UV (Ultra Violet) offset printing ink and preparation method thereof

An offset printing ink and offset printing technology, applied in inks, household appliances, applications, etc., can solve the problems of poor ink transfer from stacking rollers, easy emulsification and paste printing, etc., to facilitate large-scale promotion and application, good printing performance, and reduce printing. cost effect

Active Publication Date: 2011-03-23
惠州深赛尔化工有限公司
View PDF2 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Another object of the present invention is to provide a kind of UV offset printing ink and its preparation method, this ink and method can overcome the existing offset printing base oil easy emulsification pasting plate, the problem of easy stacking roller and poor ink transfer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Preparation of UV offset printing primer:

[0032] According to the weight ratio, add 3 parts of superfine talcum powder and 2 parts of superfine calcium carbonate filler to 10 parts of SartomerCN200 and 10 parts of Cytec’s EB436, add 1 part of Afcona-4000 dispersant, and disperse 40 parts with a high-speed disperser Minutes later, use a three-roll machine to grind 4~5 times until the fineness is ≤5um to obtain the base ink; then add 5 parts of reactive diluent ethoxylated trimethylolpropane triacrylate, 1 part of 2- Hydroxy-2-methyl-1-phenyl-1-propanone, 2 parts of bisbenzoylphenylphosphine oxide photoinitiator, 7 parts of DC-10000 additives from Dow-corning company, the speed of high-speed disperser is 1500~ Stir at 2000rpm / min for 30-60 minutes, and control the temperature at 50-60 degrees Celsius. After the photoinitiator is dissolved, add the remaining 25 parts of SartomerCN200 and 5 parts of EB436, and disperse at high speed for 5 minutes to obtain UV offset print...

Embodiment 2

[0036] Preparation of UV offset printing primer:

[0037]Add 3 parts of superfine talcum powder and 7 parts of superfine calcium carbonate filler to 10 parts of SartomerCN200 and 10 parts of Cytec's EB436, add 2 parts of Afcona-4000 dispersant, disperse with a high-speed disperser for 30 minutes, and then use a three-roller Machine milling 4~5 times until the fineness is ≤5um to obtain the base ink; then add 7 parts of reactive diluent ethoxylated trimethylolpropane triacrylate, 3 parts of 2-hydroxy-2-methanol to the base ink Base-1-phenyl-1-acetone, 5 parts of bisbenzoylphenylphosphine oxide photoinitiator, 8 parts of DC-10000 auxiliary agent from Dow-corning company, stirred at a speed of 1500~2000rpm / min in a high-speed disperser for 30 ~60 minutes, the temperature is controlled at 50~60 degrees Celsius. After the photoinitiator is dissolved, add the remaining 35 parts of SartomerCN200 and 5 parts of EB436 resin, and disperse at high speed for 10 minutes to get UV offset pr...

Embodiment 3

[0041] Preparation of UV offset printing primer:

[0042] Add 5 parts of superfine talcum powder and 10 parts of superfine calcium carbonate filler to 20 parts of SartomerCN200 and 20 parts of Cytec's EB436, add 3 parts of Afcona-4000 dispersant, disperse with a high-speed disperser for 30 minutes, and then use a three-roller Machine milling 4~5 times until the fineness is ≤5um to obtain the base ink; then add 10 parts of reactive diluent ethoxylated trimethylolpropane triacrylate, 4 parts of 2-hydroxy-2-methanol to the base ink Base-1-phenyl-1-acetone, 6 parts of bisbenzoylphenylphosphine oxide photoinitiator, 15 parts of DC-10000 auxiliary agent from Dow-corning company, stirred at a speed of 1500~2000rpm / min in a high-speed disperser for 30 ~60 minutes, the temperature is controlled at 50~60 degrees Celsius. After the photoinitiator is dissolved, add the remaining 30 parts of SartomerCN200 resin, and disperse at high speed for 20 minutes to get UV offset printing primer.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to UV (Ultra Violet) offset printing carrier oil, connection UV offset printing gloss oil and preparation methods thereof. The offset printing ink comprises UV offset printing carrier oil and connection UV offset printing gloss oil, wherein the UV offset printing carrier oil is prepared from a polyester acrylate oligomer, filling, a reactive diluent, a high-viscosity additive, and the like by firstly adding a dispersant and resin, grinding the filling to a qualified degree of fineness and then adding the active diluent, a photoinitiator and the high-viscosity additive to stir and disperse together at a high speed, the connection UV offset printing gloss oil is prepared from a high-functional urethane acrylate oligomer, a dual-functional urethane acrylate oligomer, a photoinitiator, a leveling agent, and the like by stirring at a high speed, filtering, and the like. The offset printing ink and the method enable a printed product to generate the special concentration effect so as to obtain various special surface printing effects.

Description

technical field [0001] The invention relates to the field of ink chemical industry, and mainly relates to a UV offset printing ink and a preparation method thereof. Background technique [0002] UV offset printing ink is a relatively new type of printing ink in recent years. It mainly changes the ink from liquid to solid in an instant under the irradiation of ultraviolet rays of a certain wavelength to complete the drying process. It is usually composed of fillers, oligomers, reactive diluents, photoinitiators and additives, and has the advantages of no volatile solvents, no odor, non-drying plate, strong water and solvent resistance, etc. [0003] In the UV offset printing process, users often put forward many unique requirements, such as water drop lotus leaf effect, frosted etching effect, embossed laser effect, etc. For these effects, the current UV offset printing ink cannot achieve the required effect, and the current There are relatively few manufacturers that produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/101C09D11/107
Inventor 庞秋德刘国民
Owner 惠州深赛尔化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com