap