Productive technology of precise stainless steel strip used for high-end mobile phone

A production process and technology for stainless steel strips, applied in the field of production process of precision stainless steel strips, can solve the problems of inability to meet high-end mobile phone accessories, poor flatness of plate shape, inconsistent surface color and luster, and achieve uniform surface color and luster. No chromatic aberration and small thickness tolerance fluctuations

Inactive Publication Date: 2010-10-27
YONGXIN PRECISION MATERIAL WUXI
View PDF7 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the precision stainless steel strips used in the manufacture of high-end mobile phone accessories are rolled by multi-roll mills, and other auxiliary equipment are used to improve the surface and flatness of the plate. However, the stainless steel strips ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The process of this embodiment uses stainless steel cold-rolled coils as raw materials, the grade is SUS304, the thickness is 1.50 mm, and the width is 406 mm. The target thickness of the finished steel strip is 0.50mm, the width is 400mm, the product state is 3 / 4H, and the hardness (HV) is 310-340.

[0024] The present invention adopts following processing steps:

[0025] a. First rewind the raw material of stainless steel cold-rolled coil with a thickness of 1.50mm by rewinding machine for the first time, and the coiling tension is 18kg / mm ​​when rewinding for the first time 2 , the speed is 80 m / min, and the steel strip is protected by the whole roll of backing paper during the first rewinding process;

[0026] b. The steel strip after the first rewinding is cold-rolled for the first time with a 20-high Sendzimir rolling mill. The lubricating coolant used for the first cold-rolling is "DAPHNESTAINLESS ROLL P-T" provided by Changzhou Guohong Chemical Co., Ltd. "Roll...

Embodiment 2

[0046] The process of this embodiment uses stainless steel cold-rolled coils as raw materials, the grade is SUS304, the thickness is 0.90 mm, and the width is 406 mm. The target thickness of the finished steel strip is 0.50mm, the width is 400mm, the product state is 1 / 2H, and the hardness (HV) is 250-280.

[0047] The present invention adopts following processing steps:

[0048] a. Firstly, the raw material of stainless steel cold-rolled coil with a thickness of 0.90mm is rewound by a rewinder for the first time, and the coiling tension is 16kg / mm ​​during the first rewinding 2 , the speed is 100 m / min, and the steel strip is protected by the whole roll of backing paper during the first rewinding process;

[0049] b. The steel strip after the first rewinding is cold-rolled for the first time with a 20-high Sendzimir rolling mill, and the lubricating coolant used in the cold rolling is rolled with "DAPHNESTAINLESS ROLL P-T" provided by Changzhou Guohong Chemical Co., Ltd. oi...

Embodiment 3

[0069] The process of this embodiment selects stainless steel cold-rolled coil as raw material, the grade is SUS301, the thickness is 0.80mm, the width is 406mm, the thickness of the finished steel strip is 0.30mm, the width is 400mm, the product state is 1 / 2H, and the hardness (HV) is 310~340, elongation (δ 50 ) is ≥ 15%.

[0070] The present invention adopts following processing steps:

[0071] a. Firstly, the raw material of stainless steel cold-rolled coil with a thickness of 0.80mm is rewound for the first time with a rewinder, and the coiling tension is 14kg / mm ​​during the first rewinding 2 , the speed is 120 m / min, and the steel strip is protected by the whole roll of backing paper during the first rewinding process;

[0072] b. The steel strip after rewinding is cold-rolled for the first time with a 20-high Sendzimir rolling mill, and the lubricating coolant used for the first cold-rolling is rolled with "DAPHNESTAINLESS ROLL P-T" provided by Changzhou Guohong Chemi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Unevennessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a productive technology of a precise stainless steel strip used for a high-end mobile phone, which comprises the steps of primary rewinding, primary cold rolling, primary spray degreasing, primary hot water spraying, primary hot wind drying, solid solution, secondary rewinding, secondary cold rolling, secondary spray degreasing, secondary hot water spraying, secondary hotwind drying, stretch bending straightening, clipping and the like. The stainless steel strip obtained by the technology has small tolerance fluctuation in product thickness, stable performance, uniform and consistent color of the surface without color aberration, no bruise and no convex point defect, the flatness of the strip shape is good, and compared with the technology of the prior art, the invention obviously improves the quality of the product, is suitable for industrialized production, and meets the high requirements on quality in electronic industry, and the obtained stainless steel strip is very suitable for being used on high-end mobile phones.

Description

technical field [0001] The invention relates to a production process for processing precision stainless steel strips for high-grade mobile phone accessories. Background technique [0002] At present, the precision stainless steel strips used in the manufacture of high-end mobile phone accessories are rolled by multi-roll mills, and other auxiliary equipment are used to improve the surface and flatness of the plate. However, the stainless steel strips made by the existing process have thickness tolerance fluctuations. Large, unstable mechanical properties, inconsistent surface color, scratches and bumps, poor flatness of the plate shape, etc., cannot meet the requirements of steel belts for high-end mobile phone accessories. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a precision stainless steel strip for high-grade mobile phones that can produce stable performance, small thickness tole...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B1/22B21B37/48B21B37/46C23G3/02C21D9/52
Inventor 濮永法
Owner YONGXIN PRECISION MATERIAL WUXI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap