Method for preparing organic solvent adsorbing material

A technology of adsorption materials and organic solvents, applied in the field of preparation of organic solvent adsorption materials, can solve the problems of difficult removal of reactants, no patents or public reports, etc., and achieve excellent organic solvent adsorption performance, thorough and uniform reaction, and uniform silicon-aluminum ratio Effect

Active Publication Date: 2010-10-06
马军
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] NaCl (or NaAlCl) produced due to the reaction 4 ) will cause the molecular sieves to stick together, and the reactants are not easy to remove. Using Y-type molecular sieves and SiCL 4 It is necessary to develop special equipment or special process flow to avoid NaCl (or NaAlCl 4 ) will cause the molecular sieves to stick together and prevent the reaction from proceeding further, but there are no related patents or public reports at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing organic solvent adsorbing material
  • Method for preparing organic solvent adsorbing material
  • Method for preparing organic solvent adsorbing material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] A kind of preparation method of organic solvent adsorption material of the present invention, comprises the following steps:

[0033] a) Use molecular sieves with a diameter of 1-3 microns as raw materials to manufacture molecular sieve paper; the diameter of molecular sieves is selected at 1-3 microns because the configured slurry is easy to form a suspension at this scale, which is convenient for manufacturing into molecular sieve paper .

[0034] b), the molecular sieve paper obtained in step a) is hot-pressed into a corrugated shape.

[0035] c) The corrugated molecular sieve paper obtained in step b) and the molecular sieve paper obtained in step a) are stacked alternately or rolled into a honeycomb body, and then baked.

[0036] d) Place the molecular sieve honeycomb body obtained in step c) into a closed container, and then pass nitrogen and SiCl at a temperature of 247 ° C to 500 ° C into the container 4 The mixed gas of gas or water vapor at a temperature of ...

Embodiment 1

[0043]a), making a Y-type zeolite molecular sieve with a diameter of 1 micron into molecular sieve paper by tape casting;

[0044] b), the Y-type zeolite molecular sieve paper obtained in step a) is hot-pressed into a corrugated shape;

[0045] c), the corrugated Y-type zeolite molecular sieve paper obtained in step b) and the Y-type zeolite molecular sieve paper obtained in step a) are stacked alternately or rolled into a shape such as figure 1 , figure 2 The honeycomb body shown, and then baked;

[0046] d) Place the honeycomb body obtained in step c) into a closed container, and then pass nitrogen and SiCl at a temperature of 247°C into the container 4 Gas mixture, which will chemically react with the molecular sieve on the molecular sieve honeycomb;

[0047] e) After step d) is maintained for 4 hours, stop passing the reaction gas into the container, and pass nitrogen gas at a temperature of 80° C. into the container, and discharge the remaining reaction gas in the con...

Embodiment 2

[0051] a), making a BETA molecular sieve with a diameter of 3 microns into molecular sieve paper by coating method;

[0052] b), the molecular sieve paper obtained in step a) is heat-pressed into a corrugated shape;

[0053] c), the corrugated molecular sieve paper obtained in step b) and the molecular sieve paper obtained in step a) are stacked alternately or rolled into a shape such as figure 1 , figure 2 The honeycomb body shown, and then baked;

[0054] d) Place the honeycomb body obtained in step c) into a closed container, and heat the honeycomb body to 600°C, and then pass water vapor at a temperature of 600°C into the container, which will combine with the molecular sieve on the molecular sieve honeycomb body A chemical reaction occurred;

[0055] e) After step d) is maintained for 6 hours, stop passing the reaction gas into the container, and pass nitrogen gas at a temperature of 100°C into the container to discharge the remaining reaction gas in the container, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing an organic solvent adsorbing material. The method comprises the following steps of: manufacturing molecular sieve paper; thermally pressing the molecular sieve paper into corrugated molecular sieve paper; preparing the molecular sieve paper into a honeycomb; performing a chemical reaction on the molecular sieve honeycomb and a mixed gas of nitrogen and SiCl4 gas or water vapor in an airtight container; exhausting residual reaction gas; repeatedly cleaning the molecular sieve honeycomb to remove a solid reaction product on the molecular sieve honeycomb and washing the molecular sieve honeycomb with acid; and continuing to perform a chemical reaction on the molecular sieve honeycomb and the mixed gas of nitrogen and SiCl4 gas or water vapor in the airtight container. The adsorbing material prepared by the method has a high and uniform ratio of silicate to aluminum, so the adsorbing material has excellent organic solvent adsorbing performance and can be widely used for adsorbing and separating an organic solvent from the air or adsorbing and separating the organic solvent in water which contains the organic solvent.

Description

technical field [0001] The invention relates to a preparation method of an organic solvent adsorption material, which is mainly used for absorbing and separating organic solvents from air, or for absorbing and separating organic solvents from water containing organic solvents. Background technique [0002] A large number of scientific research data and engineering application examples have proved that molecular sieves with a high silicon-aluminum ratio have good adsorption capacity for organic solvents. At present, people often use the gas phase method to dealuminate and supplement silicon to obtain molecular sieves with high silicon-aluminum ratio, that is, to use conventional molecular sieves, such as Y-type molecular sieves, BETA molecular sieves, mordenite molecular sieves or ZSM5, etc., at a temperature of 247°C-500°C. Silicon chloride (SiCl 4 ) gas undergoes a chemical reaction. Domestic patent z101115612.0 and application number 200610083440.3 are used to manufactur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/16B01J20/30B01D53/04C02F1/28C02F1/58C02F101/30
Inventor 马军
Owner 马军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com