Photosensitive composition containing photoinitiator of diphenyl sulfide based ketoxime esters and application thereof

A technology of photosensitive composition and diphenyl sulfide, which is applied in optics, optical filters, organic chemistry, etc., can solve the problem that the photosensitive composition cannot meet the application requirements, and achieve excellent curing effect and good pattern integrity , high optical transparency

Active Publication Date: 2011-11-30
CHANGZHOU TRONLY NEW ELECTRONICS MATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Most of the existing photosensitive compositions can no longer meet the increasingly urgent application needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photosensitive composition containing photoinitiator of diphenyl sulfide based ketoxime esters and application thereof
  • Photosensitive composition containing photoinitiator of diphenyl sulfide based ketoxime esters and application thereof
  • Photosensitive composition containing photoinitiator of diphenyl sulfide based ketoxime esters and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-1

[0039] (1) Photosensitive composition No.1-1

[0040] 25 parts by mass of carbon black

[0041] 32 parts by mass of alkali-soluble resin

[0042] [Benzyl methacrylate / methacrylic acid / hydroxyethyl methacrylate / acrylic acid ester of formula (II) (molar ratio is 55 / 10 / 15 / 10) copolymer] (Mw: 12000)

[0043] 16 parts by mass of dipentaerythritol hexaacrylate

[0044] Formula (I) ketoxime ester compound 8 parts by mass

[0045] (R 1 where n=1, m=3; R 2 is phenyl; R 3 for diphenyl sulfide group )

[0046] Dispersant FC-4430 0.1 parts by mass

[0047] (2) Preparation of black matrix BM

[0048] The components of the above composition are mixed and dissolved in 100 parts by mass of solvent propylene glycol monomethyl ether acetate (PGMEA) to form a liquid composition;

[0049] Use a spin coater to coat the liquid composition on a glass substrate, dry at 90°C for 5 minutes to remove the solvent, and form a coating film with a film thickness of 1.5 μm; in order to obtain a co...

Embodiment 2-1

[0081] (1) Red photosensitive composition No.2-1

[0082] C.I. Pigment Red 254 18 parts by mass

[0083] 40 parts by mass of alkali-soluble resin

[0084] [Benzyl methacrylate / methacrylic acid / hydroxyethyl methacrylate / acrylic acid ester of formula (II) (molar ratio is 60 / 10 / 10 / 10) copolymer] (Mw: 10000)

[0085] 15 parts by mass of dipentaerythritol hexaacrylate

[0086] 7 parts by mass of formula (I) ketoxime ester compound

[0087] (R 1 where n=1, m=3; R 2 is phenyl; R 3 for diphenyl sulfide group )

[0088] Dispersant FC-4430 0.05 parts by mass

[0089] (2) Preparation of filter color film

[0090] The components of the above composition are mixed and dissolved in 100 parts by mass of solvent propylene glycol monomethyl ether acetate (PGMEA) to form a liquid composition;

[0091] Apply the liquid composition on the substrate with the black matrix BM, dry at 90°C for 5 minutes to remove the solvent, and form a coating film with a film thickness of 1.5 μm; in orde...

Embodiment 3-1

[0104] (1) Green photosensitive composition No.3-1

[0105] C.I. Pigment Green 36 16 parts by mass

[0106] 27 parts by mass of alkali-soluble resin

[0107] [Benzyl methacrylate / methacrylic acid / hydroxyethyl methacrylate / acrylic acid ester of formula (II) (molar ratio is 60 / 5 / 15 / 10) copolymer] (Mw: 20000)

[0108] 18 parts by mass of dipentaerythritol hexaacrylate

[0109] Formula (I) ketoxime ester compound 6 parts by mass

[0110] (R 1 where n=1, m=3; R 2 is phenyl; R 3 for diphenyl sulfide group )

[0111] Dispersant FC-4430 0.05 parts by mass

[0112] Using the above composition, a filter color film was prepared and performance evaluated in the same manner as in Example 2-1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a photosensitive composite which contains a specific ketoxime ester compound used as a polymerization initiator, an alkali-soluble resin, DPHA (Dipentaerythritol Hexaacrylate) and a colorant. The composite has good storage stability and also has high exposure sensitivity, good developing performance, no wrinkle on formed pattern surfaces and excellent solidifying effect when used for making black matrixes (BM) and RGB (Red Green Blue) of a color filter. The invention also relates to the application of the photosensitive composite in the production of the color filter,and the filter made from the photosensitive composite has high optical transparency and no light leakage.

Description

technical field [0001] The present invention relates to a photosensitive composition, which contains a diphenyl sulfide ketoxime ester compound as a photopolymerization initiator, and also relates to the application of the photosensitive composition in the manufacture of color filters. Background technique [0002] Photocuring refers to the curing process of monomer, oligomer or polymer matrix under light induction, which is widely used in modern microelectronics technology. For example, a color filter as one of the core components of a liquid crystal display includes red (R), green (G), blue (B) polymer materials and a black matrix (BM), of which red, green, and blue are three parts Abbreviated as RGB, both RGB and BM are prepared by light curing technology in the prior art. [0003] The core of photocuring technology lies in the composition of the photosensitive composition. Under the irradiation of ultraviolet / visible light, X-ray or laser at a certain wavelength, the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/027G02B5/20G02F1/1335C07D209/86
Inventor 钱晓春胡春青王兵
Owner CHANGZHOU TRONLY NEW ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products