A low-speed heavy-duty, grease technology, applied in the field of grease, can solve the problems of difficult to meet the use requirements of the boom, the wear of the boom steel plate and slider, and the inability to withstand the high load of the boom. Low temperature performance, extended service life, good lubrication effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example
[0023] Some raw materials:
[0024] Mercaptopolysiloxane emulsion: provided by Nanjing Hualiming Chemical Co., Ltd.;
[0025] Polymethyltriethoxysilane: provided by Zhejiang Quzhou Zhengbang Organic Silicon Co., Ltd.;
[0026] Polyethylene wax: Provided by Jiande Huachen Chemical Co., Ltd.;
[0027] Graphite powder: Provided by Qingdao Dongkai Graphite Co., Ltd.
Example Embodiment
[0028] Examples 1-6
[0029] Weigh out monobasic fatty acid or dodecanoic acid, at least one dibasic acid selected from terephthalic acid and C2-C8 dibasic acid, base oil, 12% calcium hydroxide and / Or lithium hydroxide, heated to 80°C in a reactor, and saponified for 3 hours. Then the temperature was raised to 210°C, the temperature was kept for 15 minutes, the base oil was added to adjust the soap amount, and it was cooled to 120°C. Add graphite powder, extreme pressure additives, organic esters and optional hydrophobic agents, grind and disperse, distill under low pressure to remove water and gas, cool naturally to form fat, and obtain 6 samples S1-S6 respectively.
[0030] Table 1. The raw material formulations of Examples 1-6
[0031]
[0032]
[0033] Table 2. Performance parameters of sample S1-S6
[0034]
Example Embodiment
[0035] Examples 1 and 5 lack hydrophobizing agent and polytetrafluoroethylene powder, showing poor water leaching resistance, so the service life will be shorter; Example 1 lacks graphite and has a low percentage of other extreme pressure additives, showing poor extremes In addition to graphite powder, zinc didecyl dithiophosphate and molybdenum disulfide are also added in Examples 2 and 4, which is slightly worse in extreme pressure wear resistance. In addition to graphite powder, Example 3 Added molybdenum didecyl dithiocarbamate, showing good extreme pressure wear resistance; Example 5 only added a proper amount of extreme pressure additives, so the extreme pressure performance is better, but the water leaching performance, oil separation performance And low temperature performance is poor; Example 6 uses eight kinds of additives at the same time to add in appropriate proportions, showing good overall performance.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap