Method for preparing netty environmental-friendly shell fabric by utilizing diversification process

A net-like, environmentally friendly technology, applied in the direction of fabric surface trimming, weaving, rayon physical therapy, etc., can solve the problems of unsatisfactory performance limitations, single fabric types, low product grades, etc., and achieve a surface finish that is not greasy , good softness, good ventilation and heat dissipation

Active Publication Date: 2011-12-14
缪志德
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of fabric is relatively single, the product grade is low, and the limitation of performance has been increasingly unable to meet people's functional and diversified needs for clothing fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation process of a kind of multi-process net-shaped environmental protection fabric of the present invention comprises the following steps:

[0034] 1), preparation of polyvinyl chloride particles:

[0035]Get polyvinyl chloride resin white powder 50kg (Tianjin Lejin Dagu Chemical Co., Ltd. model: TL-1000), nano-active calcium carbonate 15kg, copolymer resin (vinyl chloride-vinyl acetate copolymer resin (VC / VAC) model: BL-2 Jiangsu Jiangyin Dahua Chemical Co., Ltd.) 15kg, environmental protection oil (acetyl tributyl citrate (ATBC) Shandong Qilu Plasticizer Co., Ltd.) 22kg, oxalic acid 2.5kg, put the above-mentioned raw materials into the mixer on the propeller type mixer In the pot, add calcium zinc stabilizer (HY-501) 2.5kg, PE wax 600g, stearic acid 400g, 1076 type antioxidant 150g, BP12 antiultraviolet agent 250g, antiflame retardant (antimony trioxide model: Sb203# 99.85% Hunan Hushan Antimony Zinc Products Co., Ltd.) 1.5g and environmental protection pi...

Embodiment 2

[0048] The basic process is the same as in Example 1. The difference is that the polyvinyl chloride particles consist of: 45 parts of polyvinyl chloride resin white powder, 16 kg of nano-active calcium carbonate, 13 kg of copolymer resin, 20 kg of environmental protection oil, 3 kg of oxalic acid, and 3 kg of calcium-zinc stabilizer , PE wax 0.550kg, stearic acid 0.450kg, 1076 type antioxidant 0.130kg, BP12 anti-ultraviolet agent 0.300kg, anti-flame retardant 0.001kg and environmental pigment 3g (RTC-30 titanium dioxide).

[0049] The performance index of the mixed silk yarn is:

[0050] Breaking strength BF 79N

[0051] Breaking strength TEN 8.1CN / dtex

[0052] 9.18g / den

[0053] Elongation at break EAB 13.8%

[0054] Constant load elongation EASF 6.2%

[0055] Dry heat shrinkage HAS 7.3%.

Embodiment 3

[0057]Basic technology is the same as embodiment 1, and the difference is that polyvinyl chloride particles are composed of: polyvinyl chloride resin white powder 55kg, nano-active calcium carbonate 13kg, copolymer resin 16kg, environmental protection oil 25kg, oxalic acid 2kg, calcium zinc stabilizer 2kg, PE wax 0.650kg, stearic acid 0.350kg, 1076 type antioxidant 0.160kg, BP12 anti-ultraviolet agent 0.200kg, anti-flame retardant 0.002kg and environmental protection pigment 3g (2030 red).

[0058] The performance index of described mixed silk thread is:

[0059] Breaking strength BF 79N

[0060] Breaking strength TEN 8.2CN / dtex

[0061] 9.3g / den

[0062] Elongation at break EAB 14.3%

[0063] Constant load elongation EASF 5.8%

[0064] Dry heat shrinkage HAS 7.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thermal resistanceaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a netty environmental-friendly shell fabric by utilizing a diversification process. The method comprises the following steps: 1) preparing polyvinyl chloride particles; 2) molding mixed silk threads; 3) warping and weaving; and 4) shaping. In the invention, at last, thermal collation process is carried out, thus the product surface is appreciably flat, straight, stiff and smooth; the product has good venting and heat dispersion performance; the surface part of the product has high smooth finish and is not greasy smooth; the tension strength is strong due to the rebound resilience, and the flexibility is good; and the product adapts to be matched with any pattern and color, has the characteristics of sun block, moisture resistance, water resistance, high temperature resistance, cold resistance and the like, can substitute the original fabrics in the domestic market formed by adopting polyethylene, nylon6, PE, PP, papyrus wires, bamboo skin, rattan wires, Putzwolle, artificial cellosilk and other material textures, and is suitable for the fields of leisure products, sandy beach nets, plate mats, table mats, floor mats, luggage, floor tiles, wallpaper, car seat cushions, hammocks, ornaments and other industries.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a method for preparing a mesh-shaped environmentally friendly fabric with multiple processes. Background technique [0002] Various materials such as polyethylene, nylon 6, PE, PP, papyrus thread, bamboo skin, rattan silk, cotton silk, and rayon silk used in the domestic market are organized into fabrics. This type of fabric is relatively single, the product grade is low, and the limitation of performance has been increasingly unable to meet people's functional and diversified needs for clothing fabrics. Contents of the invention [0003] In order to solve the above problems, the present invention provides a kind of multi-process net-shaped environmentally friendly fabric with good ventilation and heat dissipation performance, high surface finish and non-slippery, strong tensile strength due to strong resilience, good softness, and adaptable to any pattern and color matching. craft. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D13/00D02G3/04D01D10/00D06C7/02C08L27/06C08K13/02C08K3/26C08K3/22D03D15/283D03D15/50D03D15/54
Inventor 缪志德
Owner 缪志德
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com