Method for preparing water-based natural rubber waterproofing coating

A technology for natural rubber and waterproof coatings, applied in the field of waterproof coatings, can solve problems such as formula differences, and achieve the effects of excellent use effect, novel formula and low cost

Inactive Publication Date: 2010-11-10
程海应
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Comparative analysis of this product and relevant literature shows that the formula is still different

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] The formula of the paint: take 58 parts of water-based natural rubber, 3.5 parts of ethyl alcohol butyl ether, 0.25 parts of triethanolamine, 0.3 parts of BX-120, 2.5 parts of ethylene glycol, 0.8 parts of melamine, 12 parts of turpentine, 60 parts of styrene-acrylic emulsion in parts by weight, 11 parts of kaolin;

[0014] Another good formula: 50 parts of water-based natural rubber, 3 parts of ethyl alcohol butyl ether, 0.2 parts of triethanolamine, 0.2 parts of BX-120, 2.0 parts of ethylene glycol, 0.6 parts of melamine, 10 parts of turpentine, 50 parts of styrene-acrylic emulsion, 10 parts of kaolin .

[0015] Preparation of paint: first put natural rubber in a mixer, add ethyl alcohol butyl ether, triethanolamine, BX-12, ethylene glycol, melamine, turpentine in sequence, stir evenly under normal temperature and normal pressure, continue to add styrene-acrylic emulsion, kaolin Stir evenly to obtain the water-based natural rubber waterproof coating.

[0016] Coatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a water-based natural rubber waterproofing coating. The coating comprises the following ingredients in part by weight: 50 to 65 parts of water-based natural rubber, 3 to 4.5 parts of ethanol butyl ether, 0.2 to 0.30 part of triethanolamine, 0.2 to 0.35 part of BX-12, 2.0 to 3.5 parts of ethylene glycol, 0.6 to 0.8 part of melamine, 10 to 13 parts of turpentine, 50 to 65 parts of styrene-acrylate emulsion and 10 to 13 parts of kaolin. The method comprises the following steps of: placing natural rubber into a stirrer; adding the ethanol butyl ether, the triethanolamine, the BX-12, the ethylene glycol, the melamine and the turpentine sequentially; uniformly stirring the mixture at normal temperature and normal pressure; and continuously adding the styrene-acrylate emulsion and the kaolin, and uniformly stirring the mixture to obtain the waterproofing coating. The strength of the coating is reinforced by adding 5 to 40-mesh quartz sand in a ratio of 1:1 into the coating during use. The selected ingredients are products sold in markets, and have 46 percent of solid content of the water-based natural rubber and 48 percent of solid content of the styrene-acrylate emulsion.

Description

technical field [0001] The invention relates to a waterproof paint, especially material selection and compounding. The product obtained through repeated practice and exploration has market competitiveness and practical value. Background technique [0002] According to literature search, Li Chengshun of Binzhou Liangyou Waterproof Material Co., Ltd. invented a production method of water-based two-component polyurethane waterproof coating (patent application number: 200610166219), which is made of polyether polyol, tartaric acid and isocyanate. Form A component; make B component with rubber oil, emulsifier, water, catalyst, solid filler, calcium hydroxide, and other additives. When in use, mix A and B components, which can be used for waterproofing construction of wet base. [0003] Zhonghong (Tianjin) Industrial Co., Ltd. Zhang Yunbo invented a single-component anti-sedimentation water-based waterproof coating production process (patent application number: 200610014958). Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D107/00C09D125/14C09D7/12C09D5/00
Inventor 程海应
Owner 程海应
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com