Carbon nanotube silicone rubber

A carbon nanotube and silicone rubber technology, applied in the direction of adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve problems such as potential safety hazards, and achieve the effects of excellent performance, good elasticity, and good low temperature resistance.

Pending Publication Date: 2019-12-20
YANCHENG ZENGCAI SCI & TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the glass curtain wall is in use, it needs to be spliced ​​and sealed, otherwise it will easily cause safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1 carbon nanotube silicone rubber, in parts by weight, consists of the following components:

[0012] Siloxane: 6, borate: 1, high-quality carbon black: 3, copper powder: 1, titanium oxide: 1,

[0013] Titanium dioxide: 3, tetraethyl orthosilicate: 1, phthalates: 4, carbon nanotubes: 1.

[0014] tensile strength Low temperature resistance High temperature resistance preservative VOCs 105gpa -30℃ 200℃ 2555 hours 1％

Embodiment 2

[0015] Embodiment 2 carbon nanotube silicone rubber, in parts by weight, consists of the following components:

[0016] Siloxane: 10, Borate: 10, Premium Carbon Black: 6, Copper Powder: 3, Titanium Oxide: 3,

[0017] Titanium dioxide: 6, tetraethyl orthosilicate: 10, phthalates: 8, carbon nanotubes: 2.

[0018] tensile strength Low temperature resistance High temperature resistance preservative VOCs 115gpa -30℃ 210℃ 2555 hours 1％

Embodiment 3

[0019] Embodiment 3 carbon nanotube silicone rubber, in parts by weight, consists of the following components:

[0020] Siloxane: 5, borate: 5, high-quality carbon black: 5, copper powder: 2, titanium oxide: 2,

[0021] Titanium dioxide: 5, tetraethyl orthosilicate: 5, phthalates: 6, carbon nanotubes: 1.5.

[0022] tensile strength Low temperature resistance High temperature resistance preservative VOCs 115gpa -30℃ 201℃ 2555 hours 1％

[0023] The preparation method of the glass curtain wall sealant is as follows: according to the proportion, the components are mixed, and the finished product can be obtained after stirring and dispersing evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses carbon nanotube silicone rubber. The carbon nanotube silicone rubber is composed of the following components, in parts by weight: 6-10 parts of siloxane, 1-10 parts of borate,3-6 parts of high-quality carbon black, 1-3 parts of copper powder, 1-3 parts of titanium oxide, 3-6 parts of titanium dioxide, 1-10 parts of ethyl orthosilicate, 4-8 parts of phthalate, and 1-2 partsof carbon nanotubes. A preparation method of a novel glass curtain wall sealant comprises the following steps: mixing the components according to the above ratios, and performing stirring for uniformdispersion to obtain the finished product. Compared with the prior art, the sealant provided by the invention has excellent performance such as heat resistance, aging resistance, stress resistance and corrosion resistance, the Tg is lower than -60 DEG C, and the sealant has fairly good low-temperature resistance, good elasticity, and great application prospects.

Description

technical field [0001] The invention belongs to the technical field of adhesives, in particular to carbon nanotube silicone rubber. Background technique [0002] Sealant is a sealing material that deforms with the shape of the sealing surface, is not easy to flow, and has a certain degree of cohesion. It is an adhesive used to fill the configuration gap and play a sealing role. According to the base material, it is divided into rubber type, resin type, and oil type. Basic type, some sealants have poor bonding performance and poor sealing performance. They are easy to harden and crack when the outdoor temperature is low in winter, and produce harmful substances during and after curing, and even pollute the substrate. Glass curtain walls are widely used, mainly for decoration and other purposes. When the glass curtain wall is in use, it needs to be spliced ​​and sealed, otherwise it will easily cause safety hazards. Carbon nanotubes, also known as bucky tubes, are one-dimens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J183/04C09J11/04C09J11/06
CPCC09J183/04C09J11/04C09J11/06C08K2003/085C08K2003/2241C08K2201/011C08K13/02C08K5/55C08K3/04C08K3/08C08K3/22C08K3/041C08K5/12
Inventor 闵永刚程鹏鹏刘屹东
Owner YANCHENG ZENGCAI SCI & TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com