Manufacturing process of silastic checkered roll

A manufacturing process and silicone rubber technology, which is applied to the manufacturing process of silicone rubber pattern rollers, can solve the problems of complex pattern engraving process and low fidelity, and achieve the effects of high fidelity and advanced processing technology.

Inactive Publication Date: 2010-12-01
朱德胜
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

That is to say, the pattern on the metal roller needs to be carved out. Such a pattern carving process is complicated and the fidelity is not high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of silastic checkered roll
  • Manufacturing process of silastic checkered roll
  • Manufacturing process of silastic checkered roll

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] Silicone rubber pattern roller manufacturing process, the steps are as follows: the sample skin of animal or vegetable skin is coated with silicone rubber, after natural air drying, after peeling off the sample skin, the obtained silicone rubber block printed with the pattern on the sample skin is then coated with Coat resin on the silicone rubber block with sample skin pattern, obtain the blank mold, and then coat silicone rubber on the blank mold, splice the coated silicone rubber block into a cylindrical shape, and insert the processed cylindrical silicone rubber 3 Inside the centrifugal cylinder 2, the centrifugal cylinder 2 is driven by the following two transmission rollers 1, such as figure 1 As shown, and the pattern of the cylindrical silicone rubber faces inward, pour resin 4 on the surface of the pattern of the cylindrical silicone rubber, and the resin is generally epoxy resin. After rotating and centrifuging, it solidifies well, and after drying at 70-100°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a manufacturing process of a silastic checkered roll. The manufacturing process comprises the following steps of: coating silastic on animal skin or plant bark sample; naturally airing; peeling off the sample skin or bark to obtain silastic blocks with patterns printed on the sample skin or bark; coating resin on the silastic blocks with the sample skin or bark patterns to obtain a blank mold; then, coating silastic on the blank mold; and splicing the coated silastic blocks into a cylinder. The invention has the advantages of advanced process, environmental protection and extremely high fidelity by directly copying patterns from animal skin or plant bark.

Description

technical field [0001] The invention relates to a manufacturing process of a silicone rubber pattern roller for printing artificial leather patterns. Background technique [0002] Traditionally, patterns are printed on soft bodies such as leather by engraving desired patterns on metal rollers and embossing patterns on artificial leather heated by rolling. That is to say, the pattern on the metal roller needs to be carved out. Such a pattern carving process is complicated and the fidelity is not high. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention provides a silicon rubber patterned roller manufacturing process. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: silicon rubber pattern roller manufacturing process, the steps are as follows: the sample skin of animal or vegetable skin is coated with silicon rubber, after natural air drying, after peeling off the sample skin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C41/04B29C41/20
Inventor 朱德胜
Owner 朱德胜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap